Highly densified Al2O3-TiC-Ti3SiC2 composites were fabricated by spark plasma sintering technique and subsequently characterised. From fracture surface observation, it is found that Al2O3 is 0·2-0·4 μm, TiC is 1-1·5 μm and Ti3SiC2 is 1·5-5 μm in grain size. With the increase in Ti3SiC2 volume contents, Vickers hardness of the composites decreases because of the low hardness of monolithic Ti3SiC2. The fracture toughness rises remarkably when the contents of Ti3SiC2 increase, which is attributed to the pullout and microplastic deformation of Ti3SiC2 grains. At the same time, the flexural strength of the composites shows a considerable improvement as well. The electrical conductivity rises significantly as the Ti3SiC2 contents increase because of the formation of Ti3SiC2 network and the increase in conductive phase contents.
XiaT. D., MunirZ. A., TangY. L., ZhaoW. J. and WangT. M.: ‘Structure formation in the combustion synthesis of A1203-TiC composites’, J. Am. Ceram. Soc., 2000, 83, (3), 507–512.
2.
ShiR. X., LiJ., WangD. Z. and YinY. S.: ‘Mechanical properties and thermal shock resistance of A1203-TiC-Co composites’, J. Mater. Eng. Perform., 2009, 18, (4), 414–419.
3.
WahiR. P. and IlschnerB.: ‘Fracture behaviour of composites based on A1203-TiC ’, J. Mater. Sci, 1980, 15, (4), 875–885.
4.
ZhangY. F., WangL. J., JiangW., ChenL. D. and BaiG. Z.: ‘Microstructure and properties of A1203-TiC nanocomposites fabricated by spark plasma sintering from high-energy ball milled reactants’, J. Eur. Ceram. Soc., 2006, 26, (15), 3393–3397.
5.
LiH., SunJ. L. and HuangL. P.: ‘Effects of ductile cobalt on fracture behavior of A1203-TiC ceramic’, Mater. Set Eng. A, 2002, A323, (1–2), 17–20.
6.
BarsoumM. W. and El-RaghyT.: ‘Synthesis and characterization of a remarkable ceramic: Ti3SiC2’, J. Am. Ceram. Soc., 1996, 79, (7), 1953–1956.
7.
TangK., WangC. A., HuangY. and ZanQ. F.: ‘Growth model and morphology of Ti3SiC2 grains’, J. Cryst. Growth, 2001, 222, (1-2), 130–134.
8.
El-RaghyT. and BarsoumM. W.: ‘Processing and mechanical properties of Ti3SiC2: I, reaction path and microstructure evolu-tion’, J. Am. Ceram. Soc., 1999, 82, (10), 2849–2854.
9.
El-RaghyT., BarsoumM. W., ZavaliangosA. and KalidindiS. R.: ‘Processing and mechanical properties of Ti3SiC2: II, effect of grain size and deformation temperature’, J. Am. Ceram. Soc., 1999, 82, (10), 2855–2860.
10.
LuoY. M., LiS. Q., ChenJ., WangR. G., LiJ. Q. and PanW.: ‘Effect of composition on properties of alumina/titanium silicon carbide composites’, Proc. 4th Int. Conf. on ‘Advanced ceramics and glasses’, Maui, HI, USA, November 2001, American Ceramic Society, 3099–3101.
11.
LuoY. M., PanW., LiS. Q., WangR. G. and LiJ. Q.: ‘Fabrication of A1203-Ti3SiC2 composites and mechanical proper-ties evaluation’, Mater. Lett., 2003, 57, (16-17), 2509–2514.
12.
YehC. L., LiR. F. and ShenY. G.: ‘Formation of Ti3SiC2-A1203 in situ composites by SHS involving thermite reactions’, J. Alloys Compd, 2009, 478, (1-2), 699–704.
13.
ChenJ. X. and ZhouY. C.: ‘Strengthening of Ti3A1C2 by incorporation of A1203’, Scr. Mater., 2004, 50, (6), 897–901.
14.
ZhangH. B., BaoY. W. and ZhouY. C.: ‘Current status in layered ternary carbide Ti3SiC2, a review’, J. Mater. ScL Technol, 2009, 25, (1), 1–38.
15.
MogilevskyP., MahT. I., ParthasarathyT. A. and CookeC. M.: ‘Toughening of SiC with Ti3SiC2 particles’, J. Am. Ceram. Soc., 2006, 89, (2), 633–637.
16.
LiangB. Y. and JinS. Z.: ‘Effect of alloying time on fabrication of Ti3Si(A1)C2 by spark plasma sintering’, Adv. Appl. Ceram., 2009, 108, (3), 162–166.
17.
ZhangJ. F., WangL. J., ShiL., JiangW. and ChenL. D.: ‘Rapid fabrication of Ti3SiC2-SiC nanocomposite using the spark plasma sintering-reactive synthesis (SPS-RS) method’, Scr. Mater., 2007, 56, (3), 241–244.
18.
FuR. L. and AgathopoulosS.: Nanostructure and bimodal structure of Si3N4 ceramics developed by spark plasma sintering method‘, Adv. Appl. Ceram., 2009, 108, (6), 358–362.
19.
ZhangJ. F., WangL. J., JiangW. and ChenL. D.: ‘Effect of TiC content on the microstructure and properties of Ti3SiC2-TiC composites in situ fabricated by spark plasma sintering’, Mater. Set Eng. A, 2008, A487, (1–2), 137–143.
20.
WangL. J., JiangW., ChenL. D. and BaiG. Z.: ‘Microstructure of Ti55i3-TiC-Ti3SiC2 and Ti55i3-TiC nanocomposites in situ synthe-sized by spark plasma sintering’, J. Mater. Res., 2004, 19, (10), 3004–3008.
21.
WangL. J., JiangW., BaiS. Q., WangG. and ChenL. D.: ‘Rapid fabrication of nano-structured Ti55i3-TiC composites by spark plasma sintering’, J. Inorg. Mater., 2004, 19, (6), 1436–1440.
22.
EvansA. G. and CharlesE. A.: ‘Fracture toughness determinations by indentation’, J. Am. Ceram. Soc., 1976, 59, (7-8), 371–372.
23.
LowI. M., LeeS. K., LawnB. R. and BarsoumM. W.: ‘Contact damage accumulation in Ti3SiC2’, J. Ant Ceram. Soc., 1998, 81, (1), 225–228.
24.
ZhangJ. F., WuT., WangL. J., JiangW. and ChenL. D.: ‘Microstructure and properties of Ti3SiC2/SiC nanocomposites fabricated by spark plasma sintering’, Compos. Sci. Technol, 2008, 68, (2), 499–505.
25.
LuxF.: ‘Models proposed to explain the electrical-conductivity of mixtures made of conductive and insulating materials’, J. Mater. Set, 1993, 28, (2), 285–301.