Biocompatibility and biodegradation properties of polycaprolactone/polydioxanone composite scaffolds prepared by blend or co-electrospinning

Abstract

Electrospun polymer scaffolds are regarded as an ideal tissue engineering scaffold due to similar morphological properties with the native extracellular matrix. Among these, polycaprolactone is widely used to fabricate electrospun fibrous scaffolds due to its excellent biocompatibility, good mechanical properties, and ease of manufacture. However, its low biodegradation rate has a negative influence on its application in tissue engineering scaffold. To address this issue, this study prepared hybrid scaffolds composed of polycaprolactone and polydioxanone (a fast-degrading polyether-ester) via either the blend or co-electrospinning. Subsequently, the structural characteristics, mechanical strength, in vitro/vivo degradation, cellularization, and vascularization of two kinds of hybrid scaffolds were evaluated to decide which method is more suitable for producing tissue engineering scaffolds. The incorporation of polydioxanone increased the mechanical strength of both composite scaffolds. Moreover, co-electrospun scaffolds exhibited improved hydrophilicity compared to blend scaffolds. The results of in vitro and in vivo degradation studies showed that the degradation rate of both composite scaffolds was faster than that of neat polycaprolactone scaffolds due to the incorporated polydioxanone component. Especially in co-electrospun scaffolds, the fast degradation of polydioxanone fiber gave rise to larger pore size, thus leading to faster cellularization and better vascularization compared to blend scaffolds. Therefore, co-electrospinning was demonstrated to be superior to blend electrospinning for the preparation of composite scaffolds. Co-electrospun polycaprolactone–polydioxanone scaffolds may be promising candidates for tissue engineering.

Keywords

Polycaprolactone polydioxanone co-electrospinning blend degradation

Get full access to this article

View all access options for this article.

References

Kannan

Salacinski

Butler

et al . Current status of prosthetic bypass grafts: a review. J Biomed Mater Res B Appl Biomater 2005; 74B: 570–581.

Middleton

Tipton

. Synthetic biodegradable polymers as orthopedic devices. Biomaterials 2000; 21: 2335–2346.

Kumari

Yadav

. Biodegradable polymeric nanoparticles based drug delivery systems. Colloid Surface B 2010; 75: 1–18.

Soppimath

Aminabhavi

Kulkarni

et al . Biodegradable polymeric nanoparticles as drug delivery devices. J Control Release 2001; 70: 1–20.

Nair

Laurencin

. Biodegradable polymers as biomaterials. Prog Polym Sci 2007; 32: 762–798.

Piskin

. Biodegradable polymers as biomaterials. J Biomater Sci Polym Ed 1995; 6: 775–795.

Yao

Liu

Ding

et al . Preparation and characterization of silk fibroin/poly(l-lactide-co-ε-caprolactone) nanofibrous membranes for tissue engineering applications. J Bioact Compat Pol 2015; 30: 633–648.

Puppi

Piras

Detta

et al . Poly(vinyl alcohol)-based electrospun meshes as potential candidate scaffolds in regenerative medicine. J Bioact Compat Pol 2010; 26: 20–34.

Sun

Yang

et al . Bioactive electrospun scaffolds delivering growth factors and genes for tissue engineering applications. Pharm Res 2010; 28: 1259–1272.

10.

Yang

Seyednejad

et al . Biocompatibility and degradation characteristics of PLGA-based electrospun nanofibrous scaffolds with nanoapatite incorporation. Biomaterials 2012; 33: 6604–6614.

11.

Agarwal

Wendorff

Greiner

. Use of electrospinning technique for biomedical applications. Polymer 2008; 49: 5603–5621.

12.

Zheng

Wang

Song

et al . Endothelialization and patency of RGD-functionalized vascular grafts in a rabbit carotid artery model. Biomaterials 2012; 33: 2880–2891.

13.

Pektok

Nottelet

Tille

et al . Degradation and healing characteristics of small-diameter poly(epsilon-caprolactone) vascular grafts in the rat systemic arterial circulation. Circulation 2008; 118: 2563–2570.

14.

De Valence

Tille

Mugnai

et al . Long term performance of polycaprolactone vascular grafts in a rat abdominal aorta replacement model. Biomaterials 2012; 33: 38–47.

15.

Wang

Cui

Wang

et al . The effect of thick fibers and large pores of electrospun poly(epsilon-caprolactone) vascular grafts on macrophage polarization and arterial regeneration. Biomaterials 2014; 35: 5700–5710.

16.

Qin

Wang

et al . The regeneration of macro-porous electrospun poly(varepsilon-caprolactone) vascular graft during long-term in situ implantation. J Biomed Mater Res B Appl Biomater 2018; 106: 1618–1627.

17.

Norotte

Marga

Niklason

et al . Scaffold-free vascular tissue engineering using bioprinting. Biomaterials 2009; 30: 5910–5917.

18.

Azevedo

Mano

Alves

. Development of new poly(ϵ-caprolactone)/chitosan films. Polym Int 2013; 62: 1425–1432.

19.

Aghdam

Najarian

Shakhesi

et al . Investigating the effect of PGA on physical and mechanical properties of electrospun PCL/PGA blend nanofibers. J Appl Polym Sci 2011; 124: 123–131.

20.

McDonald

Lyons

Geever

et al . In vitro degradation and drug release from polymer blends based on poly(dl-lactide), poly(l-lactide-glycolide) and poly(ε-caprolactone). J Mater Sci 2010; 45: 1284–1292.

21.

Ding

Kimura

Sato

et al . Fabrication of blend biodegradable nanofibrous nonwoven mats via multi-jet electrospinning. Polymer 2004; 45: 1895–1902.

22.

