Comparison of microstructure,mechanical properties,and residual stresses in tungsten inert gas,laser,and electron beam welding of Ti–5Al

Abstract

Electron beam welding (EBW), pulsed Nd:YAG laser beam welding (P-LBW), and pulsed tungsten inert gas (P-TIG) welding of Ti–5Al–2.5Sn alloy were performed in order to prepare full penetration weldments. Owing to relatively high power density of EBW and LBW, the fusion zone width of EBW weldment was approximately equal to P-LBW weldment. The absence of shielding gas due to vacuum environment in EBW was beneficial to the joint quality (low oxide contents). However, less cooling rates were achieved compared to P-LBW as an increase in heat-affected zone width and partial α′ martensitic transformation in fusion zone were observed in EBW weldments. The microstructure in fusion zone in both the EBW and P-TIG weldments comprised of both acicular α and α′ martensite within the prior β grains. Hardness of the fusion zone in EBW was higher than the fusion zone of P-TIG but less than the fusion zone of P-LBW weldments due to the observed microstructural differences. Notch tensile specimen of P-LBW showed higher load capacity, ductility and absorbed energy as compared to P-TIG and EBW specimens due to the presence of high strength α′ martensite phase. Maximum sheet distortions and tensile residual stresses were observed in P-TIG weldments due to high overall heat input. The lowest residual stresses were found in P-LBW weldments, which were tensile in nature. This was owing to high power density and higher cooling rates in P-LBW operation. EBW weldment exhibited the highest compressive residual stresses due to which the service life of EBW weldment is expected to improve.

Keywords

Titanium alloys residual stress microstructure laser welding electron beam welding tungsten inert gas welding

Get full access to this article

View all access options for this article.

References

Kaur

Ribton

Balachandran

. Development of a novel approach for characterising electron beams and quality assurance of welds. J Manuf Process 2016; 24: 217–224.

Boyer

. An overview on the use of titanium in the aerospace industry. Mater Sci Eng A 1996; 213: 103–114.

Billinghurst EE, Jr. Tensile properties of cast titanium alloys: Titanium-6Al-4 V ELI and Titanium-5Al-2.5Sn ELI. NASA Technical Paper, http://ntrs.nasa.gov/search.jsp?R=19930000884 (1992, accessed 4 October 2016).

Tan

Chen

Thiruvarudchelvan

. High temperature deformation in Ti–5Al–2.5Sn alloy. J Mater Process Technol 2007; 192: 434–438.

Sun

. Tensile and low-cycle fatigue behavior of commercially pure titanium and Ti–5Al–2.5Sn alloy at 293 and 77 K. Mater Sci Eng A 2001; 316: 80–86.

Sun

Song

Zhu

et al.

Toughening of titanium alloys by twinning and martensite transformation. J Mater Sci 2002; 37: 2543–2547.

Shi

Lei

et al.

Effect of electron beam welding on the microstructures and mechanical properties of thick TC4-DT alloy. Mater Des 2012; 34: 509–515.

Short

. Gas tungsten arc welding of α + β titanium alloys: A review. Mater Sci Technol 2009; 25: 309–324.

Gao

X-L

Zhang

L-J

Liu

et al.

A comparative study of pulsed Nd:YAG laser welding and TIG welding of thin Ti6Al4V titanium alloy plate. Mater Sci Eng A 2013; 559: 14–21.

10.

Tang

. Study on the electron beam welding process of ZTC4 titanium alloy. Rare Metal Mater Eng 2014; 43: 786–790.

11.

Schultz

. Electron beam welding, Cambridge: Abington Publishing, 1993.

12.

Saxena

. Electron beam welding. Training materials for students 2014.

13.

Lei

et al.

Study on the mechanical heterogeneity of electron beam welded thick TC4-DT joints. Mater Sci Eng A 2012; 540: 135–141.

14.

Barreda

Santamar

Azpiroz

et al.

Electron beam welded high thickness Ti6Al4V plates using filler metal of similar and different composition to the base plate. Vacuum 2001; 62: 143–150.

15.

. Effects of oxygen contamination in the argon shielding gas in laser welding of commercially pure titanium thin sheet. J Mater Sci 2005; 40: 3437–3443.

16.

Wang

. Investigation on the microstructure and mechanical properties of Ti – 6Al – 4 V alloy joints with electron beam welding. Mater Des 2012; 36: 663–670.

