A homo- and three co-polycarbonates (PC-NBs) bearing pendant norbornenyl groups were synthesized via solution polycondensation of triphosgene with 4, 4'-(bicyclo (2.2.1) hept-5-en-2 yl methylene) bis (2-methoxyphenol) (BPA-NB) or various mol % compositions of BPA-NB and bisphenol-A, respectively. 1H-NMR spectroscopy confirmed the chemical structure and composition of PC-NBs. Inherent viscosity and number-average molecular weight (Mn) values of PC-NBs were in the range 0.44 – 0.64 dL g−1 and 21,800 – 34,100 g mol−1, respectively, indicating the formation of polymers of medium to reasonably high molecular weights. Tough, transparent, and flexible films of PC-NBs could be cast from chloroform solution. X-Ray diffraction studies indicated the amorphous nature of PC-NBs. Glass transition temperature (Tg) values, determined by DSC analysis, of PC-NBs were in the range 154 – 175°C and Tg values increased with the increase in mol % of BPA-NB. The post-polymerization modification of a representative PC-NB was demonstrated using 3,6-diphenyl-1,2,4,5-tetrazine via tetrazine-ene reaction.
WeiPBhatGADarensbourgDJ. Enabling new approaches: recent advances in processing aliphatic polycarbonate-based materials. Angew Chem Int Ed Engl2023; 62: e202307507.
5.
NelsonAMLongTE. A perspective on emerging polymer technologies for bisphenol-A replacement. Polym Int2012; 61: 1485–1491.
6.
LiguoriFMoreno-MarrodanCBarbaroP. Biomass-derived chemical substitutes for bisphenol A: recent advancements in catalytic synthesis. Chem Soc Rev2020; 49: 6329–6363.
7.
De HoeGXŞucuTShaverMP. Sustainability and polyesters: beyond metals and monomers to function and fate. Acc Chem Res2022; 55: 1514–1523.
8.
GandiniAMM LacerdaT. Monomers and macromolecular materials from renewable resources: state of the art and perspectives. Molecules2021; 27: 159.
9.
HarveyBGGuenthnerAJKoontzTA, et al.Sustainable hydrophobic thermosetting resins and polycarbonates from turpentine. Green Chem2016; 18: 2416–2423.
10.
HarveyBGGuenthnerAJMeylemansHA, et al.Renewable thermosetting resins and thermoplastics from vanillin. Green Chem2015; 17: 1249–1258.
11.
ChenQHuangWChenP, et al.Synthesis of lignin-derived bisphenols catalyzed by lignosulfonic acid in water for polycarbonate synthesis. ChemCatChem2015; 7: 1083–1089.
12.
FagnaniDETamiJLCopleyG, et al.100th anniversary of macromolecular science viewpoint: redefining sustainable polymers. ACS Macro Lett2021; 10: 41–53.
13.
SaxonDJLukeAMSajjadH, et al.Next-generation polymers: isosorbide as a renewable alternative. Prog Polym Sci2020; 101: 101196.
14.
ZhangXFevreMJonesGO, et al.Catalysis as an enabling science for sustainable polymers. Chem Rev2018; 118: 839–885.
15.
SchneidermanDKHillmyerMA. 50th anniversary perspective: there is a great future in sustainable polymers. Macromolecules2017; 50: 3733–3749.
16.
KoelewijnSFVan Den BoschSRendersT, et al.Sustainable bisphenols from renewable softwood lignin feedstock for polycarbonates and cyanate ester resins. Green Chem2017; 19: 2561–2570.
17.
TritaASOverLCPolliniJ, et al.Synthesis of potential bisphenol A substitutes by isomerising metathesis of renewable raw materials. Green Chem2017; 19: 3051–3060.
18.
MoriR. Replacing all petroleum-based chemical products with natural biomass-based chemical products: a tutorial review. RSC Sustain2023; 1: 179–212.
19.
