Application of a direct laser melting process for fabricating a micropattern in bipolar plates used in direct methanol fuel cells

Abstract

Direct laser melting (DLM) technology is applied to fabricate the micropattern of bipolar plates in a direct methanol fuel cell (DMFC). For the micropatterning, a DLM process with 316L stainless steel (SS316L) powder has been used. For the target point of 1 mm melt height, the DLM process conditions are optimized and an eight-layer structure is successfully formed. The performance of a bipolar plate made by the DLM micropatterning is compared with a numerical control (NC)-machined bipolar plate. For the DLM micropatterned bipolar plate, the kinetic energy in the fuel causes a more rapid chemical reaction due to the increased surface area of rough side walls. The smaller fluid rate loss enhances circulation of the fluid and, consequently, the efficiency of the micropatterned bipolar plate made by the DLM process is significantly improved. Furthermore, the use of SS316L powder material as a micropatterned material reduces the fabrication cost as well as size of the fuel cell stack.

Keywords

direct laser melting (DLM) process direct methanol fuel cell (DMFC)bipolar plate 316L stainless steel (SS316L) powder

References

Pinkerton

A. J.

Direct additive laser manufacturing using gas- and water-atomised H13 tool steel powders. Int. J. Advd Mfg Technol., 2005, 25, 471–479.

Jerrard

P. G. E.

Hao

Evans

K. E.

Experimental investigation into selective laser melting of austenitic and martensitic stainless steel powder mixtures. Proc. IMechE, Part B: J. Engineering Manufacture, 2009, 223(B11), 1409–1416.

Yadroitsev

Bertrand

Ph.

Smurov

Parametric analysis of the selective laser melting process. Appl. Surface Science, 2007, 253(19), 8064–8069.

G. Q.

Wang

C. Y.

Development of micro direct methanol fuel cells for high power applications. J. Power Sources, 2005, 144(1), 141–145.

Kuan

Y. D.

Lee

S. M.

Sung

M. F.

Experimental study on the characterization of airflow effect on the direct methanol fuel cell. Renewable Energy, 2009, 34(8), 1962–1968.

Kim

M. U.

Kim

D. H.

Han

S. H.

Kim

Y. C.

Effects of nitrogen ion implantation on the surface properties of 316L stainless steel as bipolar plate for PEMFC. Kor. J. Met. Mater., 2009, 47(11), 722–727.

Choi

J. H.

Kim

M. H.

Kim

Y. J.

Fabrication of 316L stainless steel having low contact resistance for PEMFC separator using powder metallurgy. Kor. J. Met. Mater., 2008, 46(12), 817–822.

Padhy

B. R.

Reddy

R. G.

Performance of DMFC with SS 316 bipolar/end plates. J. Power Sources, 2006, 153(1), 125–129.

Chen

C. Y.

Shiu

J. Y.

Lee

Y. S.

Development of a small DMFC bipolar plate stack for portable applications. J. Power Sources, 2006, 159(2), 1042–1047.

10.

Bagotsky

V. S.

Direct liquid fuel cells. In Fuel cells – problems and solutions, ch. 4, 2009, pp. 73–74 (John Wiley & Sons, Inc. Hoboken, New Jersey).

11.

Casalegno

Marchesi

DMFC performance and methanol cross-over: experimental analysis and model validation. J. Power Sources, 2008, 185(1), 318–330.

12.

Zhao

T. S.

Chen

Yang

W. W.

Mass transport phenomena in direct methanol fuel cells. Prog. in Energy and Combust. Sci., 2009, 35(3), 275–292.

13.

Song

Deng

Chen

Rebuilding of metal components with laser cladding forming. Appl. Surf. Sci., 2006, 252(22), 7934–7940.

14.

Gusarove

A. V.

Kruth

J.-P.

Modelling of radiation transfer in metallic powders at laser treatment. Int. J. Heat and Mass Transfer, 2005, 48(16), 3423–3434.

15.

Kim

D. J.

Lee

J. Y.

Lim

T. H.

I. H.

H. Y.

Operational characteristics of a 50 W DMFC stack. J. Power Sources, 2006, 155(2), 203–212.