Dielectric and thermal properties of flame retardant fillers in polypropylene/ethylene propylene diene monomer composites

Abstract

The incorporation of zinc hydroxystannate, calcium borate, and a phosphorus-based nonhalogenated flame retardant fillers (with trade name of NP-100) in 50% polypropylene and 50% ethylene propylene diene monomer blends was investigated. The composites were prepared using an internal mixer and were molded using a compression mold to form test samples. Studies on the effect of filler loading (15, 30, 45, and 60 vol%) on dielectric breakdown strength, dielectric properties, and thermal conductivity were determined. The flow properties analyzed using the melt flow index revealed that the addition of zinc hydroxystannate increased the melt flow index of the polypropylene/ethylene propylene diene monomer blends, whereas the addition of calcium borate and NP-100 decreased the melt flow index values. A study on the dielectric properties of zinc hydroxystannate, calcium borate, and NP-100-filled polypropylene/ethylene propylene diene monomer composites found that polypropylene/ethylene propylene diene monomer/NP-100 has higher breakdown strength compared with polypropylene/ethylene propylene diene monomer/zinc hydroxystannate and polypropylene/ethylene propylene diene monomer/calcium borate. The dielectric constant of the polypropylene/ethylene propylene diene monomer/calcium borate system is the highest, followed by polypropylene/ethylene propylene diene monomer/NP-100, and the least value of the dielectric constant is exhibited by polypropylene/ethylene propylene diene monomer/zinc hydroxystannate. For the dielectric loss of the composite, the polypropylene/ethylene propylene diene monomer/zinc hydroxystannate, polypropylene/ethylene propylene diene monomer/calcium borate, and polypropylene/ethylene propylene diene monomer/NP-100 blends recorded the lowest, medium, and highest values, respectively. The thermal conductivity of NP-100 is the highest, followed by calcium borate, and then zinc hydroxystannate. The polypropylene/ethylene propylene diene monomer filled with 15 vol% of NP-100 is found to be the most suitable composition for electrical insulation compared with other volume composition percentages on account of low thermal conductivity, good flow ability, high breakdown strength, high dielectric constant, and low dielectric loss.

Keywords

Flame retardant filler dielectric properties thermal conductivity polypropylene ethylene propylene diene monomer

Get full access to this article

View all access options for this article.

References

Ehsani

Borsi

Gockenbach

. An investigation of dynamic mechanical, thermal, and electrical properties of housing materials for outdoor polymeric insulators. Eur Polym J 2004; 40(11): 2495–2503.

Ehsani

Borsi

Gockenbach

. Study of electrical, dynamic mechanical and surface properties of silicone-EPDM blends. In: 2004 International conference on solid dielectrics 5–9 July; Vol. 1Toulouse: France, pp. 431–434.

Nasrat LS and Sharkawy RM. An investigation into the electrical properties of rubber blends for insulators. In: 2007 Electrical insulation conference and electrical manufacturing expo, Tennessee, United States, 24–27 September, Art. no. 4562607, pp.146–149.

Halimatuddahliana HI and Md. Akil H. Flow behavior of polypropylene/ethylene-propylene diene terpolymer/natural rubber (PP/EPDM/NR) blends by torque rheometer: the effect of N,N-m-phenylene bismaleimide (HVA-2) addition. Polym–Plast Technol Eng 2007; 44(8–9): 1429–1442.

Khan

Zaman

. Effect of surface modification of jute with acrylic monomers on the performance of polypropylene composites. J Reinf Plast Compos 2010; 29(8): 1195–1205.

Khalili

SMR

Farsani

Rafiezadeh

. An experimental study on the behavior of PP/EPDM/JUTE composites in impact, tensile and bending loadings. J Reinforced Plast Compos 2011; 30(16): 1341–1347.

Öksüz

Eroglu

Yildinm

. Effect of talc on the properties of polypropylene/ethylene/propylene/diene terpolymer blends. J Appl Polym Sci 2006; 101(5): 3033–3039.

Arroyo

Zitzumbo

Avalos

. Composites based on PP/EPDM blends and aramid short fibres. Morphology/behaviour relationship. Polymer 2000; 41(16): 6351–6359.

Brostow

Datashvili

Hackenberg

. Effect of different types of peroxides on properties of vulcanized EPDM + PP blends. Polym Compos 2010; 31(10): 1678–1691.

10.

Ezzati

Ghasemi

Karrabi

. Rheological behaviour of PP/EPDM blend: the effect of compatibilization. Iran Polym J (Engl Ed) 2008; 17(9): 669–679.

11.

Bouchart

Bhatnagar

Brieu

. Study of EPDM/PP polymeric blends: mechanical behavior and effects of compatibilization. Comptes Rendus— Mecanique 2008; 336(9): 714–721.

12.

Prut

Erina

Karger-Kocsis

. Effects of blend composition and dynamic vulcanization on the morphology and dynamic viscoelastic properties of PP/EPDM blends. J Appl Polym Sci 2008; 109(2): 1212–1220.

13.

Laoutid

Bonnaud

Alexandre

. New prospects in flame retardant polymer materials: from fundamentals to nanocomposites. Mater Sci Eng R 2009; 63(3): 100–125.

14.

