The present paper deals with a new vanadium and nitrogen alloyed steel for heavy products applications, which offer improved toughness and strength properties as compare with a commercial heavy product steel. A strong structural refinement, by introducing acicular ferrite microstructure, combined with an optimum cooling process can be utilised to develop tough, high strength thick products.
HoedlH., WimmerF., MayrhoferK. F., SpiessJ. S., HartmannG., DenglerJ. M. and BaumannH.: AISE Steel Technol, 2002, 79, 26.
7.
EvansJ. F. and ClarkM. T.: AISE Steel Technol., 2002, 79, 49.
8.
DonnayB.: ‘Refinement and development of homogeneous microstructures through the thickness of heavy products’, RFS-CR-04030, Research Funds Coal and Steel, European Union, Bruxelles, Belgium, 2008.
9.
Garcia de AndresC., CapdevilaC., MadariagaI. and GutierrezI.: Scr. Mater., 2001, 45, 709.
10.
LinazaM. A., RomeroJ. L., Rodriguez-IbabeJ. M. and UrcolaJ. J.: Scr. Mater., 1995, 32, 395.
11.
CapdevilaC., CaballeroF. G. and Garcia de AndresC.: Scr. Mater., 2001, 44, 593.
12.
CapdevilaC., C. Garcia de Andres and F. G. Caballero: Scr. Mater., 2001, 44, 129.
13.
National PhysicalMTDATALaboratory, Teddington, UK, 2003, available atwww.npl.co.uk/mtdata.
14.
CapdevilaC., CaballeroF. G. and Garcia de AndresC.: Acta Mater., 2002, 50, 4629.
15.
CaballeroF. G., C. Capdevila and C. Garcia de Andres: Scr. Mater., 2000, 42, 1159.
16.
CaballeroF. G., C. Capdevila and C. Garcia de Andres: Mater. Sci Technol., 2001, 17, 1114.
17.
‘Standard test method for plane strain toughness of metallic materials’, E-399, ASTM, Philadelphia, PA, USA, 1995.
18.
PineauA.: in ‘Advances in fracture research ICF5’, (ed. FrancoisD.), 553; 1982, Oxford, Pergamon Press.
19.
MackenzieA. C, HancockJ. W. and BrownD. K.: Eng. Fract. Mech., 1977, 9, 167.
20.
SpeichG. R. and SpitzingW. A.: Met. Trans., 1982, 13, 2239.