Surface modification of nanocrystalline ZrO2 powder with an ultrathin MoO3 layer was successfully carried out by a polymeric resin route using polyacrylic acid and ethylene glycol as precursors. Polyacrylic acid plays a vital role in this process, not only as the chelating agent for the molybdate cluster but also to form the uniform layer of molybdate dispersed polymeric resin on the surface of ZrO2. Thermal decomposition of the resin intermediate at 500°C creates the organic free MoO3 layer on the ZrO2 surface. Fourier transform infrared, X-ray diffraction and SEM energy dispersive spectroscopy analysis confirm the uniform formation of crystalline MoO3 on the surface of the ZrO2 powder. Further, the MoO3 layer thickness was identified by TEM characterisation and was found to be ∼3 nm.
SubbaraoE., MaitiH. and SrivastavaK.: ‘Martensitic transformation in zirconia’, Phys. Status Solidi A, 1974, 21A, (1), 9–40.
2.
YashimaM., KatoT.-A, KakihanaM., GulgunM. A., MatsuoY. and YoshimuraM.: ‘Crystallization of hafnia and zirconia during the pyrolysis of acetate gels’, J. Mater. Res., 1997, 12, (10), 2575–2583.
3.
BondioliF., FerrariA. M., LeonelliC., SiligardiC. and PellacaniG. C.: ‘Microwave - hydrothermal synthesis of nanocrystalline zirconia powders’, J. Am. Ceram. Soc., 2004, 84, (11), 2728–2730.
4.
TomishigeK., IkedaY., SakaihoriT. and FujimotoK.: ‘Catalytic properties and structure of zirconia catalysts for direct synthesis of dimethyl carbonate from methanol and carbon dioxide’, J. Catal., 2000, 192, (2), 355–362.
5.
OetzelC. and ClasenR.: ‘Preparation of zirconia dental crowns via electrophoretic deposition’, J. Mater. Sci., 2006, 41, (24), 8130–8137.
6.
TsukumaK., UedaK., MatsushitaK. and ShimadaM.: ‘High - temperature strength and fracture toughness of Y2O3 - partially - stabilized ZrO2/Al2O3 composites’, J. Am. Ceram. Soc., 2006, 68, (2), C-56–C-58.
7.
HuY., ZhouS. and WuL.: ‘Surface mechanical properties of transparent poly (methyl methacrylate)/ zirconia nanocomposites prepared by in situ bulk polymerization’, Polymer, 2009, 50, (15), 3609–3616.
8.
KotlyarchukB., PopovychD., SavchukV. and SerednyckiA.: ‘Pulsed laser deposition of ZrO2 thin films for application in microelectronic devices’, Phys. Chem. Solid State, 2003, 4, (3), 434–439.
9.
SahuS. K., GanesanR., JayaramanV. and GnanasekaranT.: ‘Development of zirconia based oxygen sensor for lead and lead–bismuth eutectic’, Mater. Sci. Forum, 2012, 751–756.
10.
VivekanandhanS., VenkateswarluM., RawlsH. and SatyanarayanaN.: ‘Acrylamide assisted polymeric citrate route for the synthesis of nanocrystalline ZrO2 powder’, Mater. Chem. Phys., 2010, 120, (1), 148–154.
11.
KonstantinovićZ., Del MuroM. G., VarelaM., BatlleX. and LabartaA.: ‘Particle growth mechanisms in Ag–ZrO2 and Au–ZrO2 granular films obtained by pulsed laser deposition’, Nanotechnology, 2006, 17, (16), 4106.
12.
RhodesM. D. and BellA. T.: ‘The effects of zirconia morphology on methanol synthesis from CO and H2 over Cu/ZrO2 catalysts: Part I. Steady-state studies’, J. Catal., 2005, 233, (1), 198–209.
13.
CastroL., ReyesP. and de CorreaC. M.: ‘Synthesis and characterization of Sol-Gel Cu-ZrO2 and Fe-ZrO2 Catalysts’, J. Sol–Gel Sci. Technol., 2002, 25, (2), 159–168.
14.
ReddyD. B. M. and KhanA.: ‘Recent advances on TiO2 - ZrO2 mixed oxides as catalysts and catalyst supports’, Catal. Rev., 2005, 47, (2), 257–296.
15.
MonteF., LarsenW. and MackenzieJ. D.: ‘Stabilization of tetragonal ZrO2 in ZrO2–SiO2 binary oxides’, J. Am. Ceram. Soc., 2004, 83, (3), 628–634.
16.
BhattyM. B., KhalidF. A. and KhanA. N.: ‘Behavior of calcia-stabilized zirconia coating at high temperature, deposited by air plasma spraying system’, J. Therm. Spray Technol., 2012, 1–11.
