To reinforce the use of kenaf-derived cellulose as a compatible plastic filler, the cellulose (C) was thermally grafted with various concentrations (5, 8, and 11 wt.%) of hydrolysed 3-aminopropyltriethoxysilane (APS). The silane-grafted cellulose (SGC) were named as SGC5, SGC8 and SGC11. C (30 wt.%) and all of the SGC were respectively melt-compounded into poly(lactic acid) (PLA) before being hot-pressed into ∼0.3 mm sheets, which is the approximate thickness of clamshell packaging. The intermolecular interaction between SGC and PLA, which was absent with C, was confirmed via Fourier Transform Infrared Spectroscopy (FTIR). PLA filled with SGC5 or SGC8 showed significant improvement in thermal, tensile, physical, and barrier properties compared with the PLA/C composite. In contrast, adverse effects were observed with the PLA/SGC11 composite. 8 wt.% of APS was concluded as the critical concentration to be thermally-grafted onto the kenaf-derived cellulose as PLA/SGC8 composite showed optimum reinforcement in tensile strength (52 MPa), crystallizability (16% crystallinity), water resistance (5.3%) and dimensional stability (3.3%), and significantly shifted oxygen barrier from medium-low range to medium range (3.2 ×10−17 m3 m/m2 s Pa). Overall, the variation in the properties of these biocomposites may extend PLA's range in food packaging applications.
RobertsonG.L., Packaging of dairy products. In, RobertsonG.L. (ed.) Food Packaging, Principles and Practice, pp. 509–44. Taylor and Francis Group, US (2013).
MohantyA.K., MisraM., DrzalL.T., Sustainable bio-composites from renewable resources, Opportunities and challenges in the green materials world. J. Polym. Environ., 10, 19–26 (2002).
4.
TeeY.B., TalibR.A., AbdanK., ChinN.L., BashaR.K., YunosK.F.M., Thermally grafting aminosilane onto kenaf-derived cellulose and its influence on the thermal properties of poly (lactic acid) composites. Bioresources, 8, 4468–4483 (2013).
5.
AbdelmoulehM., BoufiS., ben SalahA., BelgacemM.N., GandiniA., Interaction of silane coupling agents with cellulose. Langmuir, 18, 3203–3208 (2002).
6.
WeigelC., KellnerR., FTIR-ATR-spectroscopic investigation of the silanization of germanium surfaces with 3-aminopropyltriethoxysilane. Fresenius’ Zeitschrift für Analytische Chemie, 335, 663–668 (1989).
7.
Brochier SalonM.C., GerbaudG., AbdelmoulehM., BruzzeseC., BoufiS., BelgacemM.N., Studies of interactions between silane coupling agents and cellulose fibers with liquid and solid-state NMR. Magn. Reson. Chem., 45, 473–483 (2007).
AyranciE., TuncS., A method for the measurement of the oxygen permeability and the development of edible films to reduce the rate of oxidative reactions in fresh foods. Food Chem., 80, 423–431 (2003).
10.
PamułaE., BłażewicM., PaluszkiewiczC., DobrzynP., FTIR study of degradation products of aliphatic polyesters–carbon fibres composites. J. Mol. Struct., 596, 69–75 (2001).
11.
Giita SilverajahV.S., IbrahimN.A., ZainuddinN., Wan YunusW.M.Z., HassanH.A., Mechanical, thermal and morphological properties of poly(lactic acid)/epoxidized palm olein blend. Molecules, 17, 11729–11747 (2012).
12.
TawakkalI.S.M.A., TalibR.A., KhalinaA., ChinN.L., IbrahimM.N., Optimisation of processing variables of kenaf derived cellulose reinforced polylactic acid. Asian J. Chem., 22, 6652–6662 (2010).
13.
WojciechowskaE., FabiaJ., SlusarczykC., GawlowskiA., WysockiW., GraczykT., Processing and supermolecular structure of new iPP/PLA fibres. Fibres & Textiles in Eastern Europe, 13, 126–8 (2005).
