Ethylene vinyl acetate/copper sulphide with near-infrared light active shape memory behavior

Abstract

This thesis presents the preparation of ethylene vinyl acetate (EVA)-based shape memory polymer composites (SMPC) (EVA/CuS) with near-infrared light photo-thermal response. The composites were prepared using EVA as the matrix material and copper sulphide (CuS) particles as the functional phase. The designability of SMPs was considered in the preparation of these composites. The results demonstrated that the incorporation of CuS, as a functional phase, enhanced the cross-linking degree and augmented the shape memory properties of EVA. Additionally, it served as a photo-thermal functional filler, imparting its photo-thermal properties. It can be observed that as the quantity of CuS particles incorporated into the EVA/CuS composite film increases, the photothermal conversion performance of the composite film improves, the shape fixation rate rises, and the rate of recovery of light-responsive shape memory accelerates. The temperature of the composites increased to 116.7°C in 20 s when the CuS addition was 2 wt% and the NIR light intensity was 0.5 W/cm². At a NIR light intensity of 0.6 W/cm², the “U” shape of the sample was restored to a straight state in 30 s, and the shape recovery rate reached 100%. In this experiment, optical near-infrared photostimulation-responsive EVA/CuS composites have been successfully prepared. These composites demonstrate the ability to achieve remote control and fast response of EVA shape memory behavior, offering a new avenue for the preparation of photo-responsive EVA-based shape memory materials.