The effect of 0–4 wt- Sn addition on the microstructure and tensile properties of AZ80 alloys was investigated. The results indicated that Mg2Sn particles were barely formed during the extrusion process until the content of Sn is >2 wt-. The dislocation density in alloys after extrusion declined with the addition of Sn due to the promotion of dynamic recrystallisation after adding Sn. In aging treatment, Mg17Al12 precipitates were promoted by Sn and the phases distributed uniformly at low density level of dislocation. The AZ80-2 wt- Sn alloy possessed the excellent tensile properties in as extruded and as aged state.
LetzigD, SwiostekJ, BohlenJ, BeavenPA and KainerKU: ‘Wrought magnesium alloys for structural applications’, Mater. Sci. Technol., 2008, 8, (24), 991–996.
4.
ZhangMX and KellyPM: ‘Crystallography of Mg17Al12 precipitates in AZ91D alloy’, Scr. Mater., 2003, 5, (48), 647–652.
5.
DulyD, SimonJP and BrechetY: ‘On the competition between continuous and discontinuous precipitations in binary Mg–Al alloys’, Acta Metall. Mater., 1995, 1, (43), 101–106.
6.
QiFG, ZhangDF, ZhuZT, XuXX and ShiGL: ‘Effect of heat treatment on microstructure and mechanical properties of extruded ZM61 magnesium alloy’, Mater. Sci. Technol., 2012, 12, (28), 1426–1433.
7.
ZhuT, FuP, PengL, HuX, ZhuS and DingW: ‘Effects of Mn addition on the microstructure and mechanical properties of cast Mg–9Al–2Sn (wt.) alloy’, J. Mag. Alloys, 2014, 1, (2), 27–35.
8.
TurenY: ‘Effect of Sn addition on microstructure, mechanical and casting properties of AZ91 alloy’, Mater. Des., 2013, (49), 1009–1015.
9.
LiRG, XuY, QiW, AnJ, LuY, CaoZY and LiuYB: ‘Effect of Sn on the microstructure and compressive deformation behaviour of the AZ91D aging alloy’, Mater. Charact., 2008, 11, (59), 1643–1649.
10.
JungIC, KimYK, ChoTH, OhSH, KimTE, ShonSW, KimWT and KimDH: ‘Suppression of discontinuous precipitation in AZ91 by addition of Sn’, Met. Mater. Int., 2013, 1, (20), 99–103.
11.
WangC, ZhangH, WangH, LiuG and JiangQ: ‘Effects of doping atoms on the generalized stacking-fault energies of Mg alloys from first-principles calculations’, Scr. Mater., 2013, 6, (69), 445–448.
12.
MuzykM, PakielaZ and KurzydlowskiKJ: ‘Generalized stacking fault energy in magnesium alloys: density functional theory calculations’, Scr. Mater., 2012, 5, (66), 219–222.
13.
WilliamsonGK and HallWH: ‘X-ray line broadening from filed aluminium and wolfram’, Acta Met., 1953, 1, (1), 22–31.
14.
RohatgiA and VecchioKS: ‘The variation of dislocation density as a function of the stacking fault energy in shock-deformed FCC materials’, Mater. Sci. Eng. A, 2002, A1, (328), 256–266.
15.
WangYM, SansozF, LaGrangeT, OttRT, MarianJ, BarbeeTJ and HamzaAV: ‘Defective twin boundaries in nanotwinned metals’, Nat. Mater., 2013, 8, (12), 697–702.
16.
WilliamsonGB and SmallmanRE: ‘III. Dislocation densities in some annealed and cold-worked metals from measurements on the X-ray debyescherrer spectrum’, Philos. Mag., 1956, 34–46.
17.
AgnewSR and DuyguluÖ: ‘Plastic anisotropy and the role of non-basal slip in magnesium alloy AZ31B’, Int. J. Plast., 2005, 6, (21), 1161–1193.