The effect of thiosulphate/H2S on crevice corrosion behaviour of P110 carbon steel in the CO2-saturated 3.5 wt% NaCl solution was investigated. The results showed that crevice corrosion of P110 steel could not occur in the CO2-saturated solution, likely due to the inhibition of both anodic and cathodic reactions inside crevice. Further, the structure of corrosion product film along the crevice wall is influenced by the concentration of thiosulphate. Increasing the concentration of thiosulphate to 10−2 mol L−1 promotes the formation of fine flake-like mackinawite outside crevice. In addition, crevice corrosion of P110 steel in the CO2-saturated solution is promoted by increasing the concentration of thiosulphate. This is because the dense and fine mackinawite film on the steel surface has a better protectiveness and could enhance cathodic reaction rate outside crevice.
ZhuSDWeiJFBaiZQ. Failure analysis of P110 tubing string in the ultra-deep oil well. Eng Fail Anal. 2011; 18: 950–962. DOI:10.1016/j.engfailanal.2010.11.013.
2.
ZhuSDWeiJFCaiR. Corrosion failure analysis of high strength grade super 13Cr-110 tubing string. Eng Fail Anal. 2011; 18: 2222–2231. DOI:10.1016/j.engfailanal.2011.07.017.
3.
LiYZXuNLiuGR. Crevice corrosion of N80 carbon steel in CO2-saturated environment containing acetic acid. Corros Sci. 2016; 112: 426–437. DOI:10.1016/j.corsci.2016.08.002.
4.
ZhuSDFuAQMiaoJ. Corrosion of N80 carbon steel in oil field formation water containing CO2 in the absence and presence of acetic acid. Corros Sci. 2011; 53: 3156–3165. DOI:10.1016/j.corsci.2011.05.059.
5.
LiYZXuNGuoXP. The role of acetic acid or H+ in initiating crevice corrosion of N80 carbon steel in CO2-saturated NaCl solution. Corros Sci. 2017; 128: 9–22. DOI:10.1016/j.corsci.2017.08.028.
6.
HuQZhangGAQiuYB. The crevice corrosion behaviour of stainless steel in sodium chloride solution. Corros Sci. 2011; 53: 4065–4072. DOI:10.1016/j.corsci.2011.08.012.
7.
TanY-JBaileySKinsellaB.Mapping non-uniform corrosion using the wire beam electrode method. II. Crevice corrosion and crevice corrosion exemption. Corros Sci. 2001; 43: 1919–1929. DOI:10.1016/S0010-938X(00)00191-8.
8.
TanY-JFwuYBhardwajK.Electrochemical evaluation of under-deposit corrosion and its inhibition using the wire beam electrode method. Corros Sci. 2011; 53: 1254–1261. DOI:10.1016/j.corsci.2010.12.015.
9.
HuQGuoXPZhangGA. The corrosion behavior of carbon steel in CO2-saturated NaCl crevice solution containing acetic acid. Mater Corros. 2012; 63: 720–728. DOI:10.1002/maco.201006027 doi: 10.1002/maco.201005725
10.
LiYZXuNGuoXP. Inhibition effect of imidazoline inhibitor on the crevice corrosion of N80 carbon steel in the CO2-saturated NaCl solution containing acetic acid. Corros Sci. 2017; 126: 127–141. DOI:10.1016/j.corsci.2017.06.021.
11.
ZouJPangXLGaoKW.Crevice corrosion of X70 and 3Cr low alloy steels under supercritical CO2 condition. Acta Metall Sin. 2018; 54: 537–546. DOI:10.11900/0412.1961.2017.00353.
12.
ZhaoJMLuYLiuHX.Corrosion and control of P110 oil tube steel in CO2-saturated solution. Corros Eng Sci Technol. 2008; 43: 313–519. DOI:10.1179/174327808X315650.
13.
LiuZYLiHJiaZJ. Failure analysis of P110 steel tubing in low-temperature annular environment of CO2 flooding wells. Eng Fail Anal. 2015; 60: 296–306. DOI:10.1016/j.engfailanal.2015.11.041.
14.
BaiPPZhaoHZhengSQ. Initiation and developmental stages of steel corrosion in wet H2S environments. Corros Sci. 2015; 93: 109–119. DOI:10.1016/j.corsci.2015.01.024.
