Al alloy sheet was friction stir spot welded (FSSW) to galvanised steel sheet by a scroll grooved tool without probe. Tensile and fatigue tests had been conducted using tensile shear specimens, and the results were discussed in comparison with Al/steel dissimilar FSSW joint, in which steel sheet was not galvanised. Energy dispersive X-ray analyses revealed that Zn coating was melted or softened and circumferentially resolidified around the nugget. Intermetallic compound between Al and Fe was formed along the interface resulting in the joining of Al to steel. Tensile shear strength of Al/galvanised steel weld was lower than that of Al/steel one without galvanising. However, Al/galvanised steel welds exhibited higher fatigue strengths. Finite element method analyses around the nugget revealed that circumferentially resolidified Zn brought about the stress relaxation at the edge of the nugget, resulting in the better fatigue performance of Al/galvanised steel welds.
OikawaH., OhmiyaS., YoshimuraT. and SaitohT.: ‘Resistance spot welding of steel and aluminium sheet using insert metal sheet’, Sci. Technol. Weld. Joining, 1999, 4-2, 80–88.
2.
LiyanageT., KilbourneJ., GerlichA. P. and NorthT. H.: ‘Joint formation in dissimilar Al alloy/steel and Mg alloy/steel friction stir spot welds’, Sci. Technol. Weld. Joining, 2009, 14-6, 500–508.
3.
LeeC. Y., ChoiD. H., YeonY. M. and JungS. B.: ‘Dissimilar friction stir spot welding of low carbon steel and Al-Mg alloy by formation of IMCs’, Sci. Technol. Weld. Joining, 2009, 14-3, 216–220.
4.
da SilvaA. A. M., AldanondoE., AlvarezP., ArrutiE. and EcheverríaA.: ‘Friction stir spot welding of AA 1050 Al alloy and hot stamped boron steel (22MnB5)’, Sci. Technol. Weld. Joining, 2010, 15-8, 682–687.
5.
BozziS., Helbert-EtterA. L., BaudinT., CriquiB. and KerbiguetJ. G.: ‘Intermetallic compounds in Al 6016/IF-steel friction stir spot welds’, Mater. Sci. Eng. A, 2010, A527, 4505–4509.
6.
UematsuY., KakiuchiT., TozakiY. and KojinH.: ‘Comparative study of fatigue behaviour in dissimilar Al alloy/steel and Mg alloy/steel friction stir spot welds fabricated by scroll grooved tool without probe’, Sci. Technol. Weld. Joining, 2012, 17-5, 348–356.
7.
MovahediM., KokabiA. H., Seyed ReihaniS. M. and NajafiH.: ‘Effect of tool travel and rotation speeds on weld zone defects and joint strength of aluminium steel lap joints made by friction stir welding’, Sci. Technol. Weld. Joining, 2012, 17-2, 162–167.
8.
MovahediM., KokabiA. H. and Seyed ReihaniS. M.: ‘Investigation on friction stir lap welding of aluminium to aluminium clad steel sheets’, Sci. Technol. Weld. Joining, 2012, 17-5, 231–236.
9.
KainumaR., SasakiT., OhnumaI. and IshidaK.: ‘Microstructures and concentration profiles formed between solid Fe and liquid Zn–0.2wt%Al alloy at 723K’, Tetsu-to-Hagane, 2009, 95-4, 355–360.
10.
GendoT., NishiguchiK., AsakawaM. and TaniokaS.: ‘Spot friction welding of aluminum to steel’, SAE Tech. Pap., 2007, 2007-01-1703.
11.
MiyagawaK., TsubakiM., YasuiT. and FukumotoM.: ‘Spot welding between aluminium alloy and Zn-coated steel by friction stirring’, Weld. Int., 2009, 23-9, 648–653.
12.
FengK., WatanabeM. and KumaiS.: ‘Microstructure and joint strength of friction stir spot welded 6022 aluminum alloy sheets and plated steel sheets’, Mater. Trans., 2011, 52-7, 1418–1425.
13.
DasH., ChoshR. N. and PalT. K.: ‘Study on the formation and characterization of the intermetallics in friction stir welding of aluminum alloy to coated steel sheet lap joint’, Metal. Mater. Trans. A, 2014, 45A, 5098–5106.
14.
UematsuY., TokajiK., TozakiY., NakashimaY. and ShimizuT.: ‘Fatigue behaviour of dissimilar friction stir spot welds between A6061-T6 and low carbon steel sheets welded by a scroll grooved tool without probe’, Fatigue Fract. Eng. Mater. Struct., 2011, 34-8, 581–591.
15.
TozakiY., UematsuY. and TokajiK.: ‘A newly developed tool without probe for friction stir spot welding and its performance’, J. Mater. Process. Technol., 2010, 210, 844–851.
16.
SatoY. S., KokawaH., EnomotoM. and JoganA.: ‘Microstructural evolution of 6063 aluminum during friction stir welding’, Metall. Mater. Trans. A, 1999, 30A, 2429–2439.
17.
UematsuY. and TokajiK.: ‘Comparison of fatigue behaviour between resistance spot and friction stir spot welded aluminium alloy sheets’, Sci. Technol. Weld. Joining, 2009, 14-1, 62–71.
18.
DaneshpourS., KokabiA. H., EkramiA. A. and MotarjemiA. K.: ‘Crack initiation and kinking behaviours of spot welded coach peel specimens under cyclic loading’, Sci. Technol. Weld. Joining, 2007, 12-8, 696–702.
19.
YangY. P., BabuS. S., OrthF. and PetersonW.: ‘Integrated computational model to predict mechanical behaviour of spot weld’, Sci. Technol. Weld. Joining, 2008, 13-3, 232–239.
20.
TanegashimaR., AkebonoH., KatoM. and SugetaA.: ‘3-Dimensional observation of the interior fracture mechanism and establishment of cumulative fatigue damage evaluation on spot welded joints using 590 MPa-class steel’, Int. J. Fatigue, 2013, 51, 121–131.