17.

Ferro

Berto

James

. Asymptotic residual stresses in butt-welded joints under fatigue loading. Theoret Appl Fract Mech 2016; 83: 114–124.

18.

Paulo

RMF

Carlone

Valente RaF et al.

Influence of friction stir welding effects on the compressive strength of aluminium alloy thin-walled structures. Key Eng Mater 2014; 611–612: 184–190.

19.

Zhuang

Halford

. Investigation of residual stress relaxation under cyclic load. Int J Fatigue 2001; 23: 31–37.

20.

Zhang

Xue

Gong

. Residual welding stresses in laser beam and tungsten inert gas weldments of titanium alloy. Sci Technol Weld Join 2005; 10: 643–646.

21.

Pasang

Amaya

Tao

et al.

Comparison of Ti-5Al-5 V-5Mo-3Cr welds performed by laser beam, electron beam and gas tungsten arc welding. Procedia Eng 2013; 63: 397–404.

22.

Yunlian

Quan

et al.

Electron beam welding, laser beam welding and gas tungsten arc welding of titanium sheet. Mater Sci Eng A 2000; 280: 177–181.

23.

Kohandehghan

Serajzadeh

Kokabi

. A study on residual stresses in gas tungsten arc welding of AA5251. Mater Manuf Process 2010; 25: 1242–1250.

24.

Bhatti

Barsoum

Murakawa

et al.

Influence of thermo-mechanical material properties of different steel grades on welding residual stresses and angular distortion. Mater Des 2015; 65: 878–889.

25.

Huang

Murakawa

. Effect of jig constraint position and pitch on welding deformation. J Mater Process Technol 2015; 221: 154–162.

26.

Baruah

Bag

. Influence of heat input in microwelding of titanium alloy by micro plasma arc. J Mater Process Technol 2016; 231: 100–112.

27.

Baruah

Bag

. Microstructural influence on mechanical properties in plasma microwelding of Ti6Al4V alloy. J Mater Eng Perform 2016; 25: 4718–4728.

28.

Baruah

Bag

. Influence of pulsation in thermo-mechanical analysis on laser micro-welding of Ti6Al4V alloy. Optics Laser Technol 2017; 90: 40–51.

29.

Lathabai

Jarvis

Barton

. Comparison of keyhole and conventional gas tungsten arc welds in commercially pure titanium. Mater Sci Eng A 2001; 299: 81–93.

30.

Malinov

Sha

Guo

et al.

Synchrotron X-ray diffraction study of the phase transformations in titanium alloys. Mater Charact 2002; 48: 279–295.

31.

Karpagaraj

Siva shanmugam

Sankaranarayanasamy

. Some studies on mechanical properties and microstructural characterization of automated TIG welding of thin commercially pure titanium sheets. Mater Sci Eng A 2015; 640: 180–189.

32.

Ahmed

Rack

. Phase transformations during cooling in α + β titanium alloys. Mater Sci Eng A 1998; 243: 206–211.

33.

Akman

Demir

Canel

et al.

Laser welding of Ti6Al4V titanium alloys. J Mater Process Technol 2009; 209: 3705–3713.

34.

Bannour

Abderrazak

Mhiri

et al.

Effects of temperature-dependent material properties and shielding gas on molten pool formation during continuous laser welding of AZ91 magnesium alloy. Optics Laser Technol 2012; 44: 2459–2468.

35.

Liu

Nakata

Yamamoto

et al.

Mechanical properties and strengthening mechanisms in laser beam welds of pure titanium. Sci Technol Weld Join 2011; 16: 581–585.

36.

Zeng

Bieler

. Effects of working, heat treatment, and aging on microstructural evolution and crystallographic texture of α, α′, α″ and β phases in Ti–6Al–4 V wire. Mater Sci Eng A 2005; 392: 403–414.

37.

Lakshminarayanan

Balasubramanian

. An assessment of microstructure, hardness, tensile and impact strength of friction stir welded ferritic stainless steel joints. Mater Des 2010; 31: 4592–4600.

38.

Rossini

Dassisti

Benyounis

et al.

Methods of measuring residual stresses in components. Mater Des 2012; 35: 572–588.

Comparison of microstructure,mechanical properties,and residual stresses in tungsten inert gas,laser,and electron beam welding of Ti–5Al–2.5Sn titanium alloy

Abstract

Keywords

Get full access to this article

References