In this study, the behaviour of the micrometric particles of the AA2198-T8 alloy during anodising at various voltages and the effect of anodising voltage on the anodised surface morphology have been investigated in a tartaric-sulfuric acid anodising solution. The results were compared with that of the AA2024-T3 alloy. For the AA2198-T8 alloy, partial dissolution of these particles occurred at 0, 3 and 4 V. Besides, for potentials above 5 V, there is a preferential dissolution of the intermetallic particles. For the AA2024-T3 alloy, the results indicated a total dissolution of the micrometric particles at 0 V and a partial dissolution at 3 V, whereas above 4 V total dissolution occurred. Between 1 and 2 V, no dissolution was observed for both alloys. The preferential dissolution of the micrometric particles resulted in defects in the anodic film and cavities on the anodised surfaces.
BalboAFrignaniAGrassiV. Corrosion inhibition by anionic surfactants of AA2198 Li-containing aluminium alloy in chloride solutions. Corros Sci. 2013; 73: 80–88. doi: 10.1016/j.corsci.2013.03.027.
2.
AstaritaATucciFSilvestriAT. Dissimilar friction stir lap welding of AA2198 and AA7075 sheets: forces, microstructure and mechanical properties. Int J Adv Manuf Technol. 2021; 117: 1045–1059. doi: 10.1007/s00170-021-07816-7.
3.
WarnerT.Recently-developed aluminium solutions for aerospace applications. Mater Sci Forum. 2006; 519-521: 1271–1278. doi: 10.4028/www.scientific.net/MSF.519-521.1271.
4.
MoretoJAGamboniOCMarinoCEB. Corrosion behavior of Al and Al-Li alloys used as aircraft materials. Corros Prot Mater. 2012; 31: 60–64.
5.
CavalierePCabibboMPanellaF. 2198 Al–Li plates joined by friction stir welding: mechanical and microstructural behavior. Mater Des. 2009; 30: 3622–3631. doi: 10.1016/j.matdes.2009.02.021.
6.
GarnerATromansD.Direct observation of intergranular corrosion in AI-4 Wt% Cu alloy. Corrosion. 1979; 35: 55–60. doi: 10.5006/0010-9312-35.2.55.
7.
ChenYPanXZhangC. Influence of foreign object impact mode on fatigue performance of 2198-T8 Al-Li alloy thin sheets for fuselage. Fatigue Fract Eng Mater Struct. 2021; 44: 115–128. doi: 10.1111/ffe.13338.
8.
GloriaAMontanariRRichettaM. Alloys for aeronautic applications : state of the Art and perspectives. Metals. 2019; 662: 1–26. doi: 10.3390/met9060662.
9.
GuanRLouHHuangH. Development of aluminum alloy materials: current status, trend, and prospects. Chinese J Eng Sci. 2020; 22: 68. doi: 10.15302/J-SSCAE-2020.05.013.
10.
WangWZhangL.Demand of China's aeronautics industry for Al-Li alloy. Nonferrous Met Proc (In Chinese). 2019; 48: 7–10.
11.
de Sousa AraujoJVde FABugarinS. Thermomechanical treatment and corrosion resistance correlation in the AA2198 Al–Cu–Li alloy. Corros Eng Sci Technol. 2019; 54: 575–586. doi: 10.1080/1478422X.2019.1637077.
12.
BuchheitRG.Local dissolution phenomena associated with S phase (Al2CuMg) particles in aluminum Alloy 2024-T3. J Electrochem Soc. 1997; 144: 2621. doi: 10.1149/1.1837874.
13.
KowalKDeLucciaJJosefowiczJY. In situ atomic force microscopy observations of the corrosion behavior of aluminum-copper alloys. J Electrochem Soc. 1996; 143: 2471–2481. doi: 10.1149/1.1837033.
14.
LiaoRPWCMOliveJMGaoM.In-situ monitoring of pitting corrosion in aluminium alloy 2024. Corrosion. 1998; 54: 451–458.
15.
RaoACUVasuVGovindarajuM. Stress corrosion cracking behaviour of 7xxx aluminum alloys: A literature review. Trans Nonferrous Met Soc China (English Ed). 2016; 26: 1447–1471. doi: 10.1016/S1003-6326(16)64220-6.
