Pulsed tungsten inert gas welding with full penetration was performed on 1.6 mm thick Ti–5Al–2.5Sn alloy sheet. Hole-drill strain measurement method was employed to measure the distribution of residual stresses across the weld line. Tensile tests were performed on the specimens sectioned in transverse direction of the welded sample. The evolved microstructure in the welded zone was investigated by metallography and X-ray diffraction. Transverse residual stresses of tensile nature were present at different depths below the surface and decreased the yield strength and ultimate tensile strength. However, this decrease was not dependent on the maximum value of transverse residual stress. Fracture location was found to be dependent on the micro-hardness profile and fracture took place in base metal where micro-hardness was the lowest. Furthermore, the presence of tensile residual stresses in the welded sample had no influence on the fractured surface morphology. Peak current and background current had a significant influence on the fusion zone width, heat-affected zone width, and fusion zone grain size.
NagaiIIshikawaIMizoguchiT, et al.Strength and fracture toughness of Ti-5AI-2.5Sn ELI alloy at cryogenic temperatures. Cryogenics1985; 26: 1–2. .
4.
Billinghurst EE Jr. Tensile properties of cast titanium alloys: titanium-6Al-4V ELI and titanium-5Al-2.5Sn ELI. NASA Tech Pap, http://ntrs.nasa.gov/search.jsp?R=19930000884 (1992, accessed 4 October 2016).
5.
ShortAB. Gas tungsten arc welding of α + β titanium alloys: a review. Mater Sci Technol2009; 25: 309–324.
6.
ZongRChenJWuC, et al.Influence of shielding gas on undercutting formation in gas metal arc welding. J Mater Process Technol2016; 234: 169–176.
7.
BalasubramanianTSBalakrishnanMBalasubramanianV, et al.Influence of welding processes on microstructure, tensile and impact properties of Ti-6Al-4V alloy joints. Trans Nonferrous Met Soc China2011; 21: 1253–1262.
8.
LiuHNakataKZhangJX, et al.Microstructural evolution of fusion zone in laser beam welds of pure titanium. Mater Charact2011; 65: 1–7.
9.
KarpagarajASivaNSankaranarayanasamyKA. Some studies on mechanical properties and microstructural characterization of automated TIG welding of thin commercially pure titanium sheets. Mater Sci Eng A2015; 640: 180–189.
10.
MehdiBBadjiRJiV, et al.Microstructure and residual stresses in Ti-6Al-4V alloy pulsed and unpulsed TIG welds. J Mater Process Technol2016; 231: 441–448.
11.
Amaya-VazquezMRSánchez-AmayaJMBoukhaZ, et al.Microstructure, microhardness and corrosion resistance of remelted TiG2 and Ti6Al4V by a high power diode laser. Corros Sci2012; 56: 36–48.
12.
OhJKimNJLeeS, et al.Correlation of fatigue properties and microstructure in investment cast Ti-6Al-4V welds. Mater Sci Eng A2003; 340: 232–242.
13.
PasangTAmayaJSTaoY, et al.Comparison of Ti-5Al-5V-5Mo-3Cr welds performed by laser beam, electron beam and gas tungsten arc welding. Procedia Eng2013; 63: 397–404.
14.
YunlianQJuDQuanH, et al.Electron beam welding, laser beam welding and gas tungsten arc welding of titanium sheet. Mater Sci Eng A2000; 280: 177–181.
15.
GaoXLZhangLJLiuJ, et al.A comparative study of pulsed Nd:YAG laser welding and TIG welding of thin Ti6Al4V titanium alloy plate. Mater Sci Eng A2013; 559: 14–21.
16.
BabuNKSundaraSGMythiliR, et al.Correlation of microstructure with mechanical properties of TIG weldments of Ti 6Al 4V made with and without current pulsing. Materials Characterization2007; 58: 581–587.
17.
BalasubramanianM. Developing mathematical models to predict tensile properties of pulsed current gas tungsten arc welded Ti-6Al-4V alloy. Mater Des2008; 29: 92–97.
18.
Sundaresan S, Ram GDJ and Reddy GM. Microstructural refinement of weld fusion zones in α-b titanium alloys using pulsed current welding. Materials Science and Engineering A 1999; 262: 88–100.
19.
DeADebRoyT. A perspective on residual stresses in welding. Sci Technol Weld Join2011; 16: 204–208.
20.
ZhangJXXueYGongSL. Residual welding stresses in laser beam and tungsten inert gas weldments of titanium alloy. Sci Technol Weld Join2005; 10: 643–646.
21.
ZhuangWZHalfordGR. Investigation of residual stress relaxation under cyclic load. Int J Fatigue2001; 23: 31–37.
22.
FerroPBertoFJamesMN. Asymptotic residual stresses in butt-welded joints under fatigue loading. Theor Appl Fract Mech2016; 83: 114–124.
23.
BalasubramanianTSBalasubramanianVManickamMAM. Fatigue crack growth behaviour of gas tungsten arc, electron beam and laser beam welded Ti-6Al-4V alloy. Mater Des2011; 32: 4509–4520.
24.
PauloRMFCarlonePValenteRaF, et al.Influence of friction stir welding effects on the compressive strength of aluminium alloy thin-walled structures. Key Eng Mater2014; 611–612: 184–190.
25.
ComminLDumontMRotinatR, et al.Influence of the microstructural changes and induced residual stresses on tensile properties of wrought magnesium alloy friction stir welds. Mater Sci Eng A2012; 551: 288–292.
26.
