4043 aluminium deposits were elaborated using a 3D print device equipped with a Cold Metal Transfer welding source. Two sets of process parameters leading to different average powers were compared in order to establish the relations between the powers and energies produced and the geometrical characteristics of the deposits. The effects of the travel speed and layer superposition on the transfer mechanisms as well as on the geometrical characteristics of the deposits were discussed for both sets of parameters. Finally, the formed microstructures were analysed and the porosity defects were quantified and discussed with regard to the heat input characteristics and the solidification conditions.
DebRoyT, WeiHL, ZubackJS, Additive manufacturing of metallic components – process, structure and properties. Prog Mater Sci. 2018; 92:112–224. doi: 10.1016/j.pmatsci.2017.10.001
2.
DonoghueJ, AntonysamyAA, MartinaF, The effectiveness of combining rolling deformation with wire–arc additive manufacture on β-grain refinement and texture modification in Ti–6Al–4 V. Mater Charact. 2016; 114:103–114. doi: 10.1016/j.matchar.2016.02.001
3.
SzostBA, TerziS, MartinaF, A comparative study of additive manufacturing techniques: residual stress and microstructural analysis of CLAD and WAAM printed Ti–6Al–4 V components. Mater Des. 2016; 89:559–567. doi: 10.1016/j.matdes.2015.09.115
4.
XuX, DingJ, GangulyS, Oxide accumulation effects on wire + arc layer-by-layer additive manufacture process. J Mater Process Technol. 2018; 252:739–750. doi: 10.1016/j.jmatprotec.2017.10.030
5.
HadenCV, ZengG, CarterFM, Wire and arc additive manufactured steel: tensile and wear properties. Addit Manuf. 2017; 16:115–123. doi: 10.1016/j.addma.2017.05.010
6.
XiongJ, YinZ, ZhangW.Closed-loop control of variable layer width for thin-walled parts in wire and arc additive manufacturing. J Mater Process Technol. 2016; 233:100–106. doi: 10.1016/j.jmatprotec.2016.02.021
7.
OrtegaAG, GalvanLC, Deschaux-BeaumeF, Effect of process parameters on the quality of aluminium alloy Al5Si deposits in wire and arc additive manufacturing using a cold metal transfer process. Sci Technol Weld Join. 2018; 23(4):316–332. doi: 10.1080/13621718.2017.1388995
8.
MezragB, Deschaux-BeaumeF, BenachourM.Control of mass and heat transfer for steel/aluminum joining using cold metal transfer process. Sci Technol Weld Join. 2015; 20(3):189–198. doi: 10.1179/1362171814Y.0000000271
9.
MezragB, Deschaux-BeaumeF, RouquetteS, Indirect approaches for estimating the efficiency of the cold metal transfer welding process. Sci Technol Weld Join. 2018; 23(6):508–519. doi: 10.1080/13621718.2017.1417806
10.
NieY, ZhangP, WuX, Rapid prototyping of 4043 Al-alloy parts by cold metal transfer. Sci Technol Weld Join. 2018; 23(6):527–535. doi: 10.1080/13621718.2018.1438236
11.
GengH, LiJ, XiongJ, Optimisation of interpass temperature and heat input for wire and arc additive manufacturing 5A06 aluminium alloy. Sci Technol Weld Join. 2017; 22(6):472–483. doi: 10.1080/13621718.2016.1259031
12.
AlShaerAW, LiL, MistryA.The effects of short pulse laser surface cleaning on porosity formation and reduction in laser welding of aluminium alloy for automotive component manufacture. Opt Laser Technol. 2014; 64:162–171. doi: 10.1016/j.optlastec.2014.05.010
13.
GouG, ZhangM, ChenH, Effect of humidity on porosity, microstructure, and fatigue strength of A7N01S-T5 aluminum alloy welded joints in high-speed trains. Mater Des. 2015; 85:309–317. doi: 10.1016/j.matdes.2015.06.177
14.
TavakoliF, DavisSH, KavehpourHP.Spreading and arrest of a molten liquid on cold substrates. Langmuir. 2014; 30:10151–10158. doi: 10.1021/la5017998
15.
De RuiterR, ColinetP, BrunetP, Contact line arrest in solidifying spreading drops. Phys Rev Fluids. 2017; 2:043602. doi: 10.1103/PhysRevFluids.2.043602
16.
ZhangC, GaoM, WangD, Relationship between pool characteristic and weld porosity in laser arc hybrid welding of AA6082 aluminum alloy. J Mater Process Technol. 2017; 240:217–222. doi: 10.1016/j.jmatprotec.2016.10.001
17.
TaoW, YangZ, ShiC, Simulating effects of welding speed on melt flow and porosity formation during double-sided laser beam welding of AA6056-T4/AA6156-T6 aluminum alloy T-joint. J Alloys Compd. 2017; 699:638–647. doi: 10.1016/j.jallcom.2016.12.371
18.
BaoqiangC, RuijieO, BojinQ, Influence of cold metal transfer process and its heat input on weld bead geometry and porosity of aluminum-copper alloy welds. Rare Metal Mater Engineer. 2016; 45(3):606–611. doi: 10.1016/S1875-5372(16)30080-7