Fatigue damage accumulation and analysis methods are considered for composites and contrasted with metals. The failure of current analysis methods is illustrated and explained by the information missing in load idealization data. Detailed local strain operational monitoring with local strain fatigue data is proposed as a future approach to fatigue life assessment of composite materials under aircraft service loading.
ReifsniderK. L.HighsmithA.Characteristic damage states: a new approach to representing fatigue damage in composite laminates, materials, experimentation and design in fatigue. In Proceedings of fatigue (Eds SherrattF.SturgessJ. B., 1981, pp. 246–260 (Westbury House).
2.
MatsuishiM.EndoT.Fatigue of metals subjected to varying stress. Paper presented to Japan Society of Mechanical Engineers, Jukvoka, Japan, 1968.
3.
Heath SmithJ. R.Theoretical considerations in the use of FAL-STAFF loading for fatigue research in carbon fibre composite. RAe TR 79124, 26 September 1979.
4.
BaderM. G.BonifaceL.The performance of CRFP laminates subjected to complex fatigue loading programmes. In Fibre reinforced composites, April 1984, p. 7. 1.111 (The Plastics and Rubber Institute, Liverpool).
5.
YangJ. N.JonesD. L.Load sequence effect on statistical fatigue of composite materials. In Fatigue of fibrous composite materials, ASTM 723, 1981, pp. 213–323 (American Society for Testing and Materials, Philadelphia, Pennsylvania).
6.
BroutmanL. J.SahuS.A new theory to predict cumulative fatigue damage in fibreglass reinforced plastics. In Composite materials testing and design, ASTM STP 497, 1972, pp. 170–188 (American Society for Testing and Materials, Philadelphia, Pennsylvania).
7.
AmijimaS.TanimotoT.NatsuokaT.A study on fatigue life estimation of FRP under random loading. Proceedings of Fourth JSCM International Conference on Composite materials: Progress in science and engineering of composites, 1982, p. 701.
8.
JeansL. L.TribbleW. L.Simulation of fighter aircraft manoeuvre load spectra. In Service fatigue loads monitoring, simulation and analysis ASTM STP 671, 1979, pp. 240–254 (American Society for Testing and Materials, Philadelphia, Pennsylvania).
9.
de JongeJ. B.The use of standardised load sequences in coupon and component tests. Paper presented at Second AIFA Mechanical Engineers, Naples, 26–28 February 1980 (National Aerospace Laboratory NLR, 1059 CMAmsterdam, The Netherlands).
10.
BadalianceR.DillH. D.Effects of fighter attack spectrum on composite material fatigue life. McDonnell Aircraft Company TR ARWAL TR-81-3001, March 1981.
11.
Heath SmithJ. R.Fatigue of structural elements in carbon fibre composites—present indications and future research. RAE TR 79085, Ministry of Defence, Farnborough, July 1979.
12.
ArendisF. J.SippelK. O.WeisgerberD.Constant-amplitude and flight by flight tests on CRFP specimens. AGARD CP 288, 50th Meeting, Athens, 1980.
13.
GordonB.WhiteheadR. S.A critical review of life prediction methods for composite structures. British Aerospace report SON(P) 179, February 1979.
14.
YangJ. N.Fatigue and residual strength degradation for graphite/epoxy composites under tension—compression cyclic loadings. J. Composite Mater., January 1978, 12, 19–39.
15.
PoursartipA.AshbyM. F.BeaumontP. W. R.The fatigue damage mechanics of a carbon fibre composite laminate: I—development of the model. Composites Sci. Technol., 1986, 25(3).
16.
PoursartipA.BeaumontP. W. R.The fatigue damage mechanics of a carbon fibre composite laminate: II—life prediction. Composites Sci. Technol., 198625(4), 283–300.
17.
KulkarniS. V.McLaughlinP.JrPipesR. B.Fatigue of notched fibre composite laminates. Part II: analytical and experimental evaluation. NASA-13931, April 1976.
18.
FarrowI. R.Investigation of FALSTAFF and study of life and residual strength prediction for CFRP structural elements. MoD RAE final report, Contract 202/0152/XR/STR, September 1989.
19.
FarrowI. R.Fatigue of composite materials under aircraft service loading—failure of current analysis methods and a future approach. Aerospace Engineering Department report 445, Bristol University, June 1992.