15.
HuangFLiuSLiuJ. Sulfide stress cracking resistance of the welded WDL690D HSLA steel in H2S environment. Mater Sci Eng A. 2014; 591: 159–166. DOI:10.1016/j.msea.2013.10.081.
16.
SchvartzmanMMAMLopesDrEstevesL. Pitting corrosion of supermartensitic stainless steel in chloride solutions containing thiosulfate or H2S. J Mater Eng Perform. 2018; 27: 3723–3730. DOI:10.1007/s11665-018-3403-x.
17.
YanWDengJZhuP. Investigation of pH2S influence on 3% Cr tubing steel corrosion behaviours in CO2–H2S–Cl− environment. Corros Eng Sci Technol. 2015; 50: 525–532. DOI:10.1179/1743278215Y.0000000001.
18.
SingerMBrownBCamachoA. Combined effect of carbon dioxide, hydrogen sulfide, and acetic acid on bottom-of-the-line corrosion. Corrosion. 2011; 67: 015004-1–015004-16. DOI:10.5006/1.3543715.
19.
ZhaoWZouYMatsudaK. Corrosion behavior of reheated CGHAZ of X80 pipeline steel in H2S-containing environments. Mater Des. 2016; 99: 44–56. DOI:10.1016/j.matdes.2016.03.036.
20.
ElgaddafiRAhmedRShahS.Modeling and experimental studies on CO2-H2S corrosion of API carbon steels under high-pressure. J Petrol Sci Eng. 2017; 156: 682–696. DOI:10.1016/j.petrol.2017.06.030.
21.
SouzaRSantosBGonçalvesM. The role of temperature and H2S (thiosulfate) on the corrosion products of API X65 carbon steel exposed to sweet environment. J Petrol Sci Eng. 2019; 180: 78–88. DOI:10.1016/j.petrol.2019.05.036.
22.
ChoiY-SNesicSLingS.Effect of H2S on the CO2 corrosion of carbon steel in acidic solutions. Electrochim Acta. 2011; 56: 1752–1760. DOI:10.1016/j.electacta.2010.08.049.
23.
LiDPZhangLYangJW. Effect of H2S concentration on the corrosion behavior of pipeline steel under the coexistence of H2S and CO2. Int J Min Met Mater. 2014; 21: 388–394. DOI:10.1007/s12613-014-0920-y.
24.
ChoiY-SHassaniSVuTN. Effect of H2S on the corrosion behavior of pipeline steels in supercritical and liquid CO2 environments. Corrosion. 2016; 72: 999–1009. DOI:10.5006/2026.
25.
SunJBSunCZhangGA. Effect of O2 and H2S impurities on the corrosion behavior of X65 steel in water-saturated supercritical CO2 system. Corros Sci. 2016; 107: 31–40. DOI:10.1016/j.corsci.2016.02.017.
26.
SkMHQiJAbdullahA. Effect of trace H2S on the scale formation behavior in a predominant CO2 environment under hydrodynamic control: role of Cr/Mo micro-alloying in plain carbon steel. J Electrochem Soc. 2019; 166: C3233–C3240. DOI:10.1149/2.0311911jes.
27.
WeiLPangXLGaoKW.Effect of small amount of H2S on the corrosion behavior of carbon steel in the dynamic supercritical CO2 environments. Corros Sci. 2016; 103: 132–144. DOI:10.1016/j.corsci.2015.11.009.
28.
ZhangGAZengYGuoXP. Electrochemical corrosion behavior of carbon steel under dynamic high pressure H2S/CO2 environment. Corros Sci. 2012; 65: 37–47. DOI:10.1016/j.corsci.2012.08.007.
29.
TangJWShaoYWGuoJB. The effect of H2S concentration on the corrosion behavior of carbon steel at 90°C. Corros Sci. 2010; 52: 2050–2058. DOI:10.1016/j.corsci.2010.02.004.
30.
SmithSNPachecoJL.Predicting corrosion in slightly sour environments. Mater Perform. 2002; 41: 60–65.
31.
SunQChenCFZhaoX. Ion-selectivity of iron sulfides and their effect on H2S corrosion. Corros Sci. 2019; 108085. DOI:10.1016/j.corsci.2019.07.009.
