Effect of Cold Plasma Treatment on Macromolecular Structure,Thermal and Mechanical Behavior of Jute Fiber

Abstract

Cold Ar plasma treatment can be used to modify the structure of cellulosic fibers for a variety of applications. Jute fibers (Corchorus olitorius), a cellulosic fibers are treated with argon cold plasma for 5, 10, and 15 minutes. The above samples are characterized by small angle X-ray scattering (SAXS), X-ray diffraction (XRD), differential scanning calorimetric (DSC), Fourier transform infra spectroscopy (FT-IR), scanning electron microscopy (SEM), and Instron1185. Results from SAXS and XRD confirmed the macromolecular and micro-structural changes after plasma treatment. This is caused due to the bombardment of high energetic ions on the fiber surfaces. Rough topography with the formation of the pit was clearly seen in SEM micrograph for plasma treated fiber, which resulted in the loss of mechanical strength as detected by Instron 1185 in the test for single fiber mechanical strength. It was also shown that the modulus and tenacity of the jute fibers were decreased after plasma treatment. FT-IR studies supported the surface chemistry changes after treatment DSC data demonstrated that the thermal degradation of hemicelluloses lowered to 270^°C from 290^°C and cellulose degradation temperature lowered to 351^°C from 365^°C after 15-min plasma treatment resulted in the thermal instability of fiber after cold plasma treatment.

Keywords

Cold plasma treatments Jute fibers Mechanical properties Thermal properties SAXS X-ray.

References

Nayak, P.L. (1999). Biodegradable Polymers: Opportunities and Challenges, Macromol. Chem. Phys. C, 39(3): 481-505.

Sabharwol, H.S. , Denes, F. , Nielsen, L. and Yuong, R.A. (1993). Free-radical Formation in Jute from Argon Plasma Treatment, J. Agri. Food. Chem. , 41: 2202-2207.

Misra, S. and Mohanty, A. (2003). Studies on Mechanical Performance of Biofiber/Glass Reinforced Polyester Hybrid Composites, Compos. Sci. Tech. , 63: 1377-1386.

Bledzki, A.K. , Reihmane, S. and Gassan, J. (1996). Properties and Modification Methods for Vegetable Fibers for Natural Fiber Composites, J. Appl. Poly. Sci., 59: 1329-1336.

Bledzki, A.K. and Gassan, J. (1999). Composites Reinforced with Cellulose Based Fibers, J. Prog. Poly. Sci., 24: 221-274.

McCord, M.G. , Qiu, Y. , Zhang, C. , Hwang, Y.J. and Bures, B.L. (2002). The Effect of Atmospheric Pressure Helium + Oxygen Plasma Treatment on Surface and Mechanical Properties of Ultrahigh Modulus Polyethylene Fibers. J. Adhesion Sci. Tech., 16(4): 449-458.

Negulescy, I.I. , Despa, S. , Chen, J. , Collier, B.J. , Despa, M. , Denes, A. , Sarmadi, M. and Denes, F.S. (2000). Characterizing Polyester Fabrics Treated in Electrical Discharges of Radio-Frequency Plasma, Tex Res. Journal, 70: 1-7.

Roy, S.C. (1960). An X-Ray Study of Acetylated Jute, Text Res. J., 30: 450-456.

Porod, G. (1953). Die Rontgenkleinwinkelstreuung Von Dichtgepackten Kolloiden Systemen, Kolloid Z.Z. Polym., 133(1): 51.

10.

Ratho, T. and Sahu, N.C. (1970). Estimation of Molecular Weight and Other Parameters of Macromolecules in Jute by Low Angle X-ray Method, Kolloid Z.Z. Polym., 236: 43-48.

11.

Vonk, C.G. (1973). Investigation of Non-ideal Two-phase Polymer Structures by Small-angle X-ray Scattering, J. Appl. Cryst., 6: 81-86.

12.

Misra, T. , Patra, K.C. and Patel, T. (1984). Small-angle X-ray Study of Air-dried Elastoidin Using Three- and One-Dimensional Correlation Functions Obtained from Slit-smeared Intensity, Colloid Polym. Sci., 262: 611-616.

13.

Mering, J. and Tchoubar, D. (1965). Interpretation de la Diffusion Centrale Des Rayons X Par Les Systèmes Poreux. I, J. Appl. Cryst., 1: 153-165.

14.

Kortleve, G. and Vonk, C.G. (1968). X-ray Small Angle Scattering of Bulk Polyethylene, Kolloid Z.Z. Polym., 225: 124-131.

15.

Mittelbach, P. and Porod, G. (1965). Zur Rontgenkleinwinkelstreuung Kolloider Systeme, Kolloid Z.Z. Polym., 202: 40-49.

16.