Baker

Gee

Metter

et al . The potential to improve cell infiltration in composite fiber-aligned electrospun scaffolds by the selective removal of sacrificial fibers. Biomaterials 2008; 29: 2348–2358.

23.

Park

Kim

et al . Degradation behavior of 3D porous polydioxanone-b-polycaprolactone scaffolds fabricated using the melt-molding particulate-leaching method. J Biomater Sci Polym Ed 2011; 22: 225–237.

24.

Kim

H-K

et al . In vitro and in vivo degradation behaviors of synthetic absorbable bicomponent monofilament suture prepared with poly(p-dioxanone) and its copolymer. Polym Degrad Stab 2007; 92: 667–674.

25.

Kalfa

Bel

Chen-Tournoux

et al . A polydioxanone electrospun valved patch to replace the right ventricular outflow tract in a growing lamb model. Biomaterials 2010; 31: 4056–4063.

26.

Boland

Coleman

Barnes

et al . Electrospinning polydioxanone for biomedical applications. Acta Biomater 2005; 1: 115–123.

27.

Wang

Chen

Pan

et al . Enhanced vascularization in hybrid PCL/gelatin fibrous scaffolds with sustained release of VEGF. Biomed Res Int 2015; 2015: 865076.

28.

Wang

Zhang

Wang

et al . Fabrication and properties of the electrospun polylactide/silk fibroin-gelatin composite tubular scaffold. Biomacromolecules 2009; 10: 2240–2244.

29.

Baker

Handorf

Ionescu

et al . New directions in nanofibrous scaffolds for soft tissue engineering and regeneration. Expert Rev Med Devices 2009; 6: 515–532.

30.

Zhang

Venugopal

et al . Biomimetic and bioactive nanofibrous scaffolds from electrospun composite nanofibers. Int J Nanomed 2007; 2: 623–638.

31.

Pham

Sharma

Mikos

. Electrospun poly (ε-caprolactone) microfiber and multilayer nanofiber/microfiber scaffolds: characterization of scaffolds and measurement of cellular infiltration. Biomacromolecules 2006; 7: 2796–2805.

32.

Kister

Cassanas

Bergounhon

et al . Structural characterization and hydrolytic degradation of solid copolymers of D,L-lactide-co-ε-caprolactone by Raman spectroscopy. Polymer 2000; 41: 925–932.

33.

Jaidann

Brisson

. Conformation study of poly(p-dioxanone) fibers by polarized Raman spectroscopy, X-ray diffraction, and conformation analysis. J Polym Sci Pol Phys 2008; 46: 406–417.

34.

H-Y

Jing

Turng

L-S

. Fabrication of porous synthetic polymer scaffolds for tissue engineering. J Cell Plast 2014; 51: 165–196.

35.

Wang

Zhang

et al . Functionalization of the surface of electrospun poly(epsilon-caprolactone) mats using zwitterionic poly(carboxybetaine methacrylate) and cell-specific peptide for endothelial progenitor cells capture. Mater Sci Eng C 2013; 33: 1646–1653.

36.

Brito

Sabino

Ronca

et al . Changes in crystalline morphology, thermal, and mechanical properties with hydrolytic degradation of immiscible biodegradable PPDX/PCL blends. J Appl Polym Sci 2008; 110: 3848–3858.

37.

Yang

Zhao

Tang

et al . In vitro degradation of porous poly(L-lactide-co-glycolide)/β-tricalcium phosphate (PLGA/β-TCP) scaffolds under dynamic and static conditions. Polym Degrad Stabil 2008; 93: 1838–1845.

38.

Bosworth

Downes

. Physicochemical characterisation of degrading polycaprolactone scaffolds. Polym Degrad Stabil 2010; 95: 2269–2276.

39.

Bölgen

Menceloğlu

Acatay

et al . In vitro and in vivo degradation of non-woven materials made of poly(ε-caprolactone) nanofibers prepared by electrospinning under different conditions. J Biomater Sci Polym Ed 2005; 16: 1537–1555.

40.

Kobayashi

Terada

Yokoyama

et al . Vascular-inducing poly(glycolic acid)-collagen nanocomposite-fiber scaffold. J Biomed Nanotechnol 2013; 9: 1318–1326.

41.

Takahashi

Tabata

. Effect of the fiber diameter and porosity of non-woven PET fabrics on the osteogenic differentiation of mesenchymal stem cells. J Biomater Sci Polym Ed 2004; 15: 41–57.

42.

Murphy

Haugh

O’Brien

. The effect of mean pore size on cell attachment, proliferation and migration in collagen–glycosaminoglycan scaffolds for bone tissue engineering. Biomaterials 2010; 31: 461–466.

43.

Wang

Zhu

et al . Improvement of cell infiltration in electrospun polycaprolactone scaffolds for the construction of vascular grafts. J Biomed Nanotechnol 2014; 10: 1588–1598.

44.

Yannas

. Tissue regeneration by use of collagen-glycosaminoglycan copolymers. Clin Mater 1992; 9: 179–187.

45.

Karageorgiou

Kaplan

. Porosity of 3D biomaterial scaffolds and osteogenesis. Biomaterials 2005; 26: 5474–5491.

46.

Sukmana

. Microvascular guidance: a challenge to support the development of vascularised tissue engineering construct. Sci World J 2012; 2012: 201352.

47.

Donos

Hamlet

Lang

et al . Gene expression profile of osseointegration of a hydrophilic compared with a hydrophobic microrough implant surface. Clin Oral Implan Res 2011; 22: 365–372.

48.

Feng

Jinkang

Zhen

et al . The effect of pore size on tissue ingrowth and neovascularization in porous bioceramics of controlled architecture in vivo. Biomed Mater 2011; 6: 015007.