32.
KappesM.A.Evaluation of thiosulfate as a substitute for hydrogen sulfide in sour corrosion fatigue studies [Ph.D. Dissertation]. OH: Ohio State University; 2011.
33.
ChoudharyLMacdonaldDDAlfantaziA.Role of thiosulfate in the corrosion of steels: a review. Corrosion. 2015; 71: 1147–1168. DOI:10.5006/1709.
34.
ZafarMNRihanRAl-HadhramiL.Evaluation of the corrosion resistance of SA-543 and X65 steels in emulsions containing H2S and CO2 using a novel emulsion flow loop. Corros Sci. 2015; 94: 275–287. DOI:10.1016/j.corsci.2015.02.013.
35.
KappesMFrankelGSSridharN. Reaction paths of thiosulfate during corrosion of carbon steel in acidified brines. J Electrochem Soc. 2012; 159: C195–C204. DOI:10.1149/2.085204jes.
36.
KappesMFrankelGSSridharN. Corrosion behavior of carbon steel in acidified, thiosulfate-containing brines. Corrosion. 2012; 68: 872–884. DOI:10.5006/0610.
37.
ZhangHHPangXLGaoKW.Localized CO2 corrosion of carbon steel with different microstructures in brine solutions with an imidazoline-based inhibitor. Appl Surf Sci. 2018; 442: 446–460. DOI:10.1016/j.apsusc.2018.02.115.
38.
WeiLGaoKWLiQ.Corrosion of low alloy steel containing 0.5% chromium in supercritical CO2-saturated brine and water-saturated supercritical CO2 environments. Appl Surf Sci. 2018; 440: 524–534. DOI:10.1016/j.apsusc.2018.01.181.
39.
LiHXLiDPZhangL. Fundamental aspects of the corrosion of N80 steel in a formation water system under high CO2 partial pressure at 100°C. RSC Adv. 2019; 9: 11641–11648. DOI:10.1039/C8RA10487E.
40.
LiXPZhaoYQiWL. Effect of extremely aggressive environment on the nature of corrosion scales of HP-13Cr stainless steel. Appl Surf Sci. 2019; 469: 146–161. DOI:10.1016/j.apsusc.2018.10.237.
41.
ZhangGAChengYF.On the fundamentals of electrochemical corrosion of X65 steel in CO2-containing formation water in the presence of acetic acid in petroleum production. Corros Sci. 2009; 51: 87–94. DOI:10.1016/j.corsci.2008.10.013.
42.
ChenCFLuMXSunDB. Effect of chromium on the pitting resistance of oil tube steel in a carbon dioxide corrosion system. Corrosion. 2005; 61: 594–601. DOI:10.5006/1.3278195.
43.
KahyarianABrownBNesicS.Electrochemistry of CO2 corrosion of mild steel: effect of CO2 on iron dissolution reaction. Corros Sci. 2017; 129: 146–151. DOI:10.1016/j.corsci.2017.10.005.
44.
WrightRFBrandERZiomek-MorozM. Effect of HCO3− on electrochemical kinetics of carbon steel corrosion in CO2-saturated brines. Electrochim Acta. 2018; 290: 626–638. DOI:10.1016/j.electacta.2018.09.114.
45.
FioravanteIANunesRSAcciariHA. Films formed on carbon steel in sweet environments-a review. J Brazil Chem Soc. 2019; 30: 1341–1349. DOI:10.21577/0103-5053.20190055.
46.
YinZFLiuLZhangYQ. Characteristics and mechanism of corrosion film formation on antisulphur steels in CO2/H2S environments. Corros Eng Sci Technol. 2012; 47: 138–144. DOI:10.1179/1743278211Y.0000000036.
47.
HuangFChengPZhaoXY. Effect of sulfide films formed on X65 steel surface on hydrogen permeation in H2S environments. Int J Hydrogen Energy. 2017; 42: 4561–4570. DOI:10.1016/j.ijhydene.2016.10.130.
48.
RenCQLiuDXBaiZQ. Corrosion behavior of oil tube steel in simulant solution with hydrogen sulfide and carbon dioxide. Mater Chem Phys. 2005; 93: 305–309. DOI:10.1016/j.matchemphys.2005.03.010.