Wear tests were conducted using a ball-on-disc tester. In the experiment, 42CrMo4 steel disc of hardness 40 HRC was put in contact with 100Cr6 steel ball of 6.35 mm diameter. Hardness of ball was 60 HRC. Disc samples were created using vapor blasting and/or lapping techniques in order to obtain one-process and two-process isotropic surfaces. Dry and lubricated tests were carried out. During tests, the friction force was monitored as a function of time. Wear of discs and balls was measured after the test using white light interferometer. Under dry friction conditions, two batches of tests were performed. In order to decrease variation of the experimental results, during tests the wear debris was continuously removed from the disc surface. Tests under starved lubrication conditions were carried out using L-AN 46 oil. One drop of oil was supplied into the inlet side of the contact zone. It was shown that beneficial effects of two-process surfaces on tribological behavior of sliding pairs depended on the operating conditions.
JiangJArnellRD. On the running-in behaviour of diamond-like carbon coatings under the ball-on-disk contact geometry. Wear1998; 217: 190–199.
2.
Garcia-PrietoIFaulknerMDAlcockJR. The influence of specimen misalignment on wear in conforming pin on disk tests. Wear2004; 257: 157–166.
3.
GuicciardiSMelandriCLucchiniF. On data dispersion in pin-on-disk wear tests. Wear2002; 252: 1001–1006.
4.
AlmondEAGeeMG. Results from a U.K. inter-laboratory project on dry sliding wear. Wear1987; 120: 101–116.
5.
GodfreyD. Friction oscillations with a pin-on-disk tribometer. Tribol Int1995; 28: 119–126.
6.
WangLHeYZhouJ. Modelling of plowing and shear friction coefficients during high-temperature ball-on disc tests. Tribol Int2009; 42: 15–22.
7.
KucharskiSMrozZ. Identification of wear process in reciprocating ball-on-disc tests. Tribol Int2011; 311: 154–164.
8.
HegadekatteVKurzenhauserSHuberN. A predictive modelling scheme for wear in tribometers. Tribol Int2008; 42: 1020–1031.
9.
SedlacekMPodgornikBVizintinJ. Influence of surface preparation on roughness parameters, friction and wear. Wear2009; 266: 482–487.
10.
SedlacekMPodgornikBVizintinJ. Correlation between standard roughness parameters skewness and kurtosis an tribological behavior of contact surfaces. Tribol Int2012; 48: 102–112.
11.
WangSHuYZWangWZ. Transition of frictional states and surface roughness affects in lubricated contacts. Proc IMechE, Part J: J Engineering Tribology2008; 222: 407–414.
12.
WangSHuY-ZTanQ-C. Frictional behaviour of engineering surfaces in overall lubrication regimes of point contacts. Proc IMechE, Part J: J Engineering Tribology2011; 225: 1071–1080.
13.
WhitentonEPBlauPJ. A comparison of methods for determining wear volumes and surface parameters of spherically-tipped sliders. Wear1988; 124: 291–309.
14.
QuJTruhanJJ. An efficient method for accurately determining wear volumes of sliders with non-flat wear scars and compound curvatures. Wear2006; 261: 848–855.
15.
HaoQBianchiDKaestnerM. Feature-based characterization of worn surfaces for a sliding test. Tribol Int2010; 43: 1186–1192.
16.
KubiakKJLiskiewiczTWMathiaTG. Surface morphology in engineering applications: Influence of roughness on sliding and wear in fretting. Tribol Int2011; 44: 1427–1432.
17.
SantochiMVignaleM. A study on the functional properties of a honed surface. CIRP Ann1982; 31: 431–434.
18.
PawlusP. Effects of honed cylinder surface topography on the wear of piston-piston ring–cylinder assemblies under artificially increased dustiness condition. Tribol Int1993; 26: 49–56.
19.
LeefeSEBi-Gaussian representation of worn surface topography in elastic contact problems. In: DowsonDTaylorCMChildsTHC (eds). Tribology for energy conservation, Elsevier, 1998, pp. 281–290.
20.
CampbellJC. Cylinder bore surface roughness in internal combustion engines: Its appreciation and control. Wear1972; 19: 163–168.
21.
JengY. Impact of plateaued surfaces on tribological performance. Tribol Trans1996; 39/2: 354–361.
22.
GrabonWPawlusPSepJ. Tribological characteristics of one-process and two-process cylinder liner honed surfaces under reciprocating sliding conditions. Tribol Int2010; 43: 1882–1892.
23.
DzierwaAPawlusPZelaskoW. The study of the tribological properties of one-process and two-process textures after vapour blasting and lapping using pin-on-disc tests. Key Eng Mater2013; 527: 217–222.
24.
SedlacekKPodgornikBVizintinA. Planning surface texturing for reduced friction in lubricated sliding using surface roughness parameters skewness and kurtosis. Proc IMechE, Part J: J Engineering Tribology2012; 226: 661–667.
25.
KogutLKomvopoulosK. Analysis of the spherical indentation cycle for elastic-perfectly plastic solids. J Mater Res2004; 19: 2644–3653.
26.
MalburgMCRajaJ. Characterization of surface texture generated by plateau-honing process. CIRP Ann1993; 42: 637–640.
27.
BluntLJiangX. Advanced techniques for assessment surface topography, London and Sterling: Kogan Page Science, 2003.
28.
GreenwoodJAWilliamsonJBP. Contact of nominally flat surfaces. Proc R Soc (London)1966; A295: 300–319.
29.
PawlusP. Digitisation of surface topography measurement results. Measurement2007; 40: 672–686.
30.
PawlusPZelaskoW. Importance of sampling intervals in contact mechanics. Wear2012; 276: 121–129.
31.
JohnsonKL. Contact mechanics, Cambridge, UK: Cambridge University Press, 1985.