The connection between the formation of cold laps and the presence of Mn–Si oxides was studied. The underlying purpose is to understand the fundamental mechanisms of cold lap formation and to avoid it. Tandem gas metal arc welding (GMAW) was used to produce welded specimens in two different shielding gases (pure Ar and pure CO2) with base metal S355 MC (EN-10149-2) and wire G3Si1 (EN ISO 14341-A). Cross-sections of welds in the cold lap location were evaluated by light optical microscopy and scanning electron microscopy combined with energy dispersive spectroscopy. The results showed that the Mn–Si oxides significantly enhanced cold laps formation, especially the overlap type cold lap formation. The Mn–Si oxides originated from oxidation of the droplets. These oxides transfers to the surface of the weld pool at the weld toe, where they contributed to the formation of the cold laps.
NguyenTC, WeckmanDC, JohnsonDA, KerrHW: ‘The humping phenomenon during high speed gas metal arc welding’, Sci. Technol. Weld. Join., 2005, 10, (4), 447–459.
2.
GuoN, LinSB, ZhangL, YangC L.: ‘Metal transfer characteristics of rotating arc narrow gap horizontal GMAW’, Sci. Technol. Weld. Join., 2009, 14, (8), 760–764.
3.
TerasakiH, SimpsonSW: ‘Modelling of the GMAW system in free flight and short circuiting transfer’, Sci. Technol. Weld. Join., 2005, 10, (1), 120–124.
4.
OgunbiyiB, NorrishJ: ‘Monitoring indices for metal transfer in the GMAW process’, Sci. Technol. Weld. Join., 1997, 2, (1), 33–35.
5.
DeA, JantreJ, GhoshPK: ‘Prediction of weld quality in pulsed current GMAW process using artificial neural network’, Sci. Technol. Weld. Join., 2004, 9, (3), 253–259.
6.
EraT, UeyamaT, HirataY: ‘Spatter reduction in gas metal arc welding of stainless steel sheets using controlled bridge transfer process’, Sci. Technol. Weld. Join., 2009, 14, (8), 708–716.
NakamuraT, HiraokaK: ‘Ultranarrow GMAW process with newly developed wire melting control system’, Sci. Technol. Weld. Join., 2001, 6, (6), 355–362.
9.
NguyenTC, WeckmanDC, JohnsonDA: ‘Predicting onset of high speed gas metal arc weld bead defects using dimensional analysis techniques’, Sci. Technol. Weld. Join., 2007, 12, (7), 634–648.
10.
SinghPJ, AcharDRG, GuhaB, NordbergH: ‘Influence of weld geometry and process on fatigue crack growth characteristics of AISI 304L cruciform joints containing lack of penetration defects’, Sci. Technol. Weld. Join., 2002, 7, (5), 306–312.
11.
SamuelssonJ: ‘Cold laps and weld quality acceptance limits’, in‘Design and analysis of welded high strength steel structures’, 151–161; 2002, Stockholm, EMAS.
12.
MartinezLL, KorsgrenP: ‘Characterization of initial defect distribution and weld geometry in welded fatigue test specimens’, in‘Fatigue under spectrum loading and in corrosive environments’, 3–21; 1993, Lyngby, EMAS.
13.
LundinM, MartinezLL, HedegårdJ, WemanK: ‘High productive MAG welding – fatigue properties of weldments’, in‘Welded high-strength steel structures’, 33–47; 1997, Stockholm, EMAS.
14.
WemanK, LundinM, HedegårdJ: ‘High productive MAG welding of vehicle components’, in‘Welded high-strength steel structures’, 49–57; 1997, Stockholm, EMAS.
15.
BarsoumZ, JonssonB: ‘Fatigue assessment and LEFM analysis of cruciform joints fabricated with different welding processes’, Weld. World, 2008, 52, 93–105.
16.
HedegårdJ, MartinezLL, MoradashkaftiN, TrogenH: ‘The influence of welding parameters on the size and distribution of weld defects for various weld methods’, Proc. VTT Symp. 156: fatigue design 1995, 287–297; 1995, Helsinki, VTT Offset print Espoo.
17.
Farajian-SohiM, JärvstråtN, ThuvanderM: ‘Effect of welding parameters on formation of toe imperfections in tandem gas metal arc welding, Proc. 7th Int. Conf. on ‘Trends in welding research’, Pine Mountain, GA, USA, May 2005, ASM, 653–658.
18.
MartinezLL, BlomAF, SamuelssonJ: ‘Weld defects before and after post weld treatment for MAG and high-productivity MAG welding’, in‘Welded high-strength steel structures’, 391–408; 1997, Stockholm, EMAS.
19.
Farajian-SohiM, JärvstråtN: ‘A fractographical investigation of weld toe imperfections in tandem gas metal arc welding’, Steel Res. Int., 2006, 77, (12), 889–895.
20.
LiP, NylénP, MarkocsanN, KlementU: ‘Characterization of cold lap defects in tandem arc MAG welding’, Proc. 63rd Annual Assembly and Int. Conf. IIW, Istanbul, Turkey, July 2010, GEV, AWST-10/116.
21.
BlaisC, L'EspéranceG, EvansGM: ‘Characterisation of inclusions found in C–Mn steel welds containing titanium’, Sci. Technol. Weld. Join., 1999, 4, (3), 143–150.
PowellGLF, LloydPG, BeeJV: ‘Heterogeneity of coarsened oxide inclusions in C–Mn steel welds’, Sci. Technol. Weld. Join., 1998, 3, (1), 9–11.
24.
KosekiT, OhkitaS, YuriokaN: ‘Thermodynamic study of inclusion formation in low alloy steel weld metals’, Sci. Technol. Weld. Join., 1997, 2, (2), 65–69.
25.
GrongO, ChristensenN: ‘Factors controlling MIG weld metal chemistry’, Scand. J. Metall., 1983, 12, 155–165.
26.
GrongO, SiewertTA, MartinsGP, OlsonDL: ‘A model for the silicon-manganese deoxidation of steel weld metals’, Metall. Trans. A, 1986, 17A, 1797–1807.
27.
TurkdoganET: ‘Deoxidation of steel’, Chemical Metallurgy of Iron and Steel, Sheffield, UK, 1973, The Iron and Steel Institution, 153–170.
28.
LiD, LuS, DongW, LiD, LiY: ‘Study of the law between the weld pool shape variations with the welding parameters under two TIG processes’, J. Mater. Process. Technol., 2012, 212, (1), 128–136.
29.
LuS, FujiiH, NogiK: ‘Marangoni convection and weld shape variations in Ar–O2 and Ar–CO2 shielded GTA welding’, Mater. Sci. Eng. A, 2004, A380, (1–2), 290–297.
30.
ZhaoCX, KwakernaakC, PanY, RichardsonIM, SaldiZ, KenjeresS, KleijnCR: ‘The effect of oxygen on transitional Marangoni flow in laser spot welding’, Acta Mater., 2010, 58, (19), 6345–6357.