In this contribution, the author reports the effect of salt spray and oxygenated salt water immersion and 100% relative humidity conditions on the fatigue resistance of filament wound glass fibre reinforced/vinyl ester thermoset pipes. Exposure to salt spray and oxygenated sea water immersion for periods of up to 10 000 h produced varying degrees of degradation in the fatigue resistance of glass fibre reinforced plastic pipes. The most severe degradation in fatigue resistance was observed at an exposure of 300 h under salt water spray condition and at 10 000 h of exposure under oxygenated salt water immersion condition.
OswaldKJ: ‘The effects of chemical and petroleum service on epoxy and vinyl ester filament wound pipe’, Proc. Conf. Corrosion ’84, New Orleans, LA, USA, April 1984, NACE, Paper 18.
2.
JamondRM, HoffardTA, NovinsonT, MalvarLJ: ‘Composites in simulated marine environments’, Special publication no. SP-2083-SHR, Naval Facilities Engineering Service Center, Port Hueneme, CA, USA, 2000.
3.
WilliamsG: ‘Oil industry experiences with fiberglass components’, Proc. Conf. on ‘Offshore technology’, Houston, TX, USA, April 1987, 211–220.
4.
HammamiA, Al-GhuilaniN: ‘Durability and environmental degradation of glass vinyl ester composites’, Polym. Compos., 2004, 25, (6), 609–616.
5.
KootsookosA, MouritzAP: ‘Seawater durability of glass- and carbon-polymer composites’, Compos. Sci. Technol., 2004, 64, 1503–1511.
6.
HoferKE, SkaperGN, BennettLC: ‘Effect of moisture on fatigue and residual strength losses for various composites’, J. Reinf. Plast. Compos., 1987, 6, 53–65.
7.
KarbhariVM, RiveraJ, ZhangJ: ‘Low-temperature hygrothermal degradation of ambient cured E-glass/vinylester composites’, J. Appl. Polym. Sci., 2002, 86, 2255–2260.
8.
HuangG: ‘Behaviours of glass fibre/unsaturated polyester composites under seawater environment’, Mater. Des. Mater. Des., 2009, 30, 1337–1340.
9.
YaoJ, ZiegmanG: ‘Equivalence of moisture and temperature in accelerated test method and its application in prediction of long-term properties of glass-fiber reinforced epoxy pipe specimen’, Polym. Test., 2006, 25, 49–157.
10.
MiyanoY, NakadaM: ‘Accelerated testing for long-term durability of FRP laminates for marine use’, J. Compos. Mater., 2005, 39, (1), 5–20.
11.
NishizakiI, MeiarashiS: ‘Long-term deterioration of GFRP in water and moist environment’, J. Compos. Constr., 2002, 6, 21–27.
12.
AielloMA, OmbresL: ‘Environmental effects on the mechanical properties of glass-FRP and aramid-FRP rebars’, Mech. Compos. Mater., 2000, 36, (5), 395–398.
13.
JosephE, PerreuxD: ‘Fatigue behaviour of glass-fibre/epoxy-matrix filament-wound pipes: tension loading tests and results’, Compos. Sci. Technol., 1994, 52, (4), 469–480.
14.
WatanabeM: ‘Effect of water environment on fatigue behavior of fiberglass reinforced plastics’, Proc. 5th Conf. on ‘Composite materials: testing and design’, (ed. , TsaiS W, ed), 345–367, ASTM STP 674; 1979, Philadelphia, PA, American Society for Testing and Materials.
HoferKE, BenettLC, StanderM: ‘Effect of various fiber surface treatments on the fatigue behavior of glass fabric composites in high humidity environment’, Proc. 31st Annual Technical Conf. of SPI, Washington, DC, USA, February 1976, The Society of the Plastics Industry, Inc., section 6-A.
17.
ShihGC, EbertLJ: ‘The effect of the fiber/matrix interface on the flexural fatigue performance of unidirectional fiberglass composites’, Compos. Sci. Technol., 1987, 28, 147–161.
18.
EllisB, FoundFS: ‘The effect of water absorption on polyester/chopped strand mat laminates’, Composites, 1983, 4, (3), 237–243.
19.
MandellJF, McGarryFJ, BartonWD, DemchickRP: ‘Effect of water on the crack propagation rate in fiberglass laminates under static and dynamic loading’, Proc. 31st Annual Technical Conf. of the Reinforced Plastics/Composites Institute, Washington, DC, USA, February 1976, The Society of the Plastics Industry, Inc., paper 21-B.
MandellJF, MeierU: ‘Effects of stress ratio, frequency, and loading time on the tensile fatigue of glass reinforced plastics’, in ‘Long term behavior of composites’, (ed. , O'BrienT K), 55, ASTM STP 813; 1983, Philadelphia, PA, ASTM.
22.
LiaoK, SchultheiszCR, HunstonDL: ‘Long-term environmental fatigue of pultruded glass-fiber-reinforced composites under flexural loading’, Int. J. Fatigue, 1999, 21, 485–495.
23.
VauthierE, AbryJC, BailliezT, ChateauminoisA: ‘Interaction between hygrothermal ageing and fatigue damage in unidirectional glass/epoxy composites’, Compos. Sci. Technol., 1998, 55, 687–692.
24.
EllyinF, MaserR: ‘Environmental effects on the mechanical properties of glass-fiber epoxy composite tubular specimens’, Compos. Sci. Technol., 2004, 64, (12), 1863–1874.
25.
McBagonluriF, GarciaK, HayesM, VergheseKNE, LeskoJJ: ‘Characterization of fatigue and combined environment on durability performance of glass/vinyl ester composite for infrastructure applications’, Int. J. Fatigue, 2000, 22, 53–64.
26.
ASTM D2290 08: ‘Standard test method for apparent hoop tensile strength of plastic or reinforced plastic pipe by split disk method’, ASTM International, West Conshohocken, PA, USA.