Enhance cycling performance of LiMn 2 O 4 cathode by Sr 2+ and Cr 3+ doping

Abstract

Spinel LiSr_0·1Cr_0·1Mn_1·8O₄ was synthesised by high temperature solid state method in order to enhance the electrochemical performance. The LiSr_0·1Cr_0·1Mn_1·8O₄ (LSCMO) materials were characterised by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical tests. The XRD and SEM studies confirm that LSCMO had spinel crystal structure with a space group of Fd3m, and the particle of LSCMO shows irregular shape. The cyclic voltammetry data illustrated that the heavy current charge–discharge performance of LMO was improved by Sr²⁺ and Cr³⁺ doping. The galvanostatic charge–discharge of LSCMO cathode materials was measured at 1, 5, 10 and 20 C. The results indicated that LSCMO improved the capacity retention.