Effects of microstructural changes,loading conditions and test temperature on toughness of fully pearlitic eutectoid steel used in transportation industry

Abstract

The mode I fracture toughness of fully pearlitic eutectoid steel used in the transportation industry has been investigated at temperatures ranging from −196 to 225°C using bend bar specimens notched and fatigue precracked to contain different root radii. The effects of changes in microstructure on the cleavage fracture stress were determined over a similar range. In addition, the notched and fatigue precracked specimens have been subjected to combined mode I/II fracture under asymmetric three point bend loading at −125°C on different microstructural conditions. Increasing the offset distance between the notch and the loading point produces an increase in the ratio mode II/mode I, a change in the crack deflection angle and a reduction in the total energy of fracture. Significant effects of changes in microstructure, test temperature and notch root radius on the toughness will be presented, followed by the significant effects of changes in microstructure and the ratio mode II/mode I on the fracture load, crack deflection angle and resulting toughness. Fractured specimens were examined both macroscopically and microscopically using stereomicroscope and scanning electron microscopy.

Keywords

PEARLITIC STEEL FRACTURE TOUGHNESS NOTCH ROOT RADIUS LOW TEMPERATURE MIXED MODE LOADING I/II SEM CLEAVAGE FRACTURE STRESS NUCLEATION SITES

Get full access to this article

View all access options for this article.

References

Lesuer

D. R.

, Syn

C. K.

, Goldberg

, Wadsworth

and Sherby

O. D.

: JOM, 1993, 45, 40–46.

Lojkowski

, Djahanbakhsh

, Burkle

, Gierlotka

, Zielinski

and Fecht

H.-J.

: Mater. &Sci. Eng. A, 2001, A303, 197–208.

Ueda

and Uchino

: ‘Thermomechanical processing and mechanical properties of hypereutectoid steels and cast irons’, (ed.

Lesuer

D. R.

.), 161-174; 1997, Warrendale, PA, TMS.

Taleff

E. M.

, Lewandowski

J. J.

and Pourladian

: JOM, 2002, 54, 25–30.

Ochiai

, Nishida

and Tashiro

: Proc. 63rd Annual Convention of The Wire Association International, Atlanta, GA, USA, 39–49; 1993.

Taleff

E. M.

, Syn

C. K.

, Lesuer

D. R.

and Sherby

O. D.

: ‘Thermomechanical processing and mechanical properties of hypereutectoid steels and cast irons’, (ed. Lesuer

D. R.

et al.),127–142; 1997, Warrendale, PA, TMS.

Alexander

D. J.

and Bernstein

I. M.

: Metall Mater. Trans. A, 1987,20A, 2321–2335.

Porter

D. A.

, Easterling

K. E.

and Smith

G. D. W.

: Acta Metall., 1978, 26, 1405–1422

Park

Y. J.

and Bernstein

I. M.

: Metall Trans. A, 1979, 10A, 1653–1664.

10.

Lewandowski

J. J.

and Thompson

A. W.

: Metall Mater. Trans. A, 1986, 17A, 1769–1786.

11.

Hyzak

J. M.

and Bernstein

I. M.

: Metall. Mater. Trans. A, 1976, 7A, 1217–1224.

12.

Marder

A. R.

and Bramfitt

B. L.

: Metall Mater. Trans. A, 1976,7A, 365–372.

13.

O’Donnelly

B. E.

, Reuben

R. L.

and Baker

T. N.

:Met. Technol., 1984, 11, 45–51.

14.

Lewandowski

J. J.

and Thompson

A. W.

: Metall. Mater. Trans. A,1986, 17A, 461–471.

15.

Gray

G. T.

, III, J. C. Williams and A. Thompson: Metall. Mater. Trans. A, 1983, 14A, 421–433.

16.

Toribio

, Ovejero

and Toledano

: Int. J. Fracture, 1997, 87,L83–L88

17.

El-Shabasy

A. B.

and Lewandowski

J. J.

: Int. J. Fatigue, 2004, 26,305–309.

18.

Alexander

D. J.

and Bernstein

I. M.

: in ‘Phase transformation in ferrous alloys’, (ed. Marder

A. R.

and Goldstein

J. I.

), 243–257;1984, Warrendale, PA, TMS-AIME

19.

Irwin

G. R.

: in ‘Encyclopedia of physics’, (ed. Flugge

), Vol. 6,551–590;1958, Berlin, Springer.

20.

Maccagno

T. M.

and Knott

J. F.

: Eng. Fract. Mech., 1989, 34, 65–86.

21.

Erodogan

and Sih

G. C.

: J. Basic Eng. Trans., 1963, ASME Ser.D85, 519–527.

22.

M. Y.

, Cao

H. C.

and Evans

A. G.

: Acta Metall. Mater., 1990, 38, 839–846.

23.

Suresh

, Shih

C. F.

, Morrone

and O'Dowd

N. P.

: J. Am. Ceram. Soc., 1990, 73, 1257–1267.

24.

Shah

R. C.

: ‘Fracture analysis’, ASTM STP 560, 29-52; 1974, Philadelphia, PA, ASTM.

25.

Maccagno

T. M.

and Knott

J. F.

: Eng. Fract. Mech., 1992,41, 805–820.

26.

Bhattacharee

and Knott

J. F.

: Acta Metall. Mater., 1994, 42, 1747–1754.

27.

Griffiths

J. R.

and Owen

D. R. J.

: J. Mech. Phys. Solids, 1971, 19, 419–431.

28.

‘Standard test method for measurement of fatigue crack growth rate’, Annual Book of ASTM Standards, E 647-98, ASTM, Philadelphia, PA, USA, 2000.

29.

‘Standard test method for plane strain fracture toughness of metallic materials’, Annual Book of ASTM Standards, E 399-98, ASTM, Philadelphia, PA, USA, 2000.

30.

Wang

K. J.

, Hsu

C. L.

and Kao

: Fracture, 1977, 4, 123–133.

31.

Margevicius

R. W.

, Riedle

and Gumbsch

: Mater. Sci. Eng. A., 1990, A270, 197–209.

32.

Lewandowski

J. J.

and Thompson

A. W.

: Acta Metall., 1987, >35,1453–1462.

33.

Hutchinson

J. W.

: J. Mech. Phys. Solids, 1968, 16, 13–31.

34.

Rice

J. R.

and Rosengren

G. R.

: J. Mech. Phys. Solids, 1968, 16, 1–12.

35.

Ritchie

R. O.

, Knott

J. F.

and Rice

J. R.

: J. Mech. Phys. Solids, 1973, 21, 395–410.

36.

Samant

A. V.

and Lewandowski

J. J.

: Metall. Mater. Trans. A, 1997, 28A, 389–399.

37.

Samant

A. V.

and Lewandowski

J. J.

: Metall. Mater. Trans. A, 1997, 28A, 2297–2307.

38.

Lin

, Evans

A. G.

and Ritchie

R. O.

: Metall Mater. Trans. A, 1987, 18A, 641–651.

39.

McMahon

C. J.

, Jr and M. Cohen: Acta Metall., 1965, 13, 591–604.

40.

Curry

D. A.

and Knott

J. F.

: Met. Sci., 1976, 10, 1–6.

41.

Maccagno

T. M.

and Knott

J. F.

: Eng. Fract. Mech., 1991,38, 111–128.