A micromechanics-based damage model for compressive behavior analysis of impacted composite laminates

Abstract

The compressive strength of composite laminates decreases seriously after being subjected to impact loading, which is an important item to be considered in the usage of composite material. In this paper, a micromechanics-based damage model is proposed to study the compressive behavior of impacted composite laminates. The micro stresses of fiber and matrix are calculated by stress amplification factors and then used to judge the failure mechanisms according to corresponding physical failure criteria. A progressive damage model based on different failure statuses of constituents is established to study the degradation of material properties. The bi-linear cohesive model is used in the research of delamination onset and propagation. The compressive behaviors of quasi-isotropic composite laminates subjected to different impact energies are investigated by this proposed method. Good agreements in terms of structure responses, failure mechanisms, and residual compressive strengths are obtained between numerical results and experimental data. The matrix cracking and delamination caused by impact loading are responsible for the initiation and propagation of buckling, which leads to the final collapse of entire laminates. Based on the numerical investigations of material parameters, the increment of mode II interlaminar fracture toughness is capable of improving the residual compressive strength significantly.