Double sided arc welding of AA5182 aluminium alloy sheet

Abstract

The feasibility and merits of using the double sided arc welding (DSAW) process for making square welds in 1˙2 mm thick AA5182-O aluminium sheets in the butt-joint configuration for applications such as tailor welded blanks (TWB) has been studied. Full penetration, conduction mode DSAW welds were made using a balanced square wave AC, constant current power supply at welding speeds of 30 to 40 mm s^–1 when using 2˙1 kW welding power and between 40 and 60 mm s^–1 when using 3˙4 kW welding power. There was good cathodic cleaning of the oxide on both sides of the sheet and the weld bead quality and properties were excellent. All welds exhibited a columnar to equiaxed grain transition with up to 40% equiaxed grain area. The DSAW process was found to be capable of producing welds of equal or better quality and at comparable welding speeds to those produced using more traditional welding processes for TWB applications.

Keywords

DOUBLE SIDED ARC WELDING ALUMINIUM TAILOR WELDED BLANKS

Get full access to this article

View all access options for this article.

References

Kubel

: Manufact. Eng., 1997, 119, (5), 38–45.

Kazmier

R. J.

: Adv. Mater. Process., 2001, 94, (1), 42–44.

Das

: Adv. Mater. Process., 2000, 157, (3), 41–42.

Craig

: Weld. J., 1998, 67, (2), 19–25.

Duley

W. W.

: ‘Laser welding’; 1999, Toronto, ON, John Wiley & Sons.

Ion

J. C.

: Sci. Technol. Weld. Join., 2000, 5, (5), 265–276.

Zhao

, White

D. R.

and DebRoy

: Int. Mater. Rev., 1999, 44, (6), 238–266.

Venkat

, Albright

C. E.

, Ramasamy

and Hurley

J. P.

: Weld. J., 1997, 76, (7), 275s–282s.

Pastor

, Zhao

, Martukanitz

R. P.

and DebRoy

: Weld. J., 1999, 78, (6), 207s–216s.

10.

Deutsch

M. G.

, Punkari

, Weckman

D. C.

and Kerr

H. W.

: Sci. Technol. Weld. Join., 2003, 8, (4), 246–256.

11.

Punkari

, Weckman

D. C.

and Kerr

H. W.

: Sci. Technol. Weld. Join., 2003, 8, (4), 269–282.

12.

Fuerschbach

P. W.

: Weld. J., 1998, 77, (2), 76s–85s.

13.

Deutsch

: ‘Effects of Nd:YAG laser welding and VPPAW welding process variables on weld metal geometry and defects of 1·6 mm thick 5182 aluminum’, Mater's dissertation, University of Waterloo, Canada, 2002.

14.

Punkari

: ‘Variable polarity plasma arc welding and dual-beam Nd:YAG laser welding of aluminum alloys’, Master's dissertation, University of Waterloo, Canada, 2002.

15.

Zhang

and Zhang

S. B.

: US patent no. 5,990,446, 1999.

16.

Zhang

Y. M.

and Zhang

S. B.

: Weld. J., 1998, 77, (6), 57–61.

17.

Zhang

Y. M.

and Zhang

S. B.

: Weld. J., 1999, 78, (6) 202s–206s.

18.

Zhang

Y. M.

, Pan

and Male

A. T.

: J. Mater. Sci. Lett., 2000, 19, 831–833.

19.

Zhang

Y. M.

, Pan

and Male

A. T.

: Metall. Mater. Trans. A, 2000, 31A, 2537–2543.

20.

Zhang

Y. M.

, Pan

and Male

A. T.

: Mater. Sci. Technol., 2001, 17, (10), 1280–1284.

21.

Zhang

Y. M.

, Zhang

S. B.

and Jiang

: Weld. J., 2002, 81, (11), 249s–255s.

22.

Zhang

Y. M.

: Personal communications, University of Kentucky, USA, April 20, 2002.

23.

Kwon

: ‘Double-sided arc welding of AA5182 aluminum alloy sheet’, Master's dissertation, University of Waterloo, Canada, 2003.

24.

‘ASM handbook’, Vol. 2, ‘Properties and selection: nonferrous alloys and special purpose materials’, 10th edn, 95; 1990, Materials Park, OH, ASM Int.

25.

‘ASM handbook’, Vol. 6, ‘Welding, brazing and soldering’; 1993, Materials Park, OH, ASM Int.

26.

Oates

W. R.

(ed.): ‘Welding handbook’, Vol. 3, ‘Materials and applications’, Part 1, 25; 1996, Miami, FL, American Welding Soc.

27.

LaserStrobe Model 4Z – Operation Manual, 1999, Control Vision, Idaho Falls, ID, USA.

28.

Vander Voort

G. F.

: ‘Metallography principles and practice’, 510s, 610s; 1999, Materials Park, OH, ASM Int.

29.

Swift–HoofandA

D. T.

Gick

E. F.

: Weld. J., 1973, 52, (11), 492s– 499s.

30.

Rosenthal

: Trans. ASME, 1946, 43, (11), 849–866.

31.

Wells

A. A.

: Weld. J., 1952, 31, (5), 263s–267s.

32.

Fuerschbach

P. W.

and Knorovsky

G. A.

: Weld. J., 1991, 70, (11), 287s–297s.

33.

Kou

: ‘Welding metallurgy’, 2nd edn; 2003, Toronto, John Wiley & Sons.

34.

Bailey

C. J.

and Pilkey

A. K.

: Mater. Sci. Eng. A, 2005, A403, 1–10.

35.

Kou

and Le

: Metall. Trans. A, 1988, 19A, (4), 1075–1082.

36.

Davies

G. J.

and Garland

J. G.

: Int. Metall. Rev., 1975, 20, 83–106.

37.

Kerr

H. W.

: Proc. 3rd Int. Conf. on ‘Trends in welding research’, (ed. S. A. David and J. M. Vitek), Gatlinburg, TN, June 1992, ASM Int., 157–166.

38.

Hunt

J. D.

: Mater. Sci. Eng., 1984, 65, 75–83.

39.

Clarke

: ‘Columnar-to-equiaxed grains transition in gas tungsten arc welds in aluminum-copper alloys’, PhD thesis, University of Waterloo, Canada, 1998.

40.

Clarke

, Weckman

D. C.

and Kerr

H. W.

: Proc. 5th Int. Conf. on ‘Trends in welding research’, (ed. J. M. Vitek et al.), 72–76; 1999, Materials Park, OH, ASM Int.

41.

Norman

A. F.

, Drazhner

and Prangnell

P. B.

: Mater. Sci. Eng. A, 1999, A259, 53–64.