Additive manufacturing has facilitated the fabrication of orthopedic metal implants with interconnected pores. Recent reports have indicated that a pore size of 600 μm is beneficial for material-induced osteogenesis. However, the complete removal of the metal powder from such small pores of implants is extremely difficult especially in electron beam melting (EBM). We therefore developed a new type of Ti-6Al-4V implant with lattice-shaped interconnected pores measuring 880–1400 μm, which allowed for the easy removal of metal powder. This implant was fabricated by EBM and treated with NaOH, CaCl2, heat, and water (ACaHW treatment) to render the metal surface bioactivity. In the present study, the mechanical and chemical property of the implants and the biocompatibility were evaluated. The SEM and micro-CT images demonstrated the 3D interconnectivity of the porous structures. The average porosity of the porous titanium implant was 57.5%. The implant showed maximum compressive load of 78.9 MPa and Young's modulus of 3.57 GPa which matches that of human cortical bone. ACaHW treatment of the porous Ti-6Al-4V implants induced apatite formation in simulated body fluid in vitro. The ACaHW-treated porous implants harvested from rabbit femoral bone showed direct bonding of bone to the metal surface without interposition of fibrous tissue. The porous ACaHW-treated implant had a higher affinity to the bone than the untreated one. The mechanical strength of implant fixation assessed using the push-out test was significantly higher in the ACaHW-treated implant than in untreated one. FE-SEM analysis and EDX mapping after push-out test of solid implants showed a lot of bone tissue patches on the surface of the ACaHW-treated implant. These results suggest that the new ACaHW-treated Ti-6Al-4V implant with lattice-shaped interconnected pores is a superior alternative to conventional materials for medical application.
KokuboTYamaguchiS.Novel bioactive materials developed by simulated body fluid evaluation: surface-modified Ti metal and its alloys. Acta Biomater2016;
44: 16–30.
2.
NiinomiMNakaiMHiedaJ.Development of new metallic alloys for biomedical applications. Acta Biomater2012;
8: 3888–3903.
3.
KawanabeKIseKGotoK, et al.
A new cementless total hip arthroplasty with bioactive titanium porous-coating by alkaline and heat treatment: average 4.8-year results. J Biomed Mater Res B Appl Biomater2009;
90: 476–481.
4.
OchsnerPE.Osteointegration of orthopaedic devices. Semin Immunopathol2011;
33: 245–256.
AnsethSDPulidoPAAdelsonWS, et al.
Fifteen-year to twenty-year results of cementless Harris-Galante porous femoral and Harris-Galante porous I and II acetabular components. J Arthroplasty2010;
25: 687–691.
7.
McLaughlinJRLeeKR.Cementless total hip replacement using second-generation components: a 12- to 16-year follow-up. J Bone Joint Surg Br2010;
92: 1636–1641.
8.
RyanGPanditAApatsidisDP.Fabrication methods of porous metals for use in orthopaedic applications. Biomaterials2006;
27: 2651–2670.
9.
LiuCKJingCXTanXY, et al.
Using three-dimensional porous internal titanium scaffold or allogenic bone scaffold for tissue-engineering condyle as a novel reconstruction of mandibular condylar defects. J Med Hypo Ideas2014;
8: 69–73.
10.
de WildMSchumacherRMayerK, et al.
Bone regeneration by the osteoconductivity of porous titanium implants manufactured by selective laser melting: a histological and micro computed tomography study in the rabbit. Tissue Eng Part A2013;
19: 2645–2654.
11.
WarnkePHDouglasTWollnyP, et al.
Rapid prototyping: porous titanium alloy scaffolds produced by selective laser melting for bone tissue engineering. Tissue Eng Part C Methods2009;
15: 115–124.
12.
KawaseMHayashiTAsakuraM, et al.
Cell proliferation ability of mouse fibroblast-like cells and osteoblast-like cells on a Ti-6Al-4V alloy film produced by selective laser melting. Mater Sci Appl2014;
05: 475–483.
13.
de PeppoGMPalmquistABorchardtP, et al.
Free-form-fabricated commercially pure Ti and Ti6Al4V porous scaffolds support the growth of human embryonic stem cell-derived mesodermal progenitors. Scientif World J2012;
2012: 646417.
14.
HrabeNWHeinlPBordiaRK, et al.
Maintenance of a bone collagen phenotype by osteoblast-like cells in 3D periodic porous titanium (Ti-6Al-4 V) structures fabricated by selective electron beam melting. Connect Tissue Res2013;
54: 351–360.
SingSLAnJYeongWY, et al.
Laser and electron-beam powder-bed additive manufacturing of metallic implants: a review on processes, materials and designs. J Orthop Res2016;
34: 369–385.
17.
KarageorgiouVKaplanD.Porosity of 3D biomaterial scaffolds and osteogenesis. Biomaterials2005;
26: 5474–5491.
18.
Van BaelSChaiYCTruscelloS, et al.
The effect of pore geometry on the in vitro biological behavior of human periosteum-derived cells seeded on selective laser-melted Ti6Al4 V bonescaffolds. Acta Biomater2012;
8: 2824–2834.
19.
HaraDNakashimaYSatoT, et al.
Bone bonding strength of diamond-structured porous titanium-alloy implants manufactured using the electron beam-melting technique. Mater Sci Eng C Mater Biol Appl2016;
59: 1047–1052.
20.
FukudaATakemotoMSaitoT, et al.