17.
LuZ., ZhuZ., ZhengX., QiaoY., GuoJ. and LiC. M.: ‘Biocompatible fluorescence-enhanced ZrO2–CdTe quantum dot nanocomposite for in vitro cell imaging’, Nanotechnology, 2011, 22, (15), 155604.
18.
GaneevR. A., BabaM., MoritaM., RauD., FujiiH., RyasnyanskyA., IshizawaN., SuzukiM. and KurodaH.: ‘Nonlinear optical properties of CdS and ZnS nanoparticles doped into zirconium oxide films’, J. Opt. A, 2004, 6A, (4), 447.
19.
SayariA. and DickoA.: ‘The state of platinum in Pt on sulfated zirconia superacid catalysts’, J. Catal., 1994, 145, (2), 561–564.
20.
NavarraM., CroceF. and ScrosatiB.: ‘New, high temperature superacid zirconia-doped Nafion™ composite membranes’, J. Mater. Chem., 2007, 17, (30), 3210–3215.
21.
MullaI., PradhanS. and VijayamohananK.: ‘Humidity-sensing behaviour of surface-modified zirconia’, Sens. Actuators A, 1996, 57A, (3), 217–221.
22.
PaeY. I., LeeS. H. and SohnJ. R.: ‘Correlation between acidic properties of nickel sulfate supported on TiO2-ZrO2 and catalytic activity for ethylene dimerization’, Catal. Lett., 2005, 99, (3), 241–248.
23.
BrownA., HargreavesJ. and TaylorS.: ‘A study of “superacidic” MoO3/ZrO2 catalysts for methane oxidation’, Catal. Lett., 1999, 57, (3), 109–113.
DavisB. H., KeoghR. A. and SrinivasanR.: ‘Sulfated zirconia as a hydrocarbon conversion catalyst’, Catal. Today, 1994, 20, (2), 219–256.
26.
AfanasievP.: ‘On the metastability of ‘monolayer coverage’ in the MoO3/ZrO2 dispersions’, Mater. Chem. Phys., 1997, 47, (2–3), 231–238.
27.
KanmaniS. and RamachandranK.: ‘Synthesis and characterization of TiO2/ZnO core/shell nanomaterials for solar cell applications’, Renewable Energy, 2012, 43, 149–156.
28.
MorelA.-L, NikitenkoS. I., GionnetK., WattiauxA., Lai-Kee-HimJ., LabrugereC., ChevalierB., DelerisG., PetiboisC. and BrissonA.: ‘Sonochemical approach to the synthesis of Fe3O4@ SiO2 core– shell nanoparticles with tunable properties’, Acs Nano, 2008, 2, (5), 847–856.
29.
VivekanandhanS., VenkateswarluM., CarnahanD., MisraM., MohantyA. and SatyanarayanaN.: ‘Sol-gel mediated surface modification of nanocrystalline NiFe2O4 spinel powders with amorphous SiO2’, Ceram. Int., 2013, 39, (4), 4105–4111.
30.
ChungK. Y., YoonW.-S, McBreenJ., YangX.-Q, OhS. H., ShinH. C., ChoW. I. and ChoB. W.: ‘Structural studies on the effects of ZrO2 coating on LiCoO2 during cycling using in situ X-ray diffraction technique’, J. Electrochem. Soc., 2006, 153, (11), A2152–A2157.
31.
MohanP. and KalaignanG. P.: ‘Electrochemical performance of La2O3-coated layered LiNiO2 cathode materials for rechargeable lithium-ion batteries’, Ionics, 2012, 1–8.
32.
VivekanandhanS., VenkateswarluM., MisraM., MohantyA. K. and SatyanarayanaN.: ‘Novel polymeric resin route for the surface modification of nanocrystalline LiCoO2 particles with Al2O3’, Nanosci. Nanotechnol. Lett., 2011, 3, (2), 161–165.
33.
SocratesG. and SocratesG.: ‘Infrared and Raman characteristic group frequencies: tables and charts’; 2001, Chichester, Wiley.
34.
TyagiB., SidhpuriaK., ShaikB. and JasraR. V.: ‘Synthesis of nanocrystalline zirconia using sol-gel and precipitation techniques’, Ind. Eng. Chem. Res., 2006, 45, (25), 8643–8650.
35.
TangW., LiuL., TianS., LiL., YueY., WuY. and ZhuK.: ‘Aqueous supercapacitors of high energy density based on MoO3 nanoplates as anode material’, Chem. Commun., 2011, 47, (36), 10058–10060.