16.
de Sousa AraujoJVDonatusUQueirozFM. On the severe localized corrosion susceptibility of the AA2198-T851 alloy. Corros Sci. 2018; 133: 132–140. doi: 10.1016/j.corsci.2018.01.028.
17.
de Souza Carvalho MachadoCDonatusUMilagreMX. Correlating the modes of corrosion with microstructure in the friction stir welded AA2198-T8 alloy in aqueous hydrogen peroxide-chloride medium. Corrosion. 2019; 75: 628–640. doi: 10.5006/3054.
18.
BoagAHughesAGlennA.Corrosion of AA2024-T3 part I: localised corrosion of isolated IM particles. Corros Sci. 2011; 53: 17–26. doi: 10.1016/j.corsci.2010.09.009.
19.
GlennAMusterTLuoC. Corrosion of AA2024-T3 Part III: propagation. Corros Sci. 2011; 53: 40–50. doi: 10.1016/j.corsci.2010.09.035.
20.
QueirozFMMagnaniMCostaI. Investigation of the corrosion behaviour of AA 2024-T3 in low concentrated chloride media. Corros Sci. 2008; 50: 2646–2657. doi: 10.1016/j.corsci.2008.06.041.
21.
BirbilisNZhuYMKairySK. A closer look at constituent induced localised corrosion in Al-Cu-Mg alloys. Corros Sci. 2016; 113: 160–171. doi: 10.1016/j.corsci.2016.10.018.
22.
HughesABoagAGlennA.Corrosion of AA2024-T3 Part II: co-operative corrosion. Corros Sci. 2011; 53: 27–39. doi: 10.1016/j.corsci.2010.09.030.
23.
VukmirovicMBDimitrovNSieradzkiK.Dealloying and corrosion of Al alloy 2024-T3. J Electrochem Soc. 2002; 149: B428. doi: 10.1149/1.1498258.
24.
MilagreMXDonatusUMachadoCSC. Comparison of the corrosion resistance of an Al–Cu alloy and an Al–Cu–Li alloy. Corros Eng Sci Technol. 2019; 54: 402–412. doi: 10.1080/1478422X.2019.1605472.
25.
BlancCLavelleBMankowskiG.The role of precipitates enriched with copper on the susceptibility to pitting corrosion of the 2024 aluminium alloy. Corros Sci. 1997; 39: 495–510. doi: 10.1016/S0010-938X(97)86099-4.
26.
LacroixLRessierLBlancC. Combination of AFM, SKPFM, and SIMS to study the corrosion behavior of S-phase particles in AA2024-T351. J Electrochem Soc. 2008; 155: 131–137. doi: 10.1149/1.2833315.
27.
LarignonCAlexisJAndrieuE. Combined Kelvin probe force microscopy and secondary ion mass spectrometry for hydrogen detection in corroded 2024 aluminium alloy. Electrochim Acta. 2013; 110: 484–490. doi: 10.1016/j.electacta.2013.02.063.
28.
QueirozFMDe MeloHGCostaI.Effect of intermetallics on the corrosion of Al 2024-T3 alloy in solutions with different chloride concentration. Mater Sci Forum. 2008; 587-588: 415–419. doi: 10.4028/www.scientific.net/msf.587-588.415.
29.
long MaYrong ZhouXmin MengX. Influence of thermomechanical treatments on localized corrosion susceptibility and propagation mechanism of AA2099 Al–Li alloy. Trans Nonferrous Met Soc China. 2016; 26: 1472–1481. doi: 10.1016/S1003-6326(16)64252-8.
30.
MoretoJAMarinoCEBBose FilhoWW. SVET, SKP and EIS study of the corrosion behaviour of high strength Al and Al-Li alloys used in aircraft fabrication. Corros Sci. 2014; 84: 30–41. doi: 10.1016/j.corsci.2014.03.001.
31.
MaYZhouXLiaoY. Localised corrosion in AA 2099-T83 aluminium-lithium alloy: the role of grain orientation. Corros Sci. 2016; 107: 41–48. doi: 10.1016/j.corsci.2016.02.018.
32.
LuoCZhangXZhouX. Characterization of localized corrosion in an Al-Cu-Li alloy. J Mater Eng Perform. 2016; 25: 1811–1819. doi: 10.1007/s11665-016-2010-y.