IchakeABNaganeSSJadhavUA, et al. Synthesis and characterization of partially biobased aromatic (Co)polycarbonates bearing biphenylene units and pendant pentadecyl chains. Macromol Chem Phys2022; 223: 2100449.
20.
NaganeSSKuhireSSIchakeAB, et al. Synthesis, characterization and UV-crosslinking of aromatic (Co)polycarbonates bearing pendant azido groups. ChemistrySelect2022; 7: e202201020.
21.
NaganeSSMaherDMVermaS, et al.Pendant propargyloxy-functionalized aromatic (Co)polycarbonates: synthesis, thermal crosslinking and chemical modification. J Macromol Sci Part A Pure Appl Chem2022; 59: 752–763.
22.
FromelMPesterCW. Polycarbonate surface modification via aqueous SI-PET-RAFT. Macromolecules2022; 55: 4907–4915.
23.
IslamMMSeoDWJangHH, et al.Synthesis and characterization of branched bisphenol-A polycarbonates functionalized with siloxane. Macromol Res2011; 19: 1278–1286.
24.
LiZCaoWSunJ, et al.Synthesis and properties of benzocyclobutene-functionalized thermosetting polycarbonate. Chin J Org Chem2016; 36: 2442–2448.
25.
TalanikarAANaganeSSWadgaonkarPP, et al.Post-polymerization modifiable aromatic (Co)poly(ether sulfone)s possessing pendant norbornenyl groups based upon a new bisphenol. Eur Polym J2022; 176: 111431.
26.
TalanikarAANaganeSSWadgaonkarPP, et al.Norbornenyl-Pendant Aromatic (Co)poly(ether ether ketone)S. J Macromol Sci Part A Pure Appl Chem2023; 60: 790–800.
27.
BuscheSAPeplauSZuhseL, et al.Tetrazine-norbornene versus azide-norbornene ligation: evaluating the toolbox for polymer-polymer coupling. Polym Chem2023; 14: 2888–2892.
28.
NguyenKDQCrespo-RibadeneyraMPicotO, et al.Ultrafast photo-crosslinking of thiol-norbornene opaque silicone elastomer nanocomposites in air. ACS Appl Polym Mater2021; 3: 5373–5385.
29.
WilliamsRJBarkerIAOReillyRK, et al.Orthogonal modification of norbornene-functional degradable polymers. ACS Macro Lett2012; 1: 1285–1290.
30.
ChenJSoucekMDSimonsickWJ, et al.Synthesis and photopolymerization of norbornyl epoxidized linseed oil. Polymer2002; 43: 5379–5389.
31.
ColombHOTreckerDJOsterholtzFD. Radiation‐convertible polymers from norbornenyl derivatives. Crosslinking with ionizing radiation. J Appl Polym Sci1970; 14: 1659–1670.
32.
ArmaregoKNPerrinDD, Purification of laboratory chemicals. 4th ed.Oxford: Butterworth Heinemann, 1996.
33.
HanYZhangYLongX, et al. Synthesis and properties of bisphenol-Z polycarbonate via melt transesterification. J Appl Polym Sci2024; 141: e54770.
34.
TayBVan MeursMTanJ, et al.Imidazolium-catalyzed formation of bisphenol A polycarbonate with a reduced level of branching. Ind Eng Chem Res2021; 60: 17928–17941.
35.
KimWBJoshiUALeeJS. Making polycarbonates without employing phosgene: an overview on catalytic chemistry of intermediate and precursor syntheses for polycarbonate. Ind Eng Chem Res2004; 43: 1897–1914.
36.
AertsAKroonenCKampsJH, et al. High molar mass polycarbonate via dynamic solution transcarbonation using bis(methyl salicyl) carbonate, an activated carbonate. Macromol Chem Phys2021; 222: 2100186.
37.
KampsJHHoeksTKungE, et al.Activated carbonates: enabling the synthesis of differentiated polycarbonate resins via melt transcarbonation. Polym Chem2016; 7: 5294–5303.
