Dissimilar friction stir welding between steels with different carbon contents was carried out by placing the parent materials at two different fixed locations: the advancing side (AS) and the retreating side (RS). The phase transformation and the depth and width of the weld were affected by the fixed location. A smaller weld nugget was formed, and more martensite transformation occurred when the stronger SK5 steel was fixed at AS, compared to that at RS. This variation was attributed to the difference of temperature and materials flow between AS and RS.
ThomasW. M., NicholasE. D., NeedhamJ. C., MurchM. G., Temple-SmithP. and DawesC. J.: GB patent application no. 9,125,978·8, December 1991; US patent no. 5,460,317, 1995.
2.
LeeW. B., YeonY. M., and JungS. B.: ‘The joint properties of dissimilar formed Al alloys by friction stir welding according to the fixed location of materials’, Scripta Mater, 2003, 49, (5), 423–428
3.
LeeW. B. and JungS. B.: ‘The joint properties of copper by friction stir welding’, Mater Lett, 2004, 58, (6), 1041–1046.
4.
LeeW. B., BiallasG., SchmueckerM. and JungS. B.: ‘Joint properties and Interface Analysis of Friction Stir Welded Dissimilar Materials between Austenite Stainless Steel and 6013 Al Alloy’, JKWJS, 2005, 23, (5), 62–69.
5.
CavaliereP., De SantisA., PanellaF., and SquillaceA.: ‘Effect of welding parameters on mechanical and microstructural properties of dissimilar AA6082-AA2024 joints produced by friction stir welding’, Mater Design, 2009, 30, (3), 609–616.
6.
YanJ. and ReynoldsA. P.: ‘Effect of initial base metal temper on mechanical properties in AA7050 friction stir welds’, Sci Technol Weld Joi, 2009, 14, (4), 282–287.
7.
FujiiH., CuiL., TsujiN., MaedaM., NakataK. and NogiK.: ‘Friction stir welding of carbon steels’, Mater. Sci. Eng. A, Struct., 2006, A429, (1–2), 50–57.
8.
WeinbergerT., EnzingerN. and CerjakH.: ‘Microstructural and mechanical characterisation of friction stir welded 15-5PH steel’, Sci. Technol. Weld. Join., 2009, 14, (3), 210–215.
9.
CuiL., FujiiH., TsujiN. and NogiK.: ‘Friction stir welding of a high carbon steel’, Scr. Mater., 2007, 56, (7), 637–640.
10.
ChungY. D., FujiiH., UejiR. and NogiK.: ‘Friction stir welding of hypereutectoid steel (SK5) below eutectoid temperature’, Sci. Technol. Weld. Join., 2009, 14, (3), 233–238.
11.
SatoY. S., YamanoiH., KokawaH. and FuruharaT.: ‘Microstructural evolution of ultrahigh carbon steel during friction stir welding’, Scr. Mater., 2007, 57, (6), 557–560.
12.
SchmidtH. and HattelJ.: ‘Modelling heat flow around tool probe in friction stir welding’, Sci. Technol. Weld. Join., 2005, 10, (2), 176–186.
13.
GuerraM., SchmidtC., McClureJ. C., MurrL. E. and NunesA. C.: ‘Flow patterns during friction stir welding’, Mater. Charact., 2002, 49, (2), 95–101.
14.
SeidelT. U. and ReynoldsA. P.: ‘Visualization of the material flow in AA2195 friction-stir welds using a marker insert technique’, Metall. Mater. Trans. A, 2001, 32A, (11), 2879–2884.
15.
ChoJ. H., BoyceD. E. and DawsonP. R.: ‘Modeling strain hardening and texture evolution in friction stir welding of stainless steel’, Mater. Sci. Eng. A, Struct., 2005, A398, (1–2), 146–163
16.
GaleW. F. and TotemeierT. C.: ‘Smithells metals reference book’, 8th edn, 14-30-14-37; 2004, Oxford, Elsevier.