33.
MaYZhouXHuangW. Localized corrosion in AA2099-T83 aluminum-lithium alloy: The role of intermetallic particles. Mater Chem Phys. 2015; 161: 201–210. doi: 10.1016/j.matchemphys.2015.05.037.
34.
ZhangXZhouXMaY. The propagation of localized corrosion in Al-Cu-Li alloy. Surf Interface Anal. 2016; 48: 745–749. doi: 10.1002/sia.5890.
35.
ZhouXLuoCMaY. Grain-stored energy and the propagation of intergranular corrosion in AA2XXX aluminium alloys. Surf Interface Anal. 2013; 45: 1543–1547. doi: 10.1002/sia.5218.
36.
GuérinMAndrieuEOdemerG. Effect of varying conditions of exposure to an aggressive medium on the corrosion behavior of the 2050 Al – Cu – Li alloy. Corros Sci. 2014; 85: 455–470. doi: 10.1016/j.corsci.2014.04.042.
37.
BuchheitRGMoranJPStonerGE.Electrochemical behavior of the T1 (Al2CuLi) intermetallic compound and its role in localized corrosion of Al-2%Li-3%Cu alloys. Corrosion. 1994; 50: 120–130. doi: 10.5006/1.3293500.
38.
LiMSeyeuxAWiameF. Insights on the Al-Cu-Fe-Mn intermetallic particles induced pitting corrosion of Al-Cu-Li alloy. Corros Sci. 2020; 176: 109040. doi: 10.1016/j.corsci.2020.109040.
39.
LeiXSaatchiAGhanbariE. Studies on Pitting Corrosion of Al-Cu-Li alloys Part I: effect of Li addition by microstructural, electrochemical, In-situ, and Pit depth analysis. Materials. 2019; 12: 1600,. doi: 10.3390/ma12101600.
40.
ZhuYSunKGarvesJ. Micro- and nano-scale intermetallic phases in AA2070-T8 and their corrosion behavior. Electrochim Acta. 2019; 319: 634–648. doi: 10.1016/j.electacta.2019.05.028.
41.
ZhuYPoplawskyJDLiS. Localized corrosion at nm-scale hardening precipitates in Al-Cu-Li alloys. Acta Mater. 2020; 189: 204–213. doi: 10.1016/j.actamat.2020.03.006.
42.
de S. AraujoJVda SilvaRMPDonatusU. Microstructural, electrochemical and localized corrosion characterization of the AA2198-T851 alloy. Mater Res. 2020; 23; doi: 10.1590/1980-5373-mr-2020-0161.
43.
Sousa AraujoJVMilagreMXFerreiraRO. Exfoliation and intergranular corrosion resistance of the 2198 Al–Cu–Li alloy with different thermomechanical treatments. Mater Corros. 2020; 71: 1957–1970. doi: 10.1002/maco.202011839.
44.
XuXHaoMChenJ. Role of intermetallic phases in initiation and propagation of intergranular corrosion of an AlLiCuMg alloy. Mater Sci. 2021: 1–43. doi: 10.48550/arXiv.2106.15160.
45.
LiMSeyeuxAWiameF. Localized corrosion induced surface modifications of Al-Cu-Li alloy studied by ToF-SIMS 3D imaging. Mater Degrad. 2021; 5: 23. doi: 10.1038/s41529-021-00170-9.
46.
XuXHaoMChenJ. Role of constituent intermetallic phases and precipitates in initiation and propagation of intergranular corrosion of an Al-Li-Cu-Mg alloy. Corros. Sci. 2022; 201: 110294. doi: 10.1016/j.corsci.2022.110294.
GlennAMHughesAEMacRaeCM. Observations on the early stages of corrosion on AA2099-T83. Microsc Microanal. 2020; 6: 1–16. doi: 10.1017/s1431927620001634.
49.
KosariATichelaarFVisserP. Dealloying-driven local corrosion by intermetallic constituent particles and dispersoids in aerospace aluminium alloys. Corros Sci. 2020; 177: 108947. doi: 10.1016/j.corsci.2020.108947.
50.
JiYXuYZhangB. Review of micro-scale and atomic-scale corrosion mechanisms of second phases in aluminum alloys. Trans Nonferrous Met Soc China. 2021; 31: 3205–3227. doi: 10.1016/S1003-6326(21)65727-8.
