Interlaminar Normal Stiffness and Strength of Thick Orthotropic Laminates: An Experimental Study

Abstract

A test techique for measuring the interlaminar (in the thickness direction) tensile stiffness and strength of orthotropic laminates is discussed. A special gripping technique is used to eliminate the end bending of the specimens due to any misalignment of the load frame grips. The measured values of the interlaminar normal stiffness, Poisson's ratio, and strength of AS4/3501-6 composite laminates ([0/90]_100s and [0/90/ ± 45]_50S), both in tension and compression, are presented. It is observed, espe cially for the [0/90/ ± 45] laminate, that the interlaminar stiffness decreases with increas ing specimen aspect ratio (ratio of specimen gage length to thickness) of greater than 15, due to the free-edge stress effect as confirmed by a finite element analysis. The average values of the interlaminar tensile stiffness for [0/90] and [0/90/ ± 45] laminates are found to be respectively 18 and 23 percent higher than the transverse stiffness of the constituent ply. Analysis of failure strength indicates that the interlaminar compressive failure is a highly interactive failure mode, whereas the tensile failure is controlled by the in terlaminar normal stress, a non-interactive failure mode.

Keywords

interlaminar test interlaminar stiffness interlaminar strength Poisson's ratio graphite/epoxy composite laminate AS4/3501-6.

Get full access to this article

View all access options for this article.

References

Pagano, N.J. 1974. "Exact Moduli of Amsotropic Laminates," Mechanics of Composite Materials, Vol. 2, G. P. Sendeckyj , ed., Academic Press.

Chou, P.C. and J. Carleone. 1972. "Elastic Constants of Layered Media ," Journal of Composite Materials, 6:80-93.

Sun, C.T. and S. Li. 1988. "Three-Dimensional Effective Elastic Constants for Thick Laminates," Journal of Composite Materials , 22(7):629-639.

Christensen, R.M. and E. Zywicz. 1990. "A Three-Dimensional Constitutive Theory for Fiber Composite Laminated Media," Journal of Applied Mechanics, Trans. of ASME, 57:948-955.

Roy, A.K. and S.W. Tsai. 1992. "Three-dimensional Effective Moduli of Orthotropic and Symmetric Laminates, Journal of Applied Mechanics, Trans. of ASME, 59:39-47.

Adams, D.F. and D.E. Walrath. 1987. "In-Plane and Interlaminar Iosipescu Shear Properties of Various Graphite Fabric/Epoxy Laminates," Journal of Composites Technology and Research, 9(3):88-94.

Post, D. , F. Dai , Y. Guo and P. Ifju , 1989. "Interlaminar Shear Moduli of Cross-Ply Laminates: An Experimental Study," Journal of Composite Materials, 23(3):264-279.

Roy, A.K. and R.Y. Kim. 1989. "Measurement of Interlaminar Shear Stiffness of Symmetric Laminates by Three-Point Bend Test, Experimental Techniques, 14(4):34-38.

Kim, I. , H.T. Hahn and C.E. Bakis. 1991. "Laminated Plate Theory for Thick Composites: Experimental Correlation, Proceedings of the 8th International Conference on Composite Materials (ICCM/8, Honolulu, (July 15-19), pp. 30-H-1.

10.

Kim, R.Y. , F. Abrams and M. Knight. 1988. "Mechanical Characterization of a Thick Composite Laminate," Proceedings of the American Society for Composites, 3rd Technical Conference, Seattle, WA:(September 25-29).

11.

LeClair, S.R. , F.L. Abrams , T.J. Lagnese , C.W. Lee and J.B. Park. 1987. "Qualitative Process Automation for Autoclave Cure of Composite Parts," AFWAL-TR-87-4083, AFWAL/MLTC, OH: Wright-Patterson AFB, (July).

12.

Pagano, N.J. and S.R. Soni. 1988. "Strength Analysis of Composite Turbine Blades," Journal of Reinforced Plastics and Composites, 7:558-581.

13.

Tsai, S.W. and E.M. Wu. 1971. "General Theory of Strength for Anisotropic Materials," Journal of Composite Materials, 5:58-80.

14.

Roy, A.K. and T.N. Massard. 1992. "Strength Analysis and A Design Study of Thick Multilayered Composite Spherical Pressure Vessel," Journal of Reinforced Plastics and Composites, 11:479-493.