The present research aims to study the fatigue crack propagation and fracture toughness behavior of different zones of friction stir welds of AA7039 alloy, as different zones had varying microstructural and mechanical properties. Compact tension specimens with an initial notch in distinct weld zones parallel to the welding direction were machined using welded plates. Friction stir welding altered the base metal grain structure momentously, refined the grain structure in the weld nugget zone, and coarsen the same in the heat-affected zone. No correlation was observed between grain size and weld zone(s) hardness. Weld tensile properties were slightly inferior to base metal despite significantly higher hardness and alternation of grain structure. The fatigue life was dominated by the cycles consumed in crack propagation than crack initiation. The heat-affected zone had higher quasi-static fracture toughness, energy release rate, and resistance toward fatigue crack growth than other zones, because coarse grains and precipitates acted as effective impediments and slowed crack propagation. The heat-affected zone had a mixed-mode fracture, but the weld nugget zone and thermo-mechanically affected zone had an I mode fracture. On fracture surfaces, fracture characteristics such as microvoid coalescence were apparent.
Get full access to this article
View all access options for this article.
References
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.