51.
LiewYÖrnekCPanJ. Towards understanding micro-galvanic activities in localised corrosion of AA2099 aluminium alloy. Electrochim Acta. 2021; 392: 139005. doi: 10.1016/j.electacta.2021.139005.
52.
GhanbariESaatchiALeiX. Studies on Pitting Corrosion of Al-Cu-Li Alloys Part II: breakdown potential and Pit initiation. Materials. 2019; 12: 1786. doi: 10.3390/ma12111786.
53.
ZhuYSunKFrankelGS.Intermetallic phases in Aluminum Alloys and their roles in localized corrosion. J Electrochem Soc. 2018; 165: C807–C820. doi: 10.1149/2.0931811jes.
54.
GhanbariESaatchiALeiX. Studies on pitting corrosion of Al–Cu–Li alloys Part III: passivation kinetics of AA2098–T851 Based on the point defect model. Materials. 2019; 12: 1912. doi: 10.3390/ma12121912.
55.
CarangeloACurioniMAcquestaA. Application of EIS to in situ characterization of hydrothermal sealing of anodized aluminum alloys: comparison between hexavalent chromium-based sealing, hot water sealing and cerium-based sealing. J Electrochem Soc. 2016; 163: C619–C626. doi: 10.1149/2.0231610jes.
56.
DingZSmithBAHebertRR. Morphology perspective on chromic acid anodizing replacement by thin film sulfuric acid anodizing. Surf Coatings Technol. 2018; 350: 31–39. doi: 10.1016/j.surfcoat.2018.07.008.
57.
HarscoetEFroelichD.Use of LCA to evaluate the environmental benefits of substituting chromic acid anodizing (CAA). J Clean Prod. 2008; 16: 1294–1305. doi: 10.1016/j.jclepro.2007.06.010.
58.
YuXCaoC.Electrochemical study of the corrosion behavior of Ce sealing of anodized 2024 aluminum alloy. Thin Solid Films. 2003; 423: 252–256. doi: 10.1016/S0040-6090(02)01038-6.
59.
García-RubioMOcónPCliment-FontA. Influence of molybdate species on the tartaric acid/sulphuric acid anodic films grown on AA2024 T3 aerospace alloy. Corros Sci. 2009; 51: 2034–2042. doi: 10.1016/j.corsci.2009.05.034.
60.
MarzocchiVIglesias-RubianesLThompsonGE. The influence of tartaric acid additions on the anodizing behaviour of AA2024-T3 alloy in sulphuric acid. Corros Rev. 2007; 25; doi: 10.1515/CORRREV.2007.25.3-4.461.
61.
WangLSRWangLHeC. Studies on the sealing processes of corrosion resistant coatings formed on 2024 aluminium alloy with tartaric-sulfuric anodizing. Surf Coat Technol. 2007; 360: 369–375.
Iglesias-RubianesLGarcia-VergaraSJSkeldonP. Cyclic oxidation processes during anodizing of Al-Cu alloys. Electrochim Acta. 2007; 52: 7148–7157. doi: 10.1016/j.electacta.2007.05.052.
64.
CurioniMSaenz De MieraMSkeldonP. Macroscopic and local filming behavior of AA2024 T3 aluminum alloy during anodizing in sulfuric acid electrolyte. J Electrochem Soc. 2008; 155: 387–395. doi: 10.1149/1.2931522.
65.
Saenz de MieraMCurioniMSkeldonP. Modelling the anodizing behaviour of aluminium alloys in sulphuric acid through alloy analogues. Corros Sci. 2008; 50: 3410–3415. doi: 10.1016/j.corsci.2008.09.019.
66.
Saenz de MieraMCurioniMSkeldonP. The behaviour of second phase particles during anodizing of aluminium alloys. Corros Sci. 2010; 52: 2489–2497. doi: 10.1016/j.corsci.2010.03.029.
67.
NickelDDietrichDMorgensternR. Anodisation of aluminium alloys by micro-capillary technique as a tool for reliable, cost-efficient, and quick process parameter determination. Adv Mater Sci Eng. 2016; 2016: 1–12. doi: 10.1155/2016/1374897.
68.
