Flame Retardant Finishing of Cotton Fleece Fabric: Part III — The Combination of Maleic Acid and Sodium Hypophosphite

Abstract

Cotton fleece does not meet the federal flammability standard (16 CFR Part 1610: `Standard for the Flammability of Clothing Textiles') without chemical treatment. In this research, the chemical reactions of maleic acid (MA) on cotton in the presence of sodium hypophosphite (NaH₂PO₂) and the use of the combination of MA and NaH₂PO₂ as a flame retardant finishing system for cotton fleece are investigated. It has been found that MA esterifies cotton cellulose at relatively low temperatures in the presence of NaH₂PO₂ as catalyst, and that MA esterified to cotton is able to further react with NaH₂PO₂ at higher temperatures (≥150°C), which bonds phosphorus to the cotton cellulose. The reactions between MA and NaH₂PO₂ on cotton also lead to the cross-linking of cotton cellulose. The treatment using the combination of MA and NaH₂PO₂ is effective in reducing the flammability of cotton fleece from `Class III' to `Class I' (16CFR1610). This is a nonformaldehyde and low cost flame retardant finishing system for cotton fleece. The treated cotton fleece still maintains `Class I' flammability after 20 home laundering cycles.

Keywords

cotton flame retardant finishing fleece maleic acid sodium hypophosphite.

Get full access to this article

View all access options for this article.

References

16 CFR Part 1610 (2007). Code of Federal Regulations, Title 16, Chapter II-Consumer Product Safety Commission, Office of the Federal Register , Washington D.C. , pp. 603-620; 16 CFR Part 1610 (2007). Standard for the Flammability of Clothing textiles ; Proposed Rules, Federal Register, 72(38): 8844-8868.

Rearick, W.A. , Martin, W.B. and Wallace, M.L. (2002). Cotton Flame Retardant Developments-Update of Work on Raised Surface Apparel , 13th Annual BCC Conference on Flame Retardancy, BCC Communications, Stamford, Connecticut, pp. 251-263.

Rearick, W.A. , Wallace, M.L. and Martin, V.B. (2001). Raised Surface Apparel: Flammability Considerations , AATCC Conference ``Book of Paper'', AATCC, Research Triangle Park, North Carolina, pp. 114-121.

Weil, E.D. (1995). Flame Retardants, Phosphorus, In: Grayson, M. (ed.), Kirk-Other Encyclopedia of Chemical Technology, 4th edn, p. 976, Wiley, New York.

Weil, E.D. (1992). Phosphorus-Based Flame Retardants, In: Engel, R. (ed.), Handbook of Organophosphorus Chemistry, p. 683, Marcel Dekker, New York.

Welch, C.M. (2001). Formaldehyde-Free Durable Press Finishing, In: Pastore, C.M. and Kiekens, P. (eds), Surface Characteristics of Fibers & Textiles, pp. 1-32, Marcel Dekker, New York.

Blanchard, E.J. and Graves, E.E. (2002). Polycarboxylic Acids for Flame Resistant Cotton/Polyester Carpeting , Textile Research Journal, 71(1): 39-43.

Blanchard, E.J. and Graves, E.E. (2005). Improving Flame Resistance of Cotton/Polyester Fleece with Phosphorous Based Polycarboxylic Acids , AATCC Review, 5(5): 26-30.

Wu, W. and Yang, C.Q. (2004). Comparison of DMDHEU and Melamine-Formaldehyde As the Bonding Agents for A Hydroxyl-Functional Organophosphorus Flame Retarding Agent on Cotton , Journal of Fire Sciences, 22(2): 125-142.

10.

Yang, C.Q. , Wu, W. and Xu, Y. (2005). The Combination of A Hydroxyl-Functional Organophosphorus Oligomer and Melamine-Formaldehyde as A Flame Retarding System for Cotton , Fire and Materials, 29(2): 109-120.

11.

Wu, W. and Yang, C.Q. (2006). A Comparative Study of Different Organophosphorus Flame Retardant Agents for Cotton: Part I. The Covalent Bonding of the Flame Retardant Agent to Cotton , Polymer Degradation and Stability , 91(11): 2541-2548.

12.

Wu, W. and Yang, C.Q. (2007). A Comparative Study of Different Organophosphorus Flame Retardant Agents for Cotton: Part II . The Fabric Flammability and Physical Properties, Polymer Degradation and Stability, 92(3): 363-369.

13.

Yang, H. and Yang, C.Q. (2003). Nonformaldehyde Durable Flame-Retardant Finishing of Nomex/Cotton Blend Using a Hydroxyl-Functional Organophosphorus Oligomer and 1,2,3,4-Butanetetracarboxylic Acid , Journal of Fire Sciences , 25(5): 425-446.

14.

Yang, C.Q. and Qiu, X. (2007). Flame Retardant Finishing of Cotton Fleece: Part I. The Use of A Hydroxyl-Functional Organophosphorus Oligomer and DMDHEU , Fire and Materials, 31(1): 67-81.

15.

Yang, C.Q. (1991). Characterizing the Ester Cross-Linkages of Cotton Cellulose with FT-IR Photoacoustic Spectroscopy , Textile Research Journal, 61(5): 298-305.

16.

Yang, C.Q. and Bakshi, G.D. (1996). Quantitative Analysis of the Nonformaldehyde Durable Press Finish on Cotton Fabric: Acid-Base Titration and Infrared Spectroscopy , Textile Research Journal, 66(6): 377-384.

17.

Yang, C.Q. (2001). FT-IR Spectroscopy Study of the Catalysis for Ester Crosslinking of Cotton Cellulose Catalyzed by Sodium Hypophosphite , Textile Research Journal, 71(3): 201-206.

18.

Yang, C.Q. and Wang, X. (1997). Infrared Spectroscopy Studies of the Cyclic Anhydride as the Intermediate for the Ester Crosslinking of Cotton Cellulose by Polycarboxylic Acids: III . The Molecular Weight of A Crosslinking Agent, Journal of Polymer Science, Part A: Polymer Chemistry, 35(3): 557-564.

19.

Yang, C.Q. and Wang, X. (1996). Formation of the Cyclic Anhydride Intermediates and Esterification of Cotton Cellulose by Multifunctional Carboxylic Acids: An Infrared Spectroscopy Study , Textile Research Journal, 66(9): 595-603.