Structural ceramics were manufactured from industrial byproducts and lime by a compression moulding/vacuum dewatering technique. Treatment of these ceramics with supercritical carbon dioxide was found to both significantly increase their flexural strength and activate cementation in the industrial byproducts at least as efficiently as heat curing. Flexural strengths of up to 10 MPa were achieved. Strength improvements were associated with decreased porosity and conversion of calcium hydroxide to calcium carbonate. Life cycle assessment of proposed products made from such materials indicated that the total reduction in embodied carbon dioxide achieved, as a result of combining use of byproducts with recombination of carbon dioxide, was up to 70%.
PageC. L.: ‘Corrosion and protection of reinforcing steel in concrete’, in ‘Durability of concrete and cement composites’ (ed. PageC. L. and PageM. M.), 145–151; 2007, Cambridge, Woodhead Publishing.
2.
RoyS. K., PohK. B. and NorthwoodD. O.: ‘Durability of concrete — accelerated carbonation and weathering studies’, Cem. Goner. Res., 2004, 34, 597–606.
3.
ThieryM., VillainG., DanglaP. and PlatretG.: ‘Investigation of the carbonation front shape on cementitious materials: effects of the chemical kinetics’, Gem. Goner. Res., 2007, 37, 1047–1058.
4.
Garcia-GonzalezC. A., HidalgoA., AndradeC., AlonsoM. C., FraileJ., Lopez-PeriagoA. M. and DomingoC.: ‘Modification of composition and microstructure of Portland cement pastes as a result of natural and supercritical carbonate procedures’, Ind Eng. Chem. Res., 2006, 45, 4985–4992.
5.
JonesR. H.: ‘Cement treated with high pressure CO2’, US Patent5518540, 1996.
6.
KnopfF. C., RoyA., SamrowH. A. and DooleyK. M.: ‘High pressure moulding and carbonation of cementitious materials’, Ind Eng. Chem. Res., 1999, 38, 2641–2649.
7.
ShortN. R., PurnellP. and PageC. L.: ‘Preliminary investigations into supercritical carbonation of cement pastes’, J. Mater. Sci., 2001, 36, 35–41.
8.
El-TurkiA., CarterM. A., WilsonM. A., BallR. J. and AllenG. C.: ‘A microbalance study of the effects of hydraulicity and sand grain size on carbonation of lime and cement’, Constr. Build Mater., 2009, 23, 1423–1428.
9.
PurnellP., ShortN. R. and PageC. L.: ‘Supercritical carbonation of glass-fibre reinforced cement. Part I: Mechanical testing and chemical analysis’, Composites A, 2001, 32A, 1777–1787.
10.
PurnellP., SeneviratneA. M. G., ShortN. R. and PageC. L.: ‘Supercritical carbonation of glass-fibre reinforced cement. Part II: Microstructural observations’. Composites A, 2003, 34A, 1105–1112.
11.
SeneviratneA. M. G., ShortN. R., PurnellP. and PageC. L.: ‘Preliminary investigations of the dimensional stability of super-critically carbonated glass-fibre reinforced cement’, Gem. Goner. Res., 2002, 32, 1639–1644.
12.
ShortN. R., BroughA. R., SeneviratneA. M. G., PageC. L. and PurnellP.: ‘Preliminary investigations of the fine pore structure of super-critically carbonated cement pastes’, J. Mater. Set, 2004, 39, 5683–5687.
13.
van GervenT., van BaelenD., DutreV. and VandecasteeleC.: ‘Influence of carbonation and carbonation methods on leaching of metals from mortars’, Gem. Goner. Res., 2004, 34, (1), 149–156.
14.
Garcia-GonzalezC. A., HidalgoA., AndradeC., AlonsoM. C., FraileJ., Lopez-PeriagoA. M. and DomingoC.: ‘Modification of composition and microstructure of Portland cement pastes as a result of natural and supercritical carbonate procedures’, Ind Eng. Chem. Res., 2006, 45, 4985–4992.
15.
HidalgoA., DomingoC., GarciaC., PetitS., AndradeC. and AlonsoC.: ‘Microstructural changes induced in Portland cement-based materials due to natural and supercritical carbona-tion’, J. Mater. Set, 2008, 43, 3101–3111.
16.
CultroneG., SebastiánE. and Ortega HuertasM.: ‘Forced and natural carbonation of lime-based mortars with and without additives: mineralogical and textural changes’, Cent Concr. Res., 2005, 35, 2278–2289.
17.
GuimaraesM., DamtoftJ. S., PadeC. and GlavindM.: ‘The CO2 uptake of concrete during a 100 year perspective’, Proc. 1st Int. Conf. on ‘Accelerated carbonation for environmental and materials engineering’, London, UK, June2006, The Royal Society, 99–100.
18.
AstrupT., MosbaekH. and ChristensenT. H.: ‘Assessment of long-term leaching from waste incineration air-pollution-control residues’. Waste Manage., 2006, 26, (8), 803–814.
19.
FarahiE.: ‘Advanced calcareous ceramics via novel green processing and super-critical carbonation’, PhD thesis, University of Warwick, Warwick, UK, 2009.
20.
PurnellP., FarahiE., ShortN. R. and AgbonlahorS.: ‘Advanced calcareous composites: mechanical processing and supercritical carbonation;, Proc. 27th Annual Cement and Concrete Science Meet., London, UK, September 2007, The Institute of Materials, Minerals and Mining, 65–68.
21.
FarahiE., PurnellP. and ShortN. R.: ‘Advanced calcareous ceramics via novel green processing and supercritical carbonation’, in Proc. Conf. on ‘Sustainable construction materials and technologies’, 359–366; 2007, London, Taylor & Francis.
22.
AligizakiK. K.: ‘Pore structure of cement based materials: testing, interpretation and requirement’; 2006, London, Taylor & Francis.
PrusinskiJ. R., MarceauM. L. and VanGreenM. G.: ‘Life cycle inventory of slag cement concrete’, Proc. 8th CANMET/ACI Int. Conf. on ‘Fly ash, silica fume, slag, and natural pozzolans in concrete’, Las Vegas, NV, USA, May 2004, EPRI, 65–80.
26.
WorrellE., PriceL., MartinN., HendricksC. and MeidaL.: ‘Carbon dioxide emissions from the global cement industry’, Annu. Rev. Energy Environ., 2001, 26, 303–329.
27.
GoodbrakeC. J., YoungJ. F. and BergerR. L.: J. Am. Ceram. Soc., 1979, 62, 488.
28.
Department for Business Enterprise and Regulatory Reform: ‘Monthly statistics of building materials and components’, No. 408, URN 09/313b, Her Majesty's Stationery Office, London, UK, 2009.