FaresABCBelouchraniMABellayerS. Influence of intermetallic compounds and metallurgical state of the 2017A aluminium alloy on the morphology of alumina films developed by anodic oxidation. J Tribol Surf Eng. 2011; 2: 239–251.
69.
FaresCBoudiafABelouchraniMEA. Microstructural characterisation of oxide layer developed by sulphuric anodisation on 2017A alloys. Int J Mater Res. 2013; 104: 1108–1113. doi: 10.3139/146.110962.
70.
BononiMGiovanardiR.Hard anodizing of AA2011-T3 Al-Cu-Pb-Bi free-cutting alloy: improvement of the process parameters. Corros Sci. 2018; 141: 63–71. doi: 10.1016/j.corsci.2018.07.004.
71.
Abdel-GawadSAOsmanWMFekryAM.Characterization and corrosion behavior of anodized aluminum alloys for military industries applications in artificial seawater. Surf Interf. 2019; 14: 314–323. doi: 10.1016/j.surfin.2018.08.001.
72.
Veys-RenauxDChahbounNRoccaE.Anodizing of multiphase aluminium alloys in sulfuric acid: in-situ electrochemical behaviour and oxide properties. Electrochim Acta. 2016; 211: 1056–1065. doi: 10.1016/j.electacta.2016.06.131.
73.
ElkilanyHAShoeibMAAbdel-SalamOE.Influence of hard anodizing on the mechanical and corrosion properties of different aluminum alloys. Metallogr Microstruct Anal. 2019; 8: 861–870. doi: 10.1007/s13632-019-00594-5.
74.
ViejoFCoyAEGarcía-GarcíaFJ. Enhanced performance of the AA2050-T8 aluminium alloy following excimer laser surface melting and anodising processes. Thin Solid Films. 2010; 518: 2722–2731. doi: 10.1016/j.tsf.2009.09.121.
75.
MaYZhouXThompsonGE. Discontinuities in the porous anodic film formed on AA2099-T8 aluminium alloy. Corros Sci. 2011; 53: 4141–4151. doi: 10.1016/j.corsci.2011.08.023.
76.
MaYZhouXThompsonGE. Anodic film formation on AA 2099-T8 Aluminum Alloy in tartaric–sulfuric acid. J Electrochem Soc. 2011; 158: C17–C22. doi: 10.1149/1.3523262.
77.
MaYChenXZhouX. Microstructural origin of localized corrosion in anodized AA2099-T8 aluminium–lithium alloy. Surf Interface Anal. 2016; 48: 739–744. doi: 10.1002/sia.5856.
78.
MaYZhouXLiK. Corrosion and anodizing behavior of T1 (Al2CuLi) precipitates in Al-Cu-Li alloy. J Electrochem Soc. 2019; 166: C296–C303. doi: 10.1149/2.0891912jes.
79.
BononiMConteMGiovanardiR. Hard anodizing of AA2099-T8 aluminum–lithium–copper alloy: Influence of electric cycle, electrolytic bath composition and temperature. Surf Coatings Technol. 2017; 325: 627–635. doi: 10.1016/j.surfcoat.2017.07.028.
80.
WuHMaYHuangW. Effect of iron-containing intermetallic particles on film structure and corrosion resistance of anodized AA2099 alloy. J Electrochem Soc. 2018; 165: C573–C581. doi: 10.1149/2.1361809jes.
81.
LiuJRongGCenS. Dissolution behavior of intermetallic particles in AA2297-T87 during anodizing in adipic-sulfuric acid. J Electrochem Soc. 2018; 165: C980–C990. doi: 10.1149/2.0061816jes.
82.
MaYWuHZhouX. Corrosion behavior of anodized Al-Cu-Li alloy: The role of intermetallic particle-introduced film defects. Corros Sci. 2019; 158; doi: 10.1016/j.corsci.2019.108110.
83.
Samaniego-GámezPOAlmeraya-CalderonFMaldonado-BandalaE. Corrosion behavior of AA2055 aluminum-lithium alloys anodized in the presence of sulfuric acid solution. Coatings. 2021; 11: 1278. doi: 10.3390/coatings11111278.
84.
DorinTVahidALambJ.Aluminium lithium alloys. In: RogerN. Lumley, editor. Fundamentals of aluminium metallurgy. Melbourne: Elsevie;2018. p. 387–438. doi: 10.1016/B978-0-08-102063-0.00011-4.
