Microstructure and static immersion corrosion behavior of AA7020-O Al plates joined by friction stir welding

Abstract

In the present investigation, the influence of tool pin profile and postweld heat treatment on microstructure, hardness, and static immersion corrosion behavior of AA7020-O Al plates joined by friction stir welding was investigated. Friction stir welding was conducted using two tools having different pin profiles, typically, a tool with tapered cylindrical pin and a tool with two flat-sided cylindrical pin. Postweld heat treatment was carried out using a solution heat treatment temperature of 540 ± 1℃ for 12 h followed by aging at 155 ± 1℃ for 6 h. Corrosion tests were carried out by immersing the welds in an aqueous solution containing NaCl and H₂O₂ for 6 h according to ASTM-G110. The results revealed that the two flat-sided cylindrical pin tool produces finer α-Al grains, at the center of dynamically recrystallized zones, than the tapered cylindrical pin tool. The postweld heat treatment slightly increases the size of the α-Al grains at the center of dynamically recrystallized zones. In the as-welded conditions, the friction stir welded regions exhibited lower hardness values than the base alloy. However, the regions friction stir welded using two flat-sided cylindrical pin tool showed relatively higher hardness values than those regions friction stir welded using the tapered cylindrical pin tool. The postweld heat treatment slightly increases the hardness of the welded regions to values that are still lower than the base alloy. Generally, the dynamically recrystallized zones are more susceptible to corrosion than the base alloy. In both AW and postweld heat treatment conditions, the thermomechanically affected zones showed the lowest corrosion resistance when compared with dynamically recrystallized zones and heat affected zone regions. In the as-welded conditions, regions friction stir welded using tapered cylindrical pin tool exhibited better corrosion resistance than those friction stir welded using two flat-sided cylindrical pin. The postweld heat treatment improves the corrosion resistance of the dynamically recrystallized zones friction stir welded using two flat-sided cylindrical pin tool.

Keywords

Friction stir welding aluminum alloys postweld heat treatment corrosion

Get full access to this article

View all access options for this article.

References

Tejonadha Babu

Kranthi Kumar

Muthukumaran

. Mechanical, metallurgical characteristics and corrosion properties of friction stir welded AA6061-T6 using commercial pure aluminium as a filler plate. Procedia Mater Sci 2014; 6: 648–655.

Venkata Rao

Madhusudhan Reddy

Srinivasa Rao

. Microstructure and pitting corrosion resistance of AA2219 Al–Cu alloy friction stir welds – effect of tool profile. Defense Technol 2015; 11: 123–131.

Yang

Zhou

. Improving corrosion resistance of friction stir welding joint of 7075 aluminum alloy by micro-arc oxidation. J Mater Sci Technol 2014; 30: 1251–1254.

Wadeson

Zhou

Thompson

. Corrosion behavior of friction stir welded AA7108 T79 aluminium alloy. Corrosion Sci 2006; 48: 887–897.

Jariyaboon

Davenport

Ambat

. The effect of welding parameters on the corrosion behavior of friction stir welded AA2024–T351. Corrosion Sci 2007; 49: 877–909.

Pao

Gill

Feng

. Corrosion-fatigue crack growth in friction stir welded Al 7075. Scripta Mater 2001; 45: 605–612.

Surekha

Murty

Prasad Rao

. Effect of processing parameters on the corrosion behavior of friction stir processed AA 2219 aluminium alloy. Solid State Sci 2009; 11: 907–917.

Krishnan

. The effect of post weld heat treatment on the properties of 6061 friction stir welded joints. J Mater Sci 2002; 37: 473–480.

Sullivan

Robson

. Microstructural properties of friction stir welded and post-weld heat-treated 7449 aluminium alloy thick plate. Mater Sci Eng A 2008; 478: 351–360.

10.

Prisco

Squillace

Astarita

. Influence of welding parameters and post-weld aging on tensile properties and fracture location of AA2139-T351 friction-stir-welded joints. Mater Res 2013; 16: 1106–1112.

11.

Astarita

Squillace

Armentani

. Friction stir welding of AA 2198 T3 rolled sheets in butt configuration. Metall Ital 2012; 104: 31–40.

12.

Cavaliere

De Santis

Panella

. Effect of anisotropy on fatigue properties of 2198 Al-Li plates joined by friction stir welding. Eng Failure Anal 2009; 16: 1856–1865.

13.

Kandasamy

Hussain

Rajesham

. An investigation on the effect of rolling direction on the IMC formed during friction stir welding of AA7075 alloys. IUP J Mech Eng 2011; 3: 52–54.

14.

Zhang

Cao

Larose

. Review of tools for friction stirs welding and processing. Can Metall Quart 2012; 51: 3–7.

15.

ASTM Standard G110:1998. Standard practice for evaluating inter-granular corrosion resistance of heat treatable aluminium alloys by immersion in sodium chloride + H₂O₂ solutions.

16.

Aydın

Bayram

Durgun

. The effect of post-weld heat treatment on the mechanical properties of 2024-T4 friction stir-welded joints. Mater Des 2010; 31: 2568–2577.

17.

Yuan

Wang

. Effect of post-weld heat treatment on the microstructure and plastic deformation behavior of friction stir welded 2024. Mater Des (Short Commun) 2011; 32: 5055–5060.

18.

Cerri

Leo

. Mechanical properties evolution during post-welding-heat treatments of double-lap friction stir welded joints. Mater Des 2011; 32: 3465–3475.

19.

Liu

Feng

. Effect of post-processing heat treatment on microstructure and microhardness of water-submerged friction stir processed 2219-T6 aluminum alloy. Mater Des 2013; 47: 101–105.

20.

Sato

Park

SHC

Kokawa

. Microstructural factors governing hardness in friction-stir welds of solid-solution-hardened Al alloys. Metall Mater Trans A 2001; 32A: 3033–3042.

21.

ASM Handbook. Corrosion, 4th ed. Vol. 13.: ASM International, 1992, pp. 13–13.

22.

Osório

Freitas

Garcia

. Corrosion performance based on the microstructural array of Al-based monotectic alloys in a NaCl solution. J Mater Eng Perform 2014; 23: 333–341.

23.

Osório

Freitas

Garcia

. EIS parameters and cell spacings of an Al-Bi alloy in NaCl solution. Electrochim Acta 2013; 108: 781–787.

24.

Osório

Freire

Garcia

. The role of macrostructural morphology and grain size on the corrosion resistance of Zn and Al castings. Mater Sci Eng A 2005; 402: 2–32.

25.

Bousquet

Poulon-Quintin

Puiggali

. Relationship between microstructure, microhardness and corrosion sensitivity of an AA 2024-T3 friction stir welded joint. Corrosion Sci 2011; 53: 3026–3034.