Ruland, W. (1971). Small-angle Scattering of Two-phase Systems: Determination and Significance of Systematic Deviations from Porod's Law, J. Appl. Cryst, 4: 71-73.

17.

Cullity, B.D. (1978). Elements of X-ray Diffraction, p. 286, Addision Wesley Publising Company Inc., London.

18.

Segal, L. , Creely, J., Martin and Conrad, C.M. (1959). An Empirical Method for Estimating the Degree of Crystallinity of Native Cellulose Using the X-Ray Diffractometer, Tex. Res. Journal, 29: 786-794.

19.

Khan, C.W. , Chan, K. , Yuen, C.W.M. and Miao, M.H. (1998). Surface Properties of Low-Temperature Plasma Treated Wool Fabrics, Mater. Process. Technol., 83: 180.

20.

Tsenki, V. , Zafeiropoulos, N.E. , Simon, F. and Panayiotov, C. (2005). A Study of the Effect of Acetylation and Propionylation Surface Treatments on Natural Fibers, Composite: Part A, 36: 1110-1118.

21.

Xiao, B. , Sun, X.F. and Cang, S.R. (2001). Chemical, Structural, and Thermal Characterizations of Alkali-soluble Lignins and Hemicelluloses, and Cellulose from Maize Stems, Rye Straw, and Rice Straw, Polym. Degra. Stab., 74: 307-319.

22.

Sahoo, P.K. , Rana, P.R. , Sarkar, N. , Sahoo, A. and Swain, S.K. (2003). Characterization and Properties of Chemically Modified Corchorus Capsularis Jute Fiber Via Pulping and Grafting: Infrared, Thermogravimetric Analysis, Differential Scanning Calorimetry, Scanning Electron Microscopy, X-ray Diffraction, Biodegradation, and Superabsorbency, J. Polym. Sci.: Part A: Polym. Chem. , 41: 2696-2703.

23.

Zanini, S. , Riccardi, C. , Canevali, C. , Orlandi, M. , Zoia, L. and Tolppa, E.-L. (2005). Modifications of Lignocellulosic Fibers by Ar Plasma Treatments in Comparison with Biological Treatments, Surf. Coat. Tech., 200: 556-560.

24.

Yuan, X. , Jayaraman, K. and Bhattacharya, D. (2004). Effects of Plasma Treatment in Enhancing the Performance of Woodfiber-polypropylene Composites, Composite: Part A, 35: 1363-1374.

25.

Vonk, C.G. (1975). A General Computer Program for the Processing of Small-angle X-ray Scattering Data, J. Appl. Cryst., 8: 340-341.

26.

Prasad, N. , Patnaik, J. , Bohidar, N. and Mishra, T. (1998). Effect of Temperature on Nylon 6 Fibers at Different Denier Values and Study of Macromolecular Parameters by SAXS Technique, J. Appl. Poly. Sci., 76: 1735-1759.

27.

Misra, T. , Bisoyi, D.K. , Patel, T. , Patra, K.C. and Patel, A. (1988). Small Angle X-Ray Study of Cellulose in Cotton Using Correlation Functions, Poly. Journal, 20: 739-748.

28.

Khan, M.N. (1995). Small Angle x-ray Scattering Study of Sisal Fiber Using Correlation Functions, Ph.D. thesis, Sambalpur University , Orissa, India.

29.

Topping, J. (1972). Error of Observation and Their Treatment, 4th edn, Chapman and Hall, Science paper back ,

30.

Ray, D. , Sarkar, B.K. , Rana, A.K. and Bose, N.R. (2001). Effect of Alkali Treated Jute Fibers on Composite Properties, Bull. Mater. Sci., 24(2): 129-135.

31.

Cioffi, M.O.H. , Voorwald, H.J.C. , Hein, L.R.O. and Ambrosio , L. (2005). Effect of Cold Plasma Treatment on Mechanical Properties of PET/PMMA Composites , Composite Part A, 36: 615-623.

32.

Gutowski, W.S. , Wu, D.Y. and Li, S. (1993). Surface Silanization of Polyethylene for Enhanced Adhesion, J. Adhesion, 43: 139-155.

33.

Foerch, R. , Izawa, J. and Spears, J. (1991). A Comparative Study of the Effects of Remote Nitrogen Plasma, Remote Oxygen Plasma, and Corona Discharge Treatments on the Surfaceproperties of Polyethylene, J. Adhesion Sci. Techn., 5(7): 549-564.

34.

Felby, C. , Nielsen, B.R. , Olesen, P.O. and Skibsted, L.H. (1997). Identification and Quantification of Radical Reaction Intermediates by Electron Spin Resonance Spectrometry of Laccase-catalyzed Oxidation of Wood Fibers from Beech (Fagus sylvatica), Appl. Microbiol. Biotechnol., 48(4): 459-464.