Self-reinforced poly(ethylene terephthalate) composite laminates were manufactured from fabric using a hot press. Fabric was either allowed to shrink or exposed to stretching during different phases of the manufacturing process. Composite macrostructure, crimp, was investigated and results showed that shrinkage affects fibre crimp more than stretching does. Mechanical tests showed that shrinkage do not significantly affect mechanical properties while stretching fabric by 10% during heating results in 50% increase in tensile stiffness. The lack of correlation between crimp and mechanical properties indicates that mechanical properties for self-reinforced poly(ethylene terephthalate) composites are dominated by their microstructure, molecular orientation, which may be affected by the manufacturing process.
SalemDR. Orientation and crystallization in poly(ethylene terephthalate) during drawing at high temperatures and strain rates. Polym Eng Sci1999; 39: 2419–2430.
4.
GuptaVRadhakrishnanJSettS. Interaction between thermal shrinkage and crystallization in axially oriented poly(ethylene terephthalate) fibres and films. Polymer1993; 34: 3814–3822.
5.
PakulaTTrznadelM. Thermally stimulated shrinkage forces in oriented polymers: 1 Temperature dependence. Polymer1985; 26: 1011–1018.
6.
ZhangXTianXYaoX. Isothermal and non-isothermal shrinkage behaviors of highly oriented pet yarns. Fibers Polym2008; 9: 360–364.
7.
LongSDWardIM. Shrinkage force studies of oriented polyethylene terephthalate. J Appl Polym Sci1991; 42: 1921–1929.
8.
PakhomovPShablyginMTsaplinV. The molecular mechanism of shrinkage of polyethylene terephthalate. Polym Sci USSR1983; 25: 672–679.
9.
AlcockBCabreraNBarkoulaN-M. The effect of processing conditions on the mechanical properties and thermal stability of highly oriented pp tapes. Eur Polym J2009; 45: 2878–2894.
10.
AlcockBCabreraNBarkoulaN-M. The effect of temperature and strain rate on the mechanical properties of highly oriented polypropylene tapes and all-polypropylene composites. Compos Sci Technol2007; 67: 2061–2070.
11.
CabreraNAlcockBLoosJ. Processing of all polypropylene composites for ultimate recyclability. Proc Instn Mech Engrs2004; 218: 145–155.
12.
AbrahamTBanikKKarger-KocsisJ. All-pp composites (pure) with unidirectional and cross-ply lay-ups: Dynamic mechanical thermal analysis. eXPRESS Polym Lett2007; 1: 519–526.
13.
AlcockBCabreraNBarkoulaN-M. The mechanical properties of unidirectional all-polypropylene composites. Compos Part A2006