The objective of the study is to correlate the effects of temperature, H2S and Cl− concentration on the passivity limits and the onset of localised corrosion in UNS S31603 stainless steel by evaluating the changes in the semiconducting behaviour exhibited by the passive layer. The study is accomplished experimentally by using a combination of direct and alternate current electrochemical methods to study the passive layer formed by the stainless steel, in equilibrium with a gas phase at 2.8 MPa (400 psi) containing up to 60% mol of H2S (bal. CO2) at temperatures from 25°C and up to 150°C. The results obtained indicate that the decrease of the passive layer stability formed on the UNS S31603 stainless steel is consistent with the increase in the electron donor carrier density. This is observed as a consequence of the effect of temperature and the concentration of Cl− and H2S. In this context, the Cl− content in the brine was found to exert a larger effect than the H2S activity at constant temperature.
AI-SiddiqiADaweRA.A review of petroleum engineering aspects of Qatar's oil and gas. Eng J Univ Qatar1998; 11: 11–45.
2.
TjeltaMKvarekvålJ. Electrochemistry of iron sulfide and its galvanic coupling to carbon steel in sour aqueous solutions. Paper 7478 in CORROSION 2016. Vancouver (CA): NACE International; 2016.
3.
PessuFHuaYBarkerRNevilleA. An investigation of the overall corrosion behaviour of X65 (UNS K03014) carbon steel in different H 2S-CO 2-containing environments. Paper 7643 in CORROSION 2016. Vancouver (CA): NACE International; 2016.
4.
ZhangGAZengYGuoXP. Electrochemical corrosion behavior of carbon steel under dynamic high pressure H2S/CO2 environment. Corros Sci. 2012; 65: 37–47.
5.
CaseRMahajanamSDunnJ. Evaluation of corrosivity of produced fluids during SAGD operations. Paper 4273 in CORROSION 2014. San Antonio (TX): NACE International; 2014.
6.
SunWLiCLingS. Laboratory study of sour localized/pitting corrosion. Paper 11080 in CORROSION 2011. Houston (TX): NACE International; 2011.
7.
SongFHuizingaSSkogsbergL. Qualification of super 13Cr-110 in HPHT sour well service with concentrated brines. Paper 7126 in CORROSION 2016. Vancouver (CA): NACE International; 2016.
8.
SiegmundGSchmittGKuhlL. Unexpected sour cracking resistance of duplex and superduplex steels. Paper 7631 in CORROSION 2016.Vancouver (CA): NACE International; 2016.
9.
GuiFCaoLThodlaRSridharN. Localized corrosion and stress corrosion cracking of UNS S32750 in H 2S containing environment. Paper 7397 in CORROSION 2016.Vancouver (CA): NACE International; 2016.
10.
MeckNSKaneRChambersB. Sour service limits of martensitic stainless steels: a review of current knowledge, test methods and development work. Paper 2639 in CORROSION 2013. Orlando (FL): NACE International; 2013.
11.
Al-HarthiASMJongJGD. Evaluating the SCC chloride limit for UNS S31603 in sour service. Paper 2676 in CORROSION 2013. Orlando (FL): NACE International; 2013.
12.
NACEA. TM0177-2016 laboratory testing of metals for resistance to sulfide stress cracking and stress corrosion cracking in H 2S. Houston (TX): NACE International; 2016.
13.
NACE. TM0198-2011 slow strain rate test method for screening corrosion-resistant alloys for stress corrosion cracking in sour. Vol. TM0198-2011. Houston (TX): NACE International; 2011.
14.
ANSI/NACE, MR0175/ISO 15156-3 Petroleum and natural gas industries—materials for use in H 2S-containing environments in oil and gas production—Part 3: cracking-resistant CRAs (corrosion- resistant alloys) and other alloys. MR0175/ISO 15156-3, Houston, TX, 2009.
15.
ASTM G. 150-99 Standard test method for electrochemical critical pitting temperature testing of stainless steels. G 150-99. 2004.
16.
MacdonaldDD.Passivity–the key to our metals-based civilization. Pure Appl Chem. 1999; 71 (6): 951–978.
17.
NewmanRC.Whitney award lecture: understanding the corrosion of stainless steel. Corrosion. 2001; 57 (12): 1030–1041.
18.
MacdonaldDD.The point defect model for the passive state.J Electrochem Soc. 1992; 139 (12): 3434–3449.
