Stress corrosion cracking (SCC) behaviours of Z3CN20-09M stainless steel in high temperature water containing Cl− were studied. The results indicated that SCC sensitivity was inconsistent with test temperature. The minimum and maximum of SCC sensitivity occurred at 320 and 290°C respectively, and SCC sensitivity at 250°C fell between them. SCC crack initiated preferentially at bottom of corrosion pit or along phase boundary between austenite and ferrite, and its propagation depended on relative orientation to the phase boundary. SCC crack parallel to the phase boundary propagated along the phase boundary, while that perpendicular to the phase boundary was hindered to propagate.
SceniniF; GovenderK, LyonS and SherryA: ‘Stress corrosion cracking of Ru doped 304 stainless steel in high temperature water’, Corros. Eng. Sci. Technol., 2012, 47, 498–506.
2.
GovenderK, SceniniF, LyonS and SherryA: ‘Influence of Pd and Ru additions on stress corrosion cracking of austenitic stainless steels’, Corros. Eng. Sci. Technol., 2012, 47, 507–515.
3.
Albores-SilvaOE, CharlesEA and PadovaniC: ‘Effect of chloride deposition on stress corrosion cracking of 316L stainless steel used for intermediate level radioactive waste containers’, Corros. Eng. Sci. Technol., 2011, 46, 124–128.
4.
ScottPM: ‘Environment-assisted cracking in austenitic components’, Int. J. Pres. Ves. Pip., 1996, 65, 255–264.
5.
ScottPM and BenhamouC: ‘An overview of recent observation and interpretation of IGSCC in nickel base alloys in PWR primary water’, Proc. 10th Int. Symp. on ‘Environmental degradation materials nuclear power systems–water reactors’, NACE, 2001.
6.
AndresenPL: ‘Effects of temperature on crack growth rate in sensitized type 304 stainless steel and Alloy 600’, Corrosion, 1993, 49, 714–725.
7.
KondoT, NakajimaH and RyukichiN: ‘Metallographic investigation on the cladding failure in the pressure vessel of a BWR’, Nucl. Eng. Des., 1971, 16, 205–222.
8.
AtkinsonJD and ForrestJE: ‘Factors influencing the rate of growth of fatigue cracks in RPV steels exposed to a simulated PWR primary water environment’, Corros. Sci., 1985, 25, 607–631.
9.
ChopraOK and ParkHB: ‘Mechanism of fatigue crack initiation in light water reactor coolant environments’, Proc. Int. Conf. on ‘Fatigue of reactor components’, Electric Power Research Institute, 2000.
10.
KatadaY and NagataN: ‘The effect of temperature on fatigue crack growth behavior of a low alloy pressure vessel steel in a simulated BWR environment’, Corros. Sci., 1985, 25, 693–704.
11.
AriokaK: ‘Effect of temperature, hydrogen, and boric acid concentration on IGSCC susceptibility of annealed 316 stainless steel’, Proc. Int. Symp. Fontevraud 5, French Nuclear Society, 2002.
12.
AriokaK, KaneshimaK and YamadaT: ‘Influence of hydrogen, boric acid, and grain boundary carbide on IGSCC behaviors of SUS316 under hydrogenated PWR primary water’, Proc. 11th Int. Symp. on ‘Environmental degradation of materials in nuclear power systems—water reactors’, American Nuclear Society, 2003.
13.
AndresenPL and AngeliuTM: ‘Effect of martensite and hydrogen on SCC of stainless steels and Alloy 600’, Proc. CORROSION/2001, NACE, 2001.
14.
AriokaK, YamadaT, TerachiT and ChibaG: ‘Cold work and temperature dependence of stress corrosion crack growth of austenitic stainless steels in hydrogenated and oxygenated high-temperature water’, Corrosion, 2007, 63, 1114–1123.
15.
AndresenPL and AngeliuTM: ‘Effect of deformation on SCC of unsensitized stainless steel’, Proc. CORROSION/2000, NACE, 2000.
16.
LuZP, ShojiT, TakedaY, KaiA and ItoY: ‘Effects of loading mode and temperature on stress corrosion crack growth rates of a cold-worked type 316L stainless steel in oxygenated pure water’, Corrosion, 2007, 63, 1021–1032.
17.
AgrawalAK, WelchGA, BegleyJA and StaehleRW: ‘SCC of sensitized and quench-annealed type 304 stainless steel in high-purity water’, Proc. CORROSION/1978, NACE, 1978.
18.
AriokaK, HouraiM, OkamotoS and OnimuraK: ‘The effect of boric acid, solution temperature, and sensitization on SCC behavior under elevated temperature water’, in: CORROSION/83, NACE, 1983.
19.
RutherWE, SoppetWK and KassnerTF: ‘Effect of temperature and ionic impurities at very low concentrations on stress corrosion cracking of AISI 304 stainless steel’, Corrosion, 1988, 44, 791–799.
20.
AsakuraY, KarasawaH and SakagamiM: ‘Relationships between corrosion behavior of AISI 304 stainless steel in high temperature pure water and its oxide film structures’, Corrosion, 1989, 45, 119–124.
WangZX, XueF, GuoWH, ShiHJ, ZhangGD and ShuGG: ‘Investigation of thermal aging damage mechanism of the cast duplex stainless steel’, Nucl. Eng. Des., 2010, 240, 2538–2543.
26.
WangZX, XueF, JiangJW, TiWX and YuWW: ‘Experimental evaluation of temper aging embrittlement of cast austenitic stainless steel from PWR’, Eng. Fail. Anal., 2011, 18, 403–410.
27.
YaoYH, WeiJF and WangZP: ‘Effect of long-term thermal aging on the mechanical properties of casting duplex stainless steels’, Mater. Sci. Eng. A, 2012, A551, 116–121.
28.
AmzallagC and VaillantF: ‘Stress corrosion crack propagation rates in reactor vessel head penetrations in Alloy 600’, Proc. 9th Int. Symp. on ‘Environmental degradation of materials in nuclear power systems – water reactor’, TMS, 1999.
29.
CassagneT, CaronD, DaretJ and LefevreY: ‘Stress corrosion crack growth rate measurements in Alloys 600 and 182 in primary water loop under constant load’, Proc. 9th Int. Symp. on ‘Environmental degradation of materials in nuclear power systems – water reactor’, The Minerals, Metals, and Materials Society, 1999.
30.
VaillantF, AmzallagC and ChampredondeJ: ‘Crack growth rate measurements of Alloy 600 vessel head penetrations’, Proc. 8th Int. Symp. on ‘Environmental degradation of materials in nuclear power systems – water reactors’, American Nuclear Society, 1997.
31.
KimYJ: ‘Characterization of the oxide film formed on type 316 stainless steel in 288°C water in cyclic normal and hydrogen water chemistries’, Corrosion, 1995, 51, 849–860.
32.
ListerDH, DavidsonRD and McAlpineE: ‘The mechanism and kinetics of corrosion product release from stainless steel in lithiated high temperature water’, Corros. Sci., 1987, 27, 125–140.
33.
RobertsonJ: ‘The mechanism of high temperature aqueous corrosion of stainless steel’, Corros. Sci., 1991, 32, 443–465.
34.
TappingRL, DavidsonRD, McAlpineE and ListerDH: ‘The composition and morphology of oxide films formed on type 304 stainless steel in lithiated high temperature water’, Corros. Sci., 1986, 26, 563–576.