85.
HanBChenYTaoW. Microstructural evolution and interfacial crack corrosion behavior of double-sided laser beam welded 2060/2099 Al-Li alloys T-joints. Mater Des. 2017; 135: 353–365. doi: 10.1016/j.matdes.2017.09.042.
86.
GaoCMaYTangL. Microstructural evolution and mechanical behavior of friction spot welded 2198-T8 Al-Li alloy during aging treatment. Mater Des. 2017; 115: 224–230. doi: 10.1016/j.matdes.2016.11.045.
87.
ZhuPMaYLiK. Sealing of anodized AA2099-T83 Al-Cu-Li alloy with layered double hydroxides for high corrosion resistance at reduced anodic film thickness. Surf Coatings Technol. 2020; 394: 125852. doi: 10.1016/j.surfcoat.2020.125852.
88.
de Souza Carvalho MachadoCDonatusUMilagreMX. How microstructure affects localized corrosion resistance of stir zone of the AA2198-T8 alloy after friction stir welding. Mater Charact. 2021; 174: 111025. doi: 10.1016/j.matchar.2021.111025.
89.
DonatusUFerreiraROMogiliNVV. Corrosion and anodizing behaviour of friction stir weldment of AA2198-T851 Al-Cu-Li alloy. Mater Chem Phys. 2018; 219: 493–511. doi: 10.1016/j.matchemphys.2018.08.053.
90.
DonatusUTeradaMOspinaCR. On the AA2198-T851 alloy microstructure and its correlation with localized corrosion behaviour. Corros Sci. 2018; 131: 300–309. doi: 10.1016/j.corsci.2017.12.001.
91.
KlumppREDonatusUda SilvaRMP. Corrosion protection of the AA2198-T8 alloy by environmentally friendly organic-inorganic sol-gel coating based on bis-1,2-(triethoxysilyl) ethane. Surf Interface Anal. 2020: 1–16. doi: 10.1002/sia.6919.
92.
DonatusUBerbelLOCostaI.Qualitative use of potentiodynamic polarization and anodic hydrogen evolution in the assessment of corrosion susceptibility in AA2198-T851 Al–Cu–Li alloy. Mater Corros. 2018; 69: 1375–1388. doi: 10.1002/maco.201810108.
93.
BalboAFrignaniAGrassiV. Electrochemical behaviour of AA2198 and AA2139 in neutral solutions. Mater Corros. 2015; 66: 796–802. doi: 10.1002/maco.201408059.
94.
AlexopoulosNDProiouAExamiliotiT. Effect of artificial aging on the mechanical performance of (Al-Cu) 2024 and (Al-Cu-Li) 2198 aluminum alloys. Procedia Struct Integr. 2016; 2: 3782–3783. doi: 10.1016/j.prostr.2016.06.470.
95.
AlexopoulosNDProiouADietzelW. Mechanical properties degradation of (Al-Cu-Li) 2198 alloy due to corrosion exposure. Procedia Struct Integr. 2016; 2: 597–603. doi: 10.1016/j.prostr.2016.06.077.
96.
AlexopoulosNDMigklisEStylianosA. Fatigue behavior of the aeronautical Al–Li (2198) aluminum alloy under constant amplitude loading. Int J Fatigue. 2013; 56: 95–105. doi: 10.1016/j.ijfatigue.2013.07.009.
97.
CharalampidouCDietzelWZheludkevichM. Corrosion-induced mechanical properties degradation of Al-Cu-Li (2198-T351) aluminium alloy and the role of side-surface cracks. Corros Sci. 2021; 183: 109330. doi: 10.1016/j.corsci.2021.109330.
98.
GeorgoulisDCharalampidouCMSiskouN. Corrosion behaviour of AA2198–T8 and AA2024-T3 alloy in 3.5% aqueous solution. Procedia Struct Integr. 2020; 28: 2297–2303. doi: 10.1016/j.prostr.2020.11.076.
99.
CarrickDMHoggSCWilcoxGD.Corrosion of an advanced Al-Cu-Li alloy for aerospace applications. Mater Sci Forum. 2013; 765: 629–633. doi: 10.4028/www.scientific.net/MSF.765.629.
100.