14.
GonçalvesC.M.B., CoutinhoJ.A.P., MarruchoI.M., Optical properties. In, AurasR., LimL.T., SelkeS.E.M., TsujiH. (eds.) Poly(lactic acid), Synthesis, Structures, Properties, Processing, and Applications (2nd ed.), pp. 97–112. John Wiley & Sons, Inc., Hoboken, New Jersey, US (2010).
15.
Al-MullaE.A.J., YunusW.M.Z.W., IbrahimN.A.B., RahmanM.Z.A., Properties of epoxidized palm oil plasticized polytlactic acid. J. Mater. Sci., 45, 1942–1946 (2010).
16.
YewG.H., Mohd YusofA.M., Mohd IshakZ.A., IshiakuU.S., Water absorption and enzymatic degradation of poly (lactic acid)/rice starch composites. Polym. Degrad. Stab., 90, 488–500 (2005).
17.
PangA.L., IsmailH., Tensile properties, water uptake, and thermal properties of polypropylene/waste pulverized tire/kenaf (PP/WPT/KNF) composites. BioResources, 8, 806–817 (2013).
18.
GhoshS.B., Bandyopadhyay-GhoshS., SaiM., Composites. In, AurasR., LimL.T., SelkeS.E.M., TsujiH. (eds.) Poly(lactic acid), Synthesis, Structures, Properties, Processing, and Applications (2nd ed.), pp. 293–310, John Wiley & Sons, Inc., Hoboken, New Jersey, US (2010).
19.
NishidaH., Thermal degradation. In, AurasR., LimL.T., SelkeS.E.M., TsujiH. (eds.) Poly(lactic acid), Synthesis, Structures, Properties, Processing, and Applications (2nd ed.), pp. 401–12, John Wiley & Sons, Inc., Hoboken, New Jersey, US (2010).
20.
LeeS.-Y., KangI.-A., DohG.-H., YoonH.-G., ParkB.-D., WuQ., Thermal and mechanical properties of wood flour/talc-filled polylactic acid composites, Effect of filler content and coupling treatment. J. Thermoplast. Compos. Mater., 21, 209–223 (2008).
21.
CaoX., MohamedA., GordonS.H., WillettJ.L., SessaDJ., DSC study of biodegradable poly(lactic acid) and poly(hydroxy ester ether) blends. Thermochim. Acta, 406, 115–127 (2003).
22.
FischerE.W., SterzelH.J., WegnerG., Investigation of the structure of solution grown crystals of lactide copolymers by means of chemical reactions. Kolloid-Zeitschrift und Zeitschrift für Polymere, 251, 980–990 (1973).
23.
AbdelmoulehM., BoufiS., BelgacemM.N., DufresneA., Short natural-fibre reinforced polyethylene and natural rubber composites, Effect of silane coupling agents and fibres loading. Compos. Sci. Technol., 67, 1627–1639 (2007).
24.
LeeB.H., KimH.S., LeeS., KimH.J., DorganJ.R., Bio-composites of kenaf fibers in polylactide, Role of improved interfacial adhesion in the carding process. Compos. Sci. Technol., 69, 2573–2579 (2009).
25.
PeiA., ZhouQ., BerglundL.A., Functionalized cellulose nanocrystals as biobased nucleation agents in poly(l-lactide) (PLLA) - Crystallization and mechanical property effects. Compos. Sci. Technol., 70, 815–821 (2010).
26.
WasanasukK., TashiroK., Crystal structure and disorder in Poly (l-lactic acid) δ form (α’ form) and the phase transition mechanism to the ordered α form. Polymer, 52, 6097–6109 (2011).
27.
El-ShekeilY.A., SapuanS.M., AbdanK., ZainudinE.S., Influence of fiber content on the mechanical and thermal properties of kenaf fiber reinforced thermoplastic polyurethane composites. Mater. Des., 40, 299–303 (2012).
28.