38.
FukuokaSFukawaIAdachiT, et al.Industrialization and expansion of green sustainable chemical process: a review of non-phosgene polycarbonate from CO2. Org Process Res Dev2019; 23: 145–169.
39.
FukuokaSTojoMHachiyaH, et al.Green and sustainable chemistry in practice: development and industrialization of a novel process for polycarbonate production from CO 2 without using phosgene. Polym J2007; 39: 91–114.
40.
LiuYOkadaITsudaA. Flow photo-on-demand phosgenation reactions with chloroform. Org Process Res Dev2022; 26: 3336–3344.
41.
KricheldorfHRBöhmeSSchwarzG. Polycondensations of bisphenol-A with diphosgene or triphosgene in water-free organic solvents. Macromol Chem Phys2005; 206: 432–438.
42.
KricheldorfHRLübbersD. Polymers of carbonic acid, 1. Synthesis of thermotropic aromatic polycarbonates by means of bis(trichloromethyl) carbonate. Makromol Chem Rapid Commun1989; 10: 383–386.
43.
TsudaAOzawaNMuranakaR, et al.Photo-on-Demand in situ phosgenation reactions that cross three phases of a heterogeneous solution of chloroform and aqueous NaOH. ACS Omega2023; 8: 27802–27810.
44.
LawalSOWatanabeKUchinoR, et al.Gas-permeable carbon molecular sieve membranes fabricated from a norbornene-functionalized polyimide-polyhedral oligomeric silsesquioxane composite. Ind Eng Chem Res2023; 63: 1554–1565.
45.
KwartHKingK. The reverse diels-alder or retrodiene reaction. Chem Rev1968; 68: 415–447.
46.
GaniuMONepalBVan HoutenJP, et al.A decade review of triphosgene and its applications in organic reactions. Tetrahedron2020; 76: 131553.
47.
BoylesDAFilipovaTSBendlerJT, et al.Synthesis of high aspect ratio bisphenols and polycarbonates incorporating bisaryl units. Macromolecules2005; 38: 3622–3629.
48.
ZhangXZhangQWuY, et al.Polyaddition of azide-containing norbornene-based monomer through strain-promoted 1,3-dipolar cycloaddition reaction. Macromol Rapid Commun2016; 37: 1311–1317.
49.
FoxTG. Influence of diluent and of copolymer composition on the glass temperature of a poly-mer system. Bull Am Phys Soc1956; 1: 123.
50.
GalanNJFriedADCromerCE, et al.Exploring the influence of rigid carbocycles on terpenoid copolymer properties. J Polym Sci2023; 61: 1995–2001.
51.
HuangCCDuMXZhangBQ, et al.Glass transition temperatures of copolymers: molecular origins of deviation from the linear relation. Macromolecules2022; 55: 3189–3200.
52.
ChngMLXiaoYChungTS, et al.The effects of chemical structure on gas transport properties of poly(aryl ether ketone) random copolymers. Polymer2007; 48: 311–317.
53.
YehYCOuyangLHighleyCB, et al.Norbornene-modified poly(glycerol sebacate) as a photocurable and biodegradable elastomer. Polym Chem2017; 8: 5091–5099.
54.
García-AznarPEscorihuelaJ. Computational insights into the inverse electron-demand diels–alder reaction of norbornenes with 1,2,4,5-tetrazines: norbornene substituents’ effects on the reaction rate. Org Biomol Chem2022; 20: 6400–6412.
55.
HansellCFEspeelPStamenovićMM, et al.Additive-free clicking for polymer functionalization and coupling by tetrazine-norbornene chemistry. J Am Chem Soc2011; 133: 13828–13831.
56.
BarkerIAHallDJHansellCF, et al.Tetrazine-norbornene click reactions to functionalize degradable polymers derived from lactide. Macromol Rapid Commun2011; 32: 1362–1366.
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.