Interfacial debonding detection in fiber-reinforced polymer rebar–reinforced concrete using electro-mechanical impedance technique

Abstract

For reinforced concrete structures, the use of fiber-reinforced polymer rebars to replace the steel reinforcement is a topic that is receiving increasing attention, especially where corrosion is a serious issue. However, fiber-reinforced polymer rebar–reinforced concrete always carries the risk of structural failure initiated from the debonding damage that might occur at the reinforcement–concrete interface. This study employed an electro-mechanical impedance–based structural health monitoring technique by applying lead–zirconate–titanate ceramic patches to detect the debonding damage of a carbon fiber–reinforced polymer rebar reinforced concrete. In the experimental study, a carbon fiber–reinforced polymer rebar reinforced concrete specimen was fabricated and it was subjected to a pullout test to initiate the debonding damage at the reinforcement–concrete interface. The impedance and admittance signatures were measured from an impedance analyzer according to the different debonding conditions between the reinforcement and the concrete. Statistical damage metrics, root-mean-square deviation and mean absolute percentage deviation, were used to quantify the changes in impedance signatures measured at the lead–zirconate–titanate patches due to debonding conditions. The results illustrated the capability of the electro-mechanical impedance–based structural health monitoring technique for detecting the debonding damage of fiber-reinforced polymer rebar–reinforced concrete structures.