Effect of Hygrothermomechanical Aging on the Interlaminar Fracture Behavior of Woven Fabric Fiber/PEI Composite Materials

Abstract

This article addresses the experimental characterization of the mechanical properties of three types of woven fabric composites taking into account the effects of hygrothermal and hygrothermomechanical aging. Characterization was carried out using the mode I, double cantilever beam (DCB) and the mode II, end notched flexural (ENF) interlaminar fracture tests in order to determine the loss in crack propagation resistance. The materials used were two types of woven (2/2 Twill, 8-Harness Satin) glass fiber, and 8-Harness Satin carbon fiber. The matrix was polyetherimide (PEI). The critical values of the energy release rate in mode I and mode II were calculated using the corrected beam theory. The material reinforced with 8-Harness Satin glass fiber presented the best behavior in mode I and mode II. The decrease in fracture strength is more important in the material reinforced with carbon fiber.

Keywords

delamination modes glass fabric carbon fabric PEI hygrothermal hygrothermomechanical aging

References

Hull, D. and Clyne, T.W. (1987). An Introduction to Composite Materials, Cambridge Solid State Sciences Series, Great Britain .

Fernandez-Canteli, A. , Arguelles, A. , Vina, J. , Ramulu, M. and Kobayashi, A.S. (2002). Dynamic Fracture Toughness Measurements in Composites by Instrumental Charpy Testing: Influence of Aging , Composites Science and Technology, 62: 1315—1325 .

Scida, D. , Aboura, Z. and Benzeggagh, M.L. (2002). The Effect of Aging on the Damage Events in Woven-fiber Composite Materials under Different Loading Conditions , Composites Science and Technology, 62: 551—557 .

Vina, J. , García, E.A. , Arguelles, A. and Vina, I. (2000). The Effect of Moisture on the Tensile and Interlaminar Shear Strengths of Glass or Carbon Fiber Reinforced PEI , Journal of Materials Science Letters, 19: 579—581 .

Ashbee, K.H.G. and Wyatt, R.C. (1969). Water Damage in Glass Fiber-Resin Composites, In: Proc. R. Soc. London , A 312, pp. 553—564.

Chiou, P. and Bradley, W.L. (1993). The Effect of Sea Water Exposure on the Fatigue Edge Delamination Growth of a Carbon/Epoxy Composite , 9th ICCM, 5: 516—523 .

Selzer, R. and Friedrich, K. (1995). Influence of Water up take on Interlaminar Fracture Properties of Carbon Fiber Reinforced Polymer Composites , Journal of Materials Science, 30: 334—338 .

Selzer, R. and Friedrich, K. (1998). Mechanical Properties and Failure Behaviour of Carbon Fiber Reinforced Polymer Composites under the Influence of Moisture , Composites, 28A: 595—604 .

Liao, K. , Schultheisz, C.R. , Hunston, D.L. and Brinson, L.C. (1998). Long-term Durability of Fiber Reinforced Polymer — Matrix Composite Materials for Infrastructure Applications: A Review , Journal of Advanced Materials, 30(4): 3—40 .

10.

ASTM D 5528 , Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composite, Annual Book of ASTM Standards, 14.02, pp. 272—281.

11.

Bullions, T.A. , Mehta, R.H. , Taan, B. , McGrath, .E. and Kranbuehl, A.C. (1999). Mode I and Mode II Fracture Toughness of High-Performance 3000 g mole-1 Reactive Poly(etherimide)/Carbon Fiber Composites, Composites, 30A: 153—162.

12.

Naik, N.K. , Reddy, K.S. , Meduri, S. , Raju, N.B. , Prasad, P.D. , Azad, N.M. , Odge, P.A. and Reddy, B.C.K. (2002). Interlaminar Fracture Characterization for Plain Weave Fabric Composites , Journal of Materials Science, 37: 2983—2987 .

13.

O'Brien, T.K. and Martin, R.H. (1993). Round Robin Testing for Mode I Interlaminar Fracture Toughness of Composite Materials , Journal of Composite Technology and Research, 15(4): 269—281 .

14.

Davies, P. (1993). Protocols for Interlaminar Fracture Testing of Composites, European Structural Integrity Society Polymers & Composites Task Group, France.

15.

Davies, P. , Pomies, F. and Carlsson, L.A. (1996). Influence of Water Absorption on Transverse Tensile Properties and Shear Fracture Toughness of Glass/Polypropylene , Journal of Composite Materials, 30: 1004—1019 .