Kaynak

Isitman

. Synergistic fire retardancy of colemanite, a natural hydrated calcium borate, in high-impact polystyrene containing brominated epoxy and antimony oxide. Polym Degrad Stab 2011; 96(5): 798–807.

15.

Bakar

MBA

Leong

Ariffin

. Effect of chemical treatments on the mechanical, flow, and morphological properties of talc- and kaolin-filled polypropylene hybrid composites. J Appl Polym Sci 2008; 110: 2770–2779.

16.

Ruksakulpiwat

Sridee

Suppakarn

. Improvement of impact property of natural fiber-polypropylene composite by using natural rubber and EPDM rubber. Compos Part B: Eng 2009; 40(7): 619–622.

17.

Zhang

. Zinc hydroxystannate and zinc stannate as flame-retardant agents for flexible poly(vinyl chloride). J Appl Polym Sci 2005; 98(3): 1469–1475.

18.

Morgan

Wilkie

. Flame retardant polymer nanocomposites, 1st ed. Hoboken, NJ, United States: John Wiley, 2007, pp. 10–10.

19.

Albano

González

Ichazo

. Mechanical and morphological behavior of polyolefin blends in the presence of CaCO3. Compos Struct 1999; 48(1–3): 49–58.

20.

Park

E-S

. Processibility and mechanical properties of micronized polytetrafluoroethylene reinforced silicone rubber composites. J Appl Polym Sci 2008; 107(1): 372–381.

21.

Park

E-S

. Morphology, mechanical, and dielectric breakdown properties of PBT/PET/TPE, PBT/PET/PA66, PBT/PET/LMPE, and PBT/PET/TiO₂ blends. Polym Compos 2008; 29(10): 1111–1118.

22.

Babrauskas

. Mechanisms and modes for ignition of low-voltage, PVC-insulated electrotechnical products. Fire Mater 2006; 30(2): 151–174.

23.

Chand

Nigrawal

. Development, dielectric, and thermal studies on HAF carbon-filled polyester gradient composites. J Compos Mater 2009; 43(24): 2859–2869.

24.

Nisa

Rajesh

Murali

. Preparation, characterization and dielectric properties of temperature stable SrTiO₃/PEEK composites for microwave substrate applications. Compos Sci Technol 2008; 68(1): 106–112.

25.

Hong

Winberg

Schadler

. Dielectric properties of zinc oxide/low density polyethylene nanocomposites. Mater Lett 2005; 59(4): 473–476.

26.

Jylhä

Sihvola

. Equation for the effective permittivity of particle-filled composites for material design applications. J Phys D: Appl Phys 2007; 40(16): 4966–4973.

27.

Chen

Zhang

. Reinforcement of ethylene-propylene-diene rubber/samarium borate and ethylene-propylene-diene rubber/Sb-doped SnO₂ composites by three types of ethylene-acrylic acid: assessment of acrylic acid content on crystallinity, cure, mechanical, and electric properties. J Reinf Plast Compos 2010; 29(19): 2946–2960.

28.

Zhou

. Thermal and dielectric properties of the aluminum particle/epoxy resin composites. J Appl Polym Sci 2010; 118(6): 3156–3166.

29.

Xiang

Wang

Yao

. Dielectric properties of SrTiO₃/POE flexible composites for microwave applications. J Eur Ceram Soc 2007; 27: 3093–3097.

30.

Xiang

Wang

Yao

. Preparation and dielectric properties of bismuth-based dielectric/PTFE microwave composites. J Eur Ceram Soc 2006; 26(10–11): 1999–2002.

31.

Tarawneh

Ahmad

Rasid

. Thermal behavior of MWNT-reinforced thermoplastic natural rubber nanocomposites. J Reinf Plast Compos 2011; 30(3): 216–221.

32.

Chen

Zhu

. Study on thermally conductive ESBR vulcanizates. Polym Bull 2011; 67(6): 1091–1104.

33.

Puryanti

Ahmad

SHj

Abdullah

MHj

. Effect of nickel-cobalt-zinc ferrite filler on magnetic and thermal properties of thermoplastic natural rubber composites. Int J Polym Mater 2007; 56(3): 327–338.

34.

Lee

G-W

Park

Kim

. Enhanced thermal conductivity of polymer composites filled with hybrid filler. Compos Part A: Appl Sci Manuf 2006; 37(5): 727–734.

35.

Mansour

Al-Ghoury

Shalaan

. Thermal properties of graphite-loaded nitrile rubber/poly(vinyl chloride) blends. J Appl Polym Sci 2010; 116(6): 3171–3177.

36.

Chen

Y-M

Ting

J-M

. Ultra high thermal conductivity polymer composites. Carbon 2002; 40(3): 359–362.

37.

Gojny

Wichmann

MHG

Fiedler

. Evaluation and identification of electrical and thermal conduction mechanisms in carbon nanotube/epoxy composites. Polymer 2006; 47(6): 2036–2045.

38.

Kemaloglu

Ozkoc

Aytac

. Thermally conductive boron nitride/SEBS/EVA ternary composites: “Processing and characterization”. Polym Compos 2010; 31(8): 1398–1408.

39.

Dong

Fan

Wong

. Effect of interface on thermal conductivity of polymer composite. In: 2005 Electronic components and technology conference 31 May–3 June; Vol. 2Florida: United States, pp. 1451–1454.