In this paper, a micromechanical approach is developed to predict the fatigue life and fracture process in different C/SiC composites subjected to different stochastic fatigue loading spectrums at elevated temperatures. Three types of stochastic fatigue load spectrums are considered in the fatigue life prediction at elevated temperature, that is, constant, increasing, and decreasing stochastic stress with cycles. Stress distribution between intact and broken fibers and the broken fibers fraction under stochastic fatigue loading spectrum are determined using the Global Load Sharing criterion considering multiple fatigue damage mechanisms at elevated temperatures. A new damage parameter of fatigue life degradation rate is developed to characterize the effect of stochastic loading on fatigue damage and fracture in C/SiC composites. Relationships between stochastic fatigue loading spectrum, broken fibers fraction, fatigue life, and fatigue life degradation rate in different C/SiC composite are established. Effects of stochastic fatigue loading spectrum type, stress level, and testing temperature on fatigue life degradation rate are discussed. The fatigue life degradation rate is very sensitive to the fiber preform, loading sequence, and testing temperature.
NaslainR. Design, preparation and properties of non-oxide CMCs for application in engines and nuclear reactors: an overview. Compos Sci Technol2004; 64: 155–170.
LiLB. Durability of ceramic matrix composites. Oxford: Woodhead Publishing, 2020.
4.
ZhangYSunYChenX, et al.Life and reliability analysis of C/SiC ceramic matrix composite panels subjected to combined thermal-acoustic loadings. In: 21st International Conference on Composite Materials, Xi’an, China, 20–25 August2017.
5.
AlmeidaRLiYBesserB, et al.Damage analysis of 2.5D C/C-SiC composites subjected to fatigue loadings. J Euro Ceramic Soc2019; 39: 2244–2250.
6.
WangQLinHGengP, et al.Multi-scale damage mechanics method for predicting fatigue life of plain-braided C/SiC composites. Compos Struct2020; 254: 112860.
7.
HouGShangD-GZuoL-X, et al.Fatigue damage identification of SiC coated needled C/SiC composite by acoustic emission. Ceram Int2021; 47: 15129–15138.
8.
LiuYFLiLBZhangZW, et al.Micromechanical modeling cyclic loading/unloading hysteresis loops of 3D needle-punched C/SiC ceramic-matrix composites. Compos Interfaces2021; 1–24. Online. https://doi.org/10.1080/09276440.2021.1926193
9.
LiuYFLiLBZhangZW, et al.Monotonic and cyclic loading/unloading tensile behavior of 3D needle-punched C/SiC ceramic-matrix composites. Mater2021; 14: 57.
10.
ChengQTongXZhengX, et al.Experimental investigation on the fatigue characteristics about high temperature of plain-woven C/SiC composite. J Mech Strength2010; 32: 819–823.
11.
LiLB. Cyclic fatigue behavior of carbon fiber-reinforced ceramic-matrix composites at room and elevated temperatures with different fiber preforms. Mater Sci Eng A2016; 654: 368–378.
12.
LiLB. Tension-tension fatigue behavior of unidirectional C/SiC ceramic-matrix composite at room and elevated temperature and 800°C in air atmosphere. Mater2015; 8: 3316–3333.
13.
LiLB. Damage evolution and life prediction of cross-ply C/SiC ceramic-matrix composite under cyclic fatigue loading at room temperature and 800°C in air. Mater2015; 8: 8539–8560.
14.
MallSEngesserJM. Effects of frequency on fatigue behavior of CVI C/SiC at elevated temperature. Compos Sci Technol2006; 66: 863–874.
15.
YangF. Research on fatigue behavior of 2.5d woven ceramic matrix composites. Master Thesis, Nanjing University of Aeronautics and Astronautics, China, 2011.
16.
ZhangCWangXLiuY, et al.Tensile fatigue of a 2.5D-C/SiC composite at room temperature and 900oC. Mater Design2013; 49: 814–819.
17.
DalmazAReynaudPRoubyD, et al.Mechanical behavior and damage development during cyclic fatigue at high-temperature of a 2.5D carbon/SiC composite. Compos Sci Technol1998; 58: 693–699.
18.
ReynaudPDalmazATallaronC, et al.Apparent stiffening of ceramic-matrix composites induced by cyclic fatigue. J Euro Ceram Soc1998; 18: 1827–1833.
19.
DuSMQiaoSRJiGC, et al.Tension-tension fatigue behavior of 3D-C/SiC composite at room temperature and 1300°C. Mater Eng2002; 9: 22–25.
20.
DuSMQiaoSR. Tension-tension fatigue behavior of 3D-C/SiC composite at 1500°C. J Mater Eng2011; 5: 34–36.
21.
LiLBReynaudPFantozziG. Mechanical hysteresis and damage evolution in C/SiC composites under fatigue loading at room and elevated temperatures. Int J Appl Ceram Technol2019; 16: 2214–2228.
22.
LiuHYuanHYangZ. Damage modeling of oxide/oxide ceramic matrix composites under cyclic loading conditions. Ceram Int2020; 46: 23379–23389.
23.
LiLB. Fatigue life prediction of carbon fiber-reinforced ceramic-matrix composites at room and elevated temperatures. Part I: experimental analysis. Appl Compos Mater2016; 23: 101–117.
24.
LiLB. Fatigue life prediction of carbon fiber-reinforced ceramic-matrix composites at room and elevated temperatures. Part II: experimental comparisons. Appl Compos Mater2015; 22: 961–972.
WuZLiangJFuM, et al.Study of random fatigue behavior of C/SiC composite thin-wall plates. Int J Fatigue2018; 116: 553–561.
27.
SuzukiTMahfuzHTakanashiM. A new stiffness degradation model for fatigue life prediction of GFRPs under random loading. Int J Fatigue2019; 119: 220–228.
28.
GholamiPFarsiMAKouchakzadehMA. Stochastic fatigue life prediction of fiber-reinforced laminated composites by continuum damage mechanics-based damage plastic model. Int J Fatigue2021; 152: 106456.
29.
TelesmanJVerrilliMGhosnL, et al.Characterization of damage accumulation in a C/SiC composite at elevated temperatures. In: Proceedings of the 1997 Conference on Physics & Process Modeling (PPM) and Other Propulsion R&T. Part 1 (of 2), May 1, 1997. Cleveland, OH: NASA Conference Publication10193.
30.
LiLB. Damage development and lifetime prediction of fiber-reinforced ceramic-matrix composites subjected to cyclic loading at 1300°C in vacuum, inert and oxidative atmospheres. Aero Sci Technol2019; 86: 613–629.