19.
RhodesPR.Environment-assisted cracking of corrosion-resistant alloys in oil and gas production environments: a review. Corrosion.2001; 57 (11): 923–966.
20.
ZhangYUrquidi-MacdonaldMEngelhardtGRMacdonaldDD.Development of localized corrosion damage on low pressure turbine disks and blades: I. passivity.Electrochim Acta2012; 69:1–11.
21.
MacdonaldDD.The history of the point defect model for the passive state: a brief review of film growth aspects. Electrochim Acta. 2011; 56 (4): 1761–1772.
22.
BanaśJLelek-BorkowskaUMazurkiewiczB. Effect of CO2 and H2S on the composition and stability of passive film on iron alloys in geothermal water. Electrochim Acta. 2007; 52 (18): 5704–5714.
23.
CaseRPRinconHEMcIntyreDr.Corrosion. J Eng Sci. 2012; 68 (3): 035004-1–035004-12.
24.
CaseRNewmanRCOlsenS. Pit growth behavior of modified 13 Cr steel in sour environments. EUROCORR 2000. Materials, I. o., Ed.: London, UK; 2000.
25.
RinconHECaseRPTangX. Determination of the critical pitting temperature of stainless steel using electrochemical testing techniques. Paper 1334 in CORROSION 2012.Salt Lake City (UT): NACE International; 2012.
26.
LiWSLuoJL.Electrochemical investigations on formation and pitting susceptibility of passive films on iron and iron-based alloys. Int. J. Electrochem. Sci. 2007; 2: 627–665.
27.
ChoEKwonH. A study on the electronic properties of passive film formed on fe-20Cr by photo-electrochemical and mott-schottky analysis. Corrosion Sci. Technol., 2002;31(4): 275-280.
28.
FerreiraMGSHakikiNEGoodletG. Influence of the temperature of film formation on the electronic structure of oxide films formed on 304 stainless steel. Electrochim Acta. 2001; 46: 3767–3776.
KakaeiMNNeshatiJHoseinyH. Compensating the effects of frequency dispersion in Mott–Schottky analyses of passive films. Corrosion. 2017; 73 (8): 970–978.
31.
KriksunovLBMacdonaldDDMillettPJ.Tungsten/tungsten oxide pH sensing electrode for high temperature aqueous environments.J Electrochem Soc. 1994; 141 (11): 3002–3005.
32.
AyelloFEvansKThodlaR. Effect Of Impurities On Corrosion Of Steel In Supercritical CO 2. Paper 10193 in CORROSION 2010. Houston (TX): NACE International; 2010.
WangZZhangLZhangZ. Combined effect of pH and H2S on the structure of passive film formed on type 316L stainless steel. Appl Surf Sci. 2018; 458: 686–699.
35.
YangSMacdonaldDD.Theoretical and experimental studies of the pitting of type 316L stainless steel in borate buffer solution containing nitrate ion.Electrochim. Acta. 2007; 52 (5): 1871–1879.
36.
HarunaTMacdonaldDD.Theoretical prediction of the scan rate dependencies of the pitting potential and the probability distribution in the induction time.J Electrochem Soc. 1997; 144 (5): 1574–1581.
37.
ToorI-u-H. Mott-Schottky analysis of passive films on Si containing stainless steel alloys. J Electrochem Soc. 2011; 158 (11): C391–C395.
38.
DingJZhangLLuM. The electrochemical behaviour of 316L austenitic stainless steel in Cl− containing environment under different H2S partial pressures. Appl Surf Sci. 2014; 289: 33–41.
39.
MatSNewmanRC. Local chemistry aspects of hydrogen sulfide-assisted stress-corrosion cracking of stainless steels. Paper 228 in CORROSION 94. National Association of Corrosion Engineers; Houston, TX 1994.
40.
MoayedMHNewmanRC.Evolution of current transients and morphology of metastable and stable pitting on stainless steel near the critical pitting temperature. Corros Sci. 2006; 48 (4): 1004–1018.
41.
LaycockNJNewmanRC.Temperature dependence of pitting potentials for austenitic stainless steels above their critical pitting temperature. Corros Sci. 1998; 40 (6): 887–902.
42.
MoayedMHNewmanRC.The relationship between pit chemistry and pit geometry near the critical pitting temperature. J Electrochem Soc. 2006; 153 (8): B330.