KhalidM., RatnamC.T., ChuahT.G., AliS., ChoongT.S., Comparative study of polypropylene composites reinforced with oil palm empty fruit bunch fiber and oil palm derived cellulose. Mater. Des., 29, 173–178 (2008).
29.
LuzS.M., Del TioJ., RochaJ.G.M., GonçalvesA.R., Del'ArcoA.P.Jr., Cellulose and cellulignin from sugarcane bagasse reinforced polypropylene composites, Effect of acetylation on mechanical and thermal properties. Composites Part A, 39, 1362–1369 (2008).
30.
TawakkalI.S.M.A., TalibR.A., AbdanK., ChinN.L., Mechanical and physical properties of kenaf-derived cellulose (KDC)-filled polylactic acid (PLA) composites. BioResources, 7, 1643–1655 (2012).
31.
WangY., QiR., XiongC., HuangM., Effects of coupling agent and interfacial modifiers on mechanical properties of poly (lactic acid) and wood flour biocomposites. Iran Polym. J., 20, 281–294 (2011).
XieY., HillC.A., XiaoZ., MilitzH., MaiC., Silane coupling agents used for natural fiber/polymer composites, A review. Composites Part A, 41(7), 806–819 (2010).
34.
ZhaoY., QiuJ., FengH., ZhangM., The interfacial modification of rice straw fiber reinforced poly (butylene succinate) composites, Effect of aminosilane with different alkoxy groups. J. Appl. Polym. Sci., 125, 3211–3220 (2012).
35.
HudaM.S., DrzalL.T., MohantyA.K., MisraM., Effect of fiber surface-treatments on the properties of laminated biocomposites from poly(lactic acid) (PLA) and kenaf fibers. Compos. Sci. Technol.68, 424–432(2008).
36.
WellsJ.K., BeaumontP.W., Crack-tip energy absorption processes in fibre composites. J. Mater. Sci., 20, 2735–2749 (1985).
37.
ThomasonJ.L., VlugM.A., Influence of fibre length and concentration on the properties of glass fibre-reinforced polypropylene, 1. Tensile and flexural modulus. Composites Part A, 27, 477–484 (1997).
38.
RampinelliG., Di LandroL., FujiiT., Characterization of biomaterials based on microfibrillated cellulose with different modifications. J. Reinf. Plast. Compos., 29, 1793–1803 (2010).
39.
TaibR.M., RamaradS., IshakZ.A.M., TodoM., Water absorption and tensile properties of kenaf bast fiber- plasticized poly (lactic acid) biocomposites. Proceeding Polym. Process. Soc.2–5 (2008).
40.
LuJ., AskelandP., DrzalL.T., Surface modification of microfibrillated cellulose for epoxy composite applications. Polymer, 49, 1285–1296 (2008).
41.
AlmenarE., AurasR., Permeation, sorption, and diffusion in poly(lactic acid. In, AurasR., LimL.T., SelkeS.E.M., TsujiH. (eds.) Poly(lactic acid), Synthesis, Structures, Properties, Processing, and Applications (2nd ed.), pp. 55–79, John Wiley & Sons, Inc., Hoboken, New Jersey, US (2010).
AbdellatiefA., WeltB.A., Comparison of new dynamic accumulation method for measuring oxygen transmission rate of packaging against the steady-state method described by ASTM D3985. Packag. Technol. Sci., 26, 281–288 (2012).
44.
LaxmeshwarS.S., VivekaS., J, M.K.D., NagarajaG.K., Preparation and properties of composite films from modified cellulose fibre-reinforced with PLA. Der Pharma Chemica, 4, 159–168 (2012).
45.
ShogrenR., Water vapor permeability of biodegradable polymers. J. Environ. Polym. Degrad., 5, 91–95 (1997).
46.
LiaoW.-H., HsiaoS.-T., WuY.-F., ZengS.-J., LiS.-M., WangY.-S., MaC.C.M., Effect of silane-functionalized TiO2 on the optical properties and moisture barrier of silicone resin nanocomposites. RSC Adv., 4, 38614–38622 (2014).