The polyurethane (PU)/silicone rubber dynamic vulcanizated elastomer was prepared using Pt catalyst and organohydrido silicone compound as cross-linking agent. The effect of segmented PU modified by hydroxyalkyl functional polydimethylsiloxane (Si–PU) as a compatibilizer was investigated. It is found that simple blend shows co-continuous structure and worse mechanical properties. After dynamic vulcanization, the elongation at break improved to 745.8% when the contents of catalyst and cross-linking agent are 0.12 phr and 1.65 phr, respectively. The introduction of Si–PU in 4.5 phr further improves the value to 942.6% and the sizes of cross-linked rubber dispersed in the continuous PU matrix are less than 8 μm. Si–PU copolymer shows better compatibilization effect.
DeSKBhowmickAK. Thermoplastic elastomers from rubber–plastic blends. New York, NY: Ellis Horwood, 1990.
3.
VanDM. Crosslinking systems for EPDM/PP-based thermoplastic vulcanizates. Presented at the International rubber conference. Birmingham, England, 2001.
4.
MartinGCBarresPS. Morphology development in thermoplastic vulcanizates (TPV): dispersion mechanisms of a pre-crosslinked EPDM phase. Eur Polym J2009; 45(11): 3257–3268.
5.
MachadoAVVanDM. Dynamic vulcanization of EPDM/PE-based thermoplastic vulcanizates studied along the extruder axis. Polymer2005; 46(17): 6575–6586.
6.
GeorgeSRamamurthyKAnandJSGroeninckxGVarugheseKTThomasS. Rheological behavior of thermoplastic elastomers from polypropylene/acrylonitrile–butadiene rubber blends: effect of blend ratio, reactive compatibilization and dynamic vulcanization. Polymer1999; 40(15): 4325–4344.
7.
MartinPMaquetC. Conjugated effects of the compatibilization and the dynamic vulcanization on the phase inversion behavior in poly(butylene terephthalate)/epoxide-containing rubber reactive polymer blends. Polymer2004; 45(15): 5111–5125.
8.
OderkerkJGroeninckxG. Morphology development by reactive compatibilization and dynamic vulcanization of nylon6/EPDM blends with a high rubber fraction. Polymer2002; 43(8): 2219–2228.
9.
PapkeNKarger-KocsisJ. Thermoplastic elastomers based on compatibilized poly(ethylene terephthalate) blends: effect of rubber type and dynamic curing. Polymer2001; 42: 1109–1120.
10.
HuYWangYLGongXL. New magnetorheological elastomers based on polyurethane/Si-rubber hybrid. Polym Test2005; 24: 324–329.
11.
MaityMKhatuaBB. Polyblend systems of polyurethane rubber and silicone rubber in the presence of silane grafting agent. J Elastom Plast2001; 33(1): 211–225.
12.
GeraldAGCraigSGMarkDH. Thermoplastic polyurethane–silicone elastomers, US patent 6759487, 2004.
13.
YilgorIMcGrathJE. Polysiloxane-containing copolymers: a survey of recent developments. Adv Polym Sci1988; 86: 1–87.
TyagiDYilgorIMcGrathJEWilkesGL. Segmented organosiloxane copolymers: 2. Thermal and mechanical properties of siloxane-urea copolymers. Polymer1984; 25(12): 1807–1816.
16.
YilgorIEynurTYilgorE. Contribution of soft segment entanglement on the tensile properties of silicone–urea copolymers with low hard segment contents. Polymer2009; 50: 4432–4437.
17.
WangLFJiQ. Glass synthesis and characterization of organosiloxane modified segmented polyether polyurethanes. Polymer2000; 41: 5083–5093.
FanQLFangJLCheoQMYuXH. Synthesis and properties of polyurethane modified with aminoethylaminopropylpoly(dimethylsiloxane). J Appl Polym Sci1999; 74(6): 2552–2558.
20.
ChuangFSTsenWCShuYC. The effect of different siloxane chain-extenders on the thermal degradation and stability of segmented polyurethanes. Polym Degrad Stabil2004; 84(1): 69–77.
21.
ShibayamaMSuetsuguMSakuraiSYamamotoTNomuraS. Structure characterization of polyurethanes containing poly(dimethylsiloxane). Macromolecules1991; 24(23): 6254–6262.
22.
LeiCHLiSLHuangWLXuRJXuYQ. Phase structure control of TPU/silicone rubber TPV. Plast Ind2011; 7: 92–94.
23.
FengXYZhangYHChenL. Preparation and properties of dynamically vulcanized thermoplastic elastomers based on VMQ and LLDPE. China Elastom2007; 2: 42–45.
24.
TangBEHaoZGPanHM. Study on vulcanization process of silicone addition rubber. Spec Purpose Rubber Prod2000; 21(4): 9–12.
25.
WuS. Formation of dispersed phase in incompatible polymer blends: interfacial and rheological effects. Polym Eng Sci1987; 27(5): 335–343.