In this study, films from polyethylene and coated calcium carbonate blends were generated and the effects of calcium carbonate type, calcium carbonate loading and stretching temperature were investigated for roughness, morphology, crystallinity, pore size distribution, water pressure resistance and water vapor permeability of the films. The results showed that both breathability and waterproofness properties were only achieved with calcium carbonate possessing small particles (CC2 type) at both 25 and 50℃. Stretching at 80℃ led to ruptures in the films independent of calcium carbonate and loading amount employed. Increasing the calcium carbonate level provided better breathability performance without affecting the waterproofness considerably.
Johnson L and Schultze D. Breathable TPE films for medical applications. In: NIIR Board of Consultants and Engineers (ed.) The Complete Book on Medical Plastics. Delhi, India: Asia Pacific Business Press Inc., 2000.
2.
SadeghiFAjjiACarreauPJ. Study of polypropylene morphology obtained from blown and cast film processes: Initial morphology requirements for making porous membrane by stretching. J Plast Film Sheet2005; 21: 199–216.
3.
ChandavasuCXanthosMSirkarKK. Preparation of microporous films from immiscible blends via melt processing. J Plast Film Sheet2000; 16: 288–300.
4.
ChangbinCCaihongLQiC. Influence of Annealing time on the structure and properties of high-density polyethylene microporous membrane. J Plast Film Sheet2015; 31: 78–95.
5.
MorierasG. Baby boom market for fillers – GCC in microporous films. Ind Min2001; 6: 29–33.
6.
Ansari D, Calhoun A and Merriman P. The role of calcium carbonate in microporous film applications. In: Intertech’s functional fillers and additives proceedings, San Antonio, TX, September 2001.
7.
FTTS-FA-005. Test method of specified requirements of water-vapor permeable and liquid-water impermeable textiles. Committee for Conformity Assessment of Accreditation and Certification on Functional and Technical Textiles, www.ftts.org.tw/images/fa005E.pdf (2005, accessed 9 July 2015).
8.
WuPJonesGShelleyC. Novel microporous films and their composites. J Eng Fibers Fabr2007; 2: 49–59.
9.
QaissASaidiHFassi-FehriO. Porosity formation by biaxial stretching in polyolefin films filled with calcium carbonate particles. J Appl Polym Sci2012; 123: 3425–3436.
10.
NagoSMizutaniY. Preparation of microporous polypropylene sheets containing CaCO3 filler: Effect of draft ratio. J Appl Polym Sci1996; 61: 31–35.
11.
NagoSMizutaniY. Microporous polypropylene sheets containing CaCO3 filler: Effects of stretching ratio and removing CaCO3 filler, Y. J Appl Polym Sci1998; 68: 1543–1553.
HaleWRCrawfordEDDohrerKK. Linear low density polyethylene resins for breathable microporous films. Int Nonwovens J2002; 11: 34–40.
14.
Grondin P, Kamnikar P, Erdos V, et al. Breathable nonwoven/film laminate. US 20020132547 A1, USA, 2002.
15.
Carroll N, Lim H, Ostapchenko G, et al. Breathable composite sheet structure and absorbent articles utilizing same. US 20040142621 A1, USA, 2004.
16.
Anderson G and Gelotte S. Microporous composite sheet material. US 20040029469 A1, USA, 2004.
17.
Becke GS, Carmody DJ and Dobosy MJ. Microporous breathable film with internal barrier layer or layers. US Patent 0131676A1, USA, 2008.
18.
Afshari M. Vapor permeable, substantially water impermeable multilayer article, WO 2012177996 A3, USA, 2012.
19.
Burleigh MB. Waterproof, moisture-vapor permeable sheet material and method of making the same. US 4613544 A, USA, 1986.
20.
Calhoun AA, Shurling DS, Mobley GR, et al. Particulate carbonates and their preparation and use in breathable film. US Patent 6,682,775B2, USA, 2004.
21.
Gutierrez CA and Paynter CD. Breathable film. WO Patent 2003050167A1, Great Britain, 2003.
22.
Bonelli G, Cimini C and Veglio P. Breathable microporous film. EP Patent 0979838A1, USA, 2000.
23.
Antoon MK and Hill DJ. Breathable microporous film and methods for making it. US Patent 5011698A, USA, 1991.
24.
Antoon MK and Hill DJ. Breathable microporous film. US Patent 5008296A, USA, 1991.
25.
ÖzenİŞimşekS. Vital importance of moisture level in all stages of processing from calcium carbonate coating through polyethylene/calcium carbonate compounding to film generation. Powder Technol2015; 270: 320–328.
Özen İ and Şimşek Ş. Changing breathability of polyethylene composite films with different porous structures depending on stretching processes. Adv Polym Tech 2015 [Accepted for publication].
28.
TS 7128 EN ISO 5084. Textiles – determination of thickness of textiles and textile products, 1998.
29.
TS 251. Determination of mass per unit length and mass per unit area of woven fabrics, 2008.
30.
ASTM E 96. Standard test methods for water vapor transmission of materials, 2014.
31.
AATCC 127. Water resistance: hydrostatic pressure test, 1989.
32.
ASTM F316-03. Standard test methods for pore size characteristics of membrane filters by bubble point and mean flow pore test, 2011.
Aydın Madencilik AŞ. AY103 technical datasheet, Bursa, Turkey, 2012.
35.
MolefiJALuytASKrupaI. Comparison of the influence of Cu micro- and nano-particles on the thermal properties of polyethylene/Cu composites. Exp Polym Lett2009; 3: 639–649.
36.
PukánszkyBVanesMMaurerFHJ. Micromechanical deformations in particulate filled thermoplastics: Volume strain measurements. J Mater Sci1994; 29: 2350–2358.
37.
Fung W. Coated and laminated textiles. 1st ed. Cambridge: Woodhead Publishing Ltd and CRC Press LLC, 2002, pp.149–249.
38.
HaleWRDohrerKTantM. A diffusion model for water vapor transmission through microporous polyethylene/caco3 films. Coll and Surf A: Physicochem Eng Asp2001; 187–188: 483–491.