JunaidMBaigMNShamirM, et al.A comparative study of pulsed laser and pulsed TIG welding of Ti-5Al-2.5Sn titanium alloy sheet. J Mater Process Technol2017; 242: 24–38.
27.
GaoXZhangLLiuJ, et al.Comparison of Tensile Damage Evolution in Ti6A14V Joints between Laser Beam Welding and Gas Tungsten Arc Welding2014; 23: 4316–4327.
28.
ChamanfarAPasangTVenturaA, et al.Mechanical properties and microstructure of laser welded Ti-6Al-2Sn-4Zr-2Mo (Ti6242) titanium alloy. Mater Sci Eng A2016; 663: 213–224.
29.
CaoXÃJahaziM. Effect of welding speed on butt joint quality of Ti – 6Al – 4V alloy welded using a high-power Nd: YAG laser. Opt Lasers Eng2009; 47: 1231–1241.
30.
MaawadEGanWHofmannM, et al.Influence of crystallographic texture on the microstructure, tensile properties and residual stress state of laser-welded titanium joints. Mater Des2016; 101: 137–145.
31.
Senthil KumarTBalasubramanianVSanavullahMY. Influences of pulsed current tungsten inert gas welding parameters on the tensile properties of AA 6061 aluminium alloy. Mater Des2007; 28: 2080–2092.
32.
TchoumiTPeyrautFBolotR. Influence of the welding speed on the distortion of thin stainless steel plates - numerical and experimental investigations in the framework of the food industry machines. J Mater Process Technol2016; 229: 216–229.
33.
SubravelVPadmanabanGBalasubramanianV. Effect of welding speed on microstructural characteristics and tensile properties of GTA welded AZ31B magnesium alloy. Trans Nonferrous Met Soc China2014; 24: 2776–2784.
34.
ASTM. Determining residual stresses by the hole-drilling strain-gage method. Stand Test Method E837-13a 2008; i: 1–16.
35.
NasimKArifAFAl-NassarY, et al.Investigation of residual stress development in spiral welded pipe. J Mater Process Technol2015; 215: 225–238.
36.
KohandehghanARSerajzadehSKokabiAH. A study on residual stresses in gas tungsten arc welding of AA5251. Mater Manuf Process2010; 25: 1242–1250.
37.
BarrosoACanasJPiconR, et al.Prediction of welding residual stresses and displacements by simplified models: experimental validation. Mater Des2010; 31: 1338–1349.
38.
BaruahMBagS. Influence of heat input in microwelding of titanium alloy by micro plasma arc. J Mater Process Technol2016; 231: 100–112.
39.
BaruahMBagS. Influence of pulsation in thermo-mechanical analysis on laser micro-welding of Ti6Al4V alloy. Opt Laser Technol2017; 90: 40–51.
40.
LathabaiSJarvisBLBartonKJ. Comparison of keyhole and conventional gas tungsten arc welds in commercially pure titanium. Mater Sci Eng A2001; 299: 81–93.
41.
KarpagarajASiva shanmugamNSankaranarayanasamyK. Some studies on mechanical properties and microstructural characterization of automated TIG welding of thin commercially pure titanium sheets. Mater Sci Eng A2015; 640: 180–189.
42.
LiX. Effects of oxygen contamination in the argon shielding gas in laser welding of commercially pure titanium thin sheet. J Mater Sci2005; 40: 3437–3443.
43.
MalinovSShaWGuoZ, et al.Synchrotron X-ray diffraction study of the phase transformations in titanium alloys. Mater Charact2002; 48: 279–295.
44.
ElmerJWPalmerTABabuSS, et al.Phase transformation dynamics during welding of Ti-6Al-4V. J Appl Phys2004; 95: 8327–8337.
45.
AhmedTRackHJ. Phase transformations during cooling in α+β titanium alloys. Mater Sci Eng A1998; 243: 206–211.
46.
JunaidMKhanFNRahmanK, et al.Effect of laser welding process on the microstructure, mechanical properties and residual stresses in Ti-5Al-2.5Sn alloy. Opt Laser Technol2017; 97: 405–419.
47.
JunaidMKhanFNBakshN, et al.Study of microstructure, mechanical properties and residual stresses in full penetration electron beam welded Ti-5Al-2.5Sn alloy sheet. Mater Des2018; 139: 198–211.
48.
AkmanEDemirACanelT, et al.Laser welding of Ti6Al4V titanium alloys. J Mater Process Technol2009; 209: 3705–3713.
49.
Zain-ul-abdeinMNéliasDJullienJ-F, et al.Experimental investigation and finite element simulation of laser beam welding induced residual stresses and distortions in thin sheets of AA 6056-T4. Mater Sci Eng A2010; 527: 3025–3039.
50.
BhattiAABarsoumZMurakawaH, et al.Influence of thermo-mechanical material properties of different steel grades on welding residual stresses and angular distortion. Mater Des2015; 65: 878–889.
51.
ChuanLJianxunZJingN. Numerical and experimental analysis of residual stresses in full-penetration laser beam welding of Ti6Al4V alloy. Rare Met Mater Eng2009; 38: 1317–1320.
52.
MaNHuangHMurakawaH. Effect of jig constraint position and pitch on welding deformation. J Mater Process Technol2015; 221: 154–162.
53.
SundaresanSJanaki RamGDMadhusudhan ReddyG. Microstructural refinement of weld fusion zones in α–β titanium alloys using pulsed current welding. Mater Sci Eng A1999; 262: 88–100.
54.
MiGWeiYZhanX, et al.A coupled thermal and metallurgical model for welding simulation of Ti–6Al–4V alloy. J Mater Process Technol2014; 214: 2434–2443.