Waste tire rubber (WTR) supplied by a truck tire retreader were processed in an intermeshing co-rotating twin-screw extruder (ICTSE). The extrusion process evaluated the efficiency of the thermomechanical recycling in the devulcanization of WTR rubbers. Samples were prepared by varying the process parameters, the particles sizes and thermoplastics, and the latter was used as devulcanization auxiliary agents. After extrusion, samples were subjected to solvent extraction to determine the soluble fraction (SF). Subsequently, these SF were characterized by Fourier transform infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The highest SF (29 wt%) was obtained with higher screw rotating speed and with smaller particle size. Higher SF indicated a higher degree of devulcanization. The FTIR and DSC analyses showed that natural rubber was the main rubber extracted from extruded samples. In addition, polypropylene was more effective than low-density polyethylene in the devulcanization process, promoting higher SF.
ImbernonLNorvezS. From landfilling to vitrimer chemistry in rubber life cycle. Eur Polym J2016; 82: 347–376.
4.
AdhikariBDeDMaitiS. Reclamation and recycling of waste rubber. Prog Polym Sci2000; 25(7): 909–948.
5.
IsayevAIYushanovSPChenJ. Ultrasonic devulcanization of rubber vulcanizates. I. Process model. J Appl Polym Sci1996; 59(5): 803–813.
6.
GarciaPSSousaFDBLimaJA. Devulcanization of ground tire rubber: physical and chemical changes after different microwave exposure times. Exp Polym Lett2015; 9(11): 1015–1026.
7.
FormelaKCysewskaMHaponiukJ. The influence of screw configuration and screw speed of co-rotating twin screw extruder on the properties of products obtained by thermomechanical reclaiming of ground tire rubber. Polimery2014; 59(2): 170–177.
8.
JalilvandARGhasemiIKarrabiM. A study of EPDM devulcanization in a co-rotating twin-screw extruder. Iran Polym J2007; 16(5): 327–335.
9.
EdwardsDWDanonBvan der GrypP. Quantifying and comparing the selectivity for crosslink scission in mechanical and mechanochemical devulcanization processes. J Appl Polym Sci2016; 133(37): 43932.
10.
BarbosaRNunesATAmbrósioJD. Devulcanization of natural rubber in composites with distinct crosslink densities by twin-screw extruder. Mater Res2017; 20(2): 77–83.
11.
SiHChenTZhangY. Effects of high shear stress on the devulcanization of ground tire rubber in a twin-screw extruder. J Appl Polym Sci2013; 128: 2307–2318.
12.
MatsushitaMMouriMOkamotoH. Rubber composition and method for producing the same. Patent 6,316,508, USA, 2001.
13.
ShiJJiangKRenD. Structure and performance of reclaimed rubber obtained by different methods. J Appl Polym Sci2013; 129(3): 999–1007.
14.
YazdaniHGhasemiIKarrabiM. Continuous devulcanization of waste tires by using a co-rotating twin screw extruder: effects of screw configuration, temperature profile, and devulcanization agent concentration. J Vinyl Addi Technol2013; 19(1): 65–72.
15.
FloryLH. Introduction to physical polymer science. New Jersey: John Wiley & Sons, 2006.
16.
NoraHMEbdonbJR. Ozonolysis of natural rubber in chloroform solution. Part 1. A study by GPC and FTIR spectroscopy. Polymer2000; 41: 2359–2365.
17.
WangaZFPengZLiSD. The impact of esterification on the properties of starch/natural rubber composite. Compos Sci Technol2009; 69: 1797–1803.
18.
LeHHAbhijeetSIlischS. The role of linked phospholipids in the rubber-filler interaction in carbon nanotube (CNT) filled natural rubber (NR) composites. Polymer2014; 55(18): 4738–4747.
19.
DattaSStocekRKuritkaI. Determination of compounding formulation of cured rubber by reverse engineering. Polym Eng Sci2015; 55(6): 1450–1458.
20.
MartínezJDPuyNMurilloR. Waste tire pyrolysis – A review. Renew Sustain Energy Rev2013; 23: 179–213.
21.
RamesanMT. Thermogravimetric analysis, flammability and oil resistance properties in natural rubber and dichlorocarbene modified styrene butadiene rubber blends. React Funct Polym2004; 59(3): 267–274.
22.
MartinsMAPessoaJDCGonçalvesPS. Thermal and mechanical properties of the açaí fiber/natural rubber composites. J Mater Sci2008; 43: 6531–6538.
23.
ColomXFaliqAFormelaK. FTIR spectroscopic and thermogravimetric characterization of ground tyre rubber devulcanized by microwave treatment. Polym Test2016; 52: 200–208.
24.
GarciaPSde SousaFDBde LimaJA. Devulcanization of ground tire rubber: physical and chemical changes after different microwave exposure times. Exp Polym Lett2015; 9(11): 1015–1026.
25.
FainleibAPiresRVLucasEF. Degradation of Non-vulcanized Natural Rubber – Renewable Resource for Fine Chemicals Used in Polymer Synthesis. Polím Ciência e Tecnol2013; 23: 441–450.
26.
AmbrósioJDLaroccaNMPessanLA. Influence of the process parameters of an intermeshing co-rotating twin screw extruder on the morphology and notched Izod impact strength of PBT/ABS/MGE blends. Polym Eng Sci2010; 50: 2382–2391.
27.
AgostiniDLSConstantinoCJLJobAE. Thermal degradation of both latex and latex cast films forming membranes. J Therm Anal Calorim2008; 91(3): 703–707.
28.
SilversteinRMWebsterFXKiemleDJ. Spectrometric identification of organic compounds. New Jersey: John Wiley and Sons, 2005.