Osteoinduction of porous Ti implants with a channel structure fabricated by selective laser melting. Acta Biomater2011;
7: 2327–2336.
21.
FujibayashiSNeoMKimHM, et al.
Osteoinduction of porous bioactive titanium metal. Biomaterials2004;
25: 443–450.
22.
TaniguchiNFujibayashiSTakemotoM, et al.
Effect of pore size on bone ingrowth into porous titanium implants fabricated by additive manufacturing: an in vivo experiment. Mater Sci Eng C Mater Biol Appl2016;
59: 690–701.
23.
BenazzoFBottaLScaffinoMF, et al.
Trabecular titanium can induce in vitro osteogenic differentiation of human adipose derived stem cells without osteogenic factors. J Biomed Mater Res A2014;
102: 2061–2071.
24.
ColenSHarakeRDe HaanJ, et al.
A modified custom-made triflanged acetabular reconstruction ring (MCTARR) for revision hip arthroplasty with severeacetabular defects. Acta Orthop Belg2013;
79: 71–75.
25.
HunterLWBrackettDBrierleyN, et al.
Assessment of trapped powder removal and inspection strategies for powder bed fusion techniques. Int J Adv Manuf Technol2020;
106: 4521–4532.
26.
KokuboTYamaguchiS.Bioactive titanate layers formed on titanium and its alloys by simple chemical and heat treatments. Open Biomed Eng J2015;
9: 29–41.
27.
De GrootKGeesinkRKleinC, et al.
Plasma sprayed coatings of hydroxyapatite. J Biomed Mater Res1987;
21: 1375–1381.
28.
KleinCPPatkaPvan der LubbeHB, et al.
Plasma-sprayed coatings of tetracalciumphosphate, hydroxyl-apatite, and alpha-TCP on titanium alloy: an interface study. J Biomed Mater Res1991;
25: 53–65.
29.
FukudaATakemotoMSaitoT, et al.
Bone bonding bioactivity of Ti metal and Ti-Zr-Nb-Ta alloys with Ca ions incorporated on their surfaces by simple chemical and heat treatments. Acta Biomater2011;
7: 1379–1386.
30.
TianYFujibayashiSYamaguchiS, et al.
In vivo study of the early bone-bonding ability of Ti meshes formed with calcium titanate via chemical treatments. J Mater Sci Mater Med2015;
26: 271.
31.
AkedaKYamaguchiSMatsushitaT, et al.
Bioactive pedicle screws prepared by chemical and heat treatments improved biocompatibility and bone-bonding ability in canine lumbar spines. PLoS One2018;
13: e0196766.
32.
KizukiTTakadamaHMatsushitaT, et al.
Preparation of bioactive Ti metal surface enriched with calcium ions by chemical treatment. Acta Biomater2010;
6: 2836–2842.
33.
VillanuevaARMehrLA.Modifications of the Goldner and Gomori one-step trichrome stains for plastic-embedded thin sections of bone. Am J Med Technol1977;
43: 536–538.
34.
FujibayashiSNeoMKimHM, et al.
A comparative study between in vivo bone ingrowth and in vitro apatite formation on Na2O–CaO–SiO2 glasses. Biomaterials2003;
24: 1349–1356.
35.
NishiguchiSKatoHFujitaH, et al.
Titanium metals form direct bonding to bone after alkali and heat treatments. Biomaterials2001;
22: 2525–2533.
36.
TrevisanFCalignanoFAversaA, et al.
Additive manufacturing of titanium alloys in the biomedical field: processes, properties and applications. J Appl Biomater Funct Mater2018;
16: 57–67.
37.
BallaVKBodhakSBoseS, et al.
Porous tantalum structures for bone implants: fabrication, mechanical and in vitro biological properties. Acta Biomater2010;
6: 3349–3359.
38.
WillieBMYangXKellyNH, et al.
Osseointegration into a novel titanium foam implant in the distal femur of a rabbit. J Biomed Mater Res B Appl Biomater2010;
92: 479–488.
39.
TakemotoMFujibayashiSNeoM, et al.
Mechanical properties and osteoconductivity of porous bioactive titanium. Biomaterials2005;
26: 6014–6023.
40.
TakemotoMFujibayashiSNeoM, et al.
A porous bioactive titanium implant for spinal interbody fusion: an experimental study using a canine model. J Neurosurg Spine2007;
7: 435–443.
41.
XueWKrishnaBVBandyopadhyayA, et al.
Processing and biocompatibility evaluation of laser processed porous titanium. Acta Biomater2007;
3: 1007–1018.
42.
ArjunanADemetriouMBaroutajiA, et al.
Mechanical performance of highly permeable laser melted Ti6Al4V bone scaffolds. J Mech Behav Biomed Mater2020;
102: 103517.
43.
IbrahimHEsfahaniSNPoorganjiB, et al.
Resorbable bone fixation alloys, forming, and post-fabrication treatments. Mater Sci Eng C Mater Biol Appl2017;
70: 870–888.
44.
YamaguchiSTakadamaHMatsushitaT, et al.
Apatite-forming ability of Ti-15Zr-4Nb-4Ta alloy induced by calcium solution treatment. J Mater Sci Mater Med2010;
21: 439–444.
45.
TanakaMTakemotoMFujibayashiS, et al.
Bone bonding ability of a chemically and thermally treated low elastic modulus Ti alloy: gum metal. J Mater Sci Mater Med2014;
25: 635–643.