DonatusUOluwatosin BodunrinMOlayinkaA. Corrosion resistance of precipitation-hardened Al alloys: a comparison between new generation Al-Cu-Li and conventional alloy. In: Aluminium alloys. IntechOpen. 2020. doi: 10.5772/intechopen.92807.
101.
Alenia AeronauticaSPAAlenia AeronauticaSPA. Anodizing process, with low environmental impact, for a workpiece of aluminium or aluminium alloys. European Patent Application EP. n.d.: 1233084 A2.
102.
Fratila-ApachiteiLTerrynHSkeldonP. Influence of substrate microstructure on the growth of anodic oxide layers. Electrochim Acta. 2004; 49: 1127–1140. doi: 10.1016/j.electacta.2003.10.024.
103.
MoonS-MSakairiMTakahashiH.Application of CSLM to the surface morphological study of Al 5052 alloy anodized in sulfuric acid solution. J Electrochem Soc. 2003; 150: B473. doi: 10.1149/1.1603248.
104.
MoonSMSakairiMTakahashiH.Behavior of second-phase particles in Al5052 alloy during anodizing in a sulfuric acid solution CSLM observation. J Electrochem Soc. 2004; 151: 399–405. doi: 10.1149/1.1752933.
105.
ParkhutikVPShershulskyVI.Theoretical modelling of porous oxide growth on aluminium. J Phys D Appl Phys. 1992; 25: 1258–1263. doi: 10.1088/0022-3727/25/8/017.
106.
LeeWParkSJ.Porous anodic aluminum oxide: anodization and templated synthesis of functional nanostructures. Chem Rev. 2014; 114: 7487–7556. doi: 10.1021/cr500002z.
107.
ZhouXThompsonGESkeldonP. Film formation and detachment during anodizing of Al-Mg alloys. Corros Sci. 1999; 41: 1599–1613. doi: 10.1016/S0010-938X(99)00007-4.
BirbilisNBuchheitRG.Electrochemical characteristics of intermetallic phases in Aluminum alloys. J Electrochem Soc. 2005; 152: B140. doi: 10.1149/1.1869984.
110.
BuchheilRG.A compilation of corrosion potentials reported for intermetallic phases in aluminum alloys. J Electrochem Soc. 1995; 142: 3994–3996. doi: 10.1149/1.2048447.
111.
de Sousa AraujoJVMilagreMXFerreiraRO. Microstructural characteristics of the Al alloys: The dissimilarities among the 2XXX alloys series used in aircraft structures. Metallogr Microstruct Anal. 2020, doi: 10.1007/s13632-020-00688-5.
112.
MaYZhouXThompsonGE. Distribution of intermetallics in an AA 2099-T8 aluminium alloy extrusion. Mater Chem Phys. 2011; 126: 46–53. doi: 10.1016/j.matchemphys.2010.12.014.
113.
LiuYArenasMASkeldonP. Anodic behaviour of a model second phase: Al-20at.%Mg-20at.%Cu. Corros Sci. 2006; 48: 1225–1248. doi: 10.1016/j.corsci.2005.05.007.
114.
de MieraMS.Effects of microstructure on anodizing of high strength aluminium alloys. Manchester: Manchester University; 2008.
115.
SepulvedaYPaezMAZagalJH. Anodizing of al 2024-T3 in mixtures of sulphuric-boric acids. Boletín La Soc Chil Química. 2001; 46; doi: 10.4067/S0366-16442001000400003.
116.
MoutarlierVGigandetMPPagettiJ. Molybdate/sulfuric acid anodising of 2024-aluminium alloy: Influence of inhibitor concentration on film growth and on corrosion resistance. Surf Coatings Technol. 2003; 173: 87–95. doi: 10.1016/S0257-8972(03)00511-5.
117.
MacRaeCMHughesAELairdJS. An examination of the composition and microstructure of coarse intermetallic particles in AA2099-T8, including Li detection. Microsc Microanal. 2018: 1–17. doi: 10.1017/S1431927618000454.
118.
Saenz De MieraMCurioniMSkeldonP. Preferential anodic oxidation of second-phase constituents during anodising of AA2024-T3 and AA7075-T6 alloys. Surf Interface Anal. 2010; 42: 241–246. doi: 10.1002/sia.3191.