Influence of void content on the flexural fracture behaviour of carbon fiber reinforced polypropylene

Abstract

In order to investigate the influence of void content on the fracture behaviour of carbon fiber reinforced polypropylene (CF/PP), we investigated the relationship between the mechanical properties of carbon fiber reinforced thermoplastics and their void content using CF/PP prepreg sheet and partially impregnated sheet. Two types of flexural properties of cross-ply (CP) plates and chopped carbon fiber tape reinforced thermoplastic (CTT) plates with different void contents were measured by three-point bending tests. The flexural strength of CP specimens decreased drastically when their void content became higher than 1%, whereas the flexural strength of the CTT specimens decreased gradually with an increase in void content. Un-impregnated regions in the composites resulted in small dotted defects under loading conditions, although they were only found on the tape along the longitudinal direction in the case of CTT. In addition, a larger number of defects was observed on CP and CTT specimens with lower strengths. Therefore, cyclic loading tests were conducted to observe flexural fracture behaviour in more detail to elucidate the reason behind voids causing a decrease in strength. During these tests, the dotted defects in the CP specimens were shown to be connected along the in-plane transverse direction, while those in the CTT specimen propagated along the second layered tape.

Keywords

Carbon fiber thermoplastics impregnation void content

Get full access to this article

View all access options for this article.

References

Takahashi J and Ishikawa T. Recent Japanese activity in CFRTP for mass production automobile. In: Proceedings of ITHEC 2014, Bremen, Germany, 27–28 October 2014.

Takahashi J and Ishikawa T. Next challenge in CFRTP for mass production automotive application. In: Proceedings of SAMPE SEICO 14, Paris, France, 10–11 March 2014, pp. 181–188.

TAPAS Project homepage, http://www.tapasproject.nl/en/technologies (accessed 5 May 2016).

Gebart

. Permeability of unidirectional reinforcements for RTM. J Compos Mater 1992; 26: 100–133.

Calado

Advani

. Effective average permeability of multi-layer preforms in resin transfer molding. Compos Sci Tech 1996; 56: 519–531.

Gutowski

Cai

Bauer

et al.

Consolidation experiments for laminate composites. J Compos Mater 1987; 21: 650–669.

Bernet

Michaud

Bourban

et al.

An impregnation model for the consolidation of thermoplastic composites made from commingled yarns. J Compos Mater 1999; 33: 751–772.

Chang

Lees

. Recent development in thermoplastic composites: a review of matrix systems and processing methods. J Thermoplast Compos 1988; 1: 277–296.

Ijaz

Robinson

Wright

PNH

et al.

Vacuum consolidation of commingled thermoplastic matrix composites. J Compos Mater 2007; 41: 243–262.

10.

Klinkmuller

Friedrich

. Impregnation and consolidation in composites made of GF/PP powder impregnated bundles. J Thermoplast Compos 1992; 5: 32–48.

11.

Bates

Ekhator

. Continuous consolidation of commingled glass and polypropylene roving. J Reinf Plast Comp 2004; 23: 1409–1424.

12.

Kanesaki

Saito

Tanaka

et al.

Improvement of CAI strength and its mechanisms on CFRTP laminate with thinning in ply-thicknes. J Jpn Soc Compos Mater 2013; 39: 89–98.

13.

TenCate. Product data sheet – TenCate Cetex® TC1200 PEEK resin system, http://www.tencate.com/emea/Images/CETEX-TC1200_DS_071515_Web_tcm28-3782.pdf (accessed 5 May 2016).

14.

TenCate. Technical data sheet -Out of autoclave (OOA) prepreg dystems, http://www.tencate.com/emea/Images/TCAC_OutofAutoclave_V4.1_032316_Web_tcm28-33680.pdf (accessed 5 May 2016).

15.

Yoshida

Ogasa

Hayashi

. Statistical approach to the relationship between ILSS and void content of CFRP. Compos Sci Technol 1986; 25: 3–18.

16.

Frascino

Almeida

. Effect of void content on the strength of composite laminates. Compos Struct 1994; 28: 139–148.

17.

Sisodia

Garcea

Fullwood

et al.

High-resolution computed tomography in resin infused woven carbon fiber composites with voids. Comp Sci Tech 2016; 131: 12–21.

18.

Sisodia SM, Mavrogordato M, George A, et al. Characterisation of voids and their influence on damage propagation in resin infused carbon fiber reinforced polymers. Proceedings of ICCM20, Copenhagen, Denmark, 19–24 July 2015.

19.

Sisodia SM, Gamstedt EK, Edgren F, et al. Effects of voids on quasi-static and tension fatigue behaviour of carbon-fiber composite laminates. J Compos Mater 2015; 49: 2137–2148.

20.

Sato Y, Takahashi J, Matsuo T, et al. Elastic modulus estimation of chopped carbon fiber tape reinforced thermoplastics using the Monte Carlo simulation. In: Proceedings of ICCM19, Montreal, Canada, 28 July–2 August 2013, pp. 6718–6725.

21.

Yamashita S, Nakashima Y, Takahashi J, et al. Tape length dependence of the electrical conductivity of ultra-thin chopped carbon fiber tape reinforced thermoplastics. In: Proceedings of the 14th Japan International SAMPE Symposium and Exhibition, Kanazawa, Japan, 6–9 December 2015.

22.

ASTM D790-15. Standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating materials, West Conshohocken: American Society for Testing of Materials, 2015.

23.

ASTM D2734-09. Standard test methods for void content of reinforced plastics, West Conshohocken: American Society for Testing of Materials, 2009.

24.

ASTM D792-13. Standard test methods for density and specific gravity (relative density) of plastics by displacement, West Conshohocken: American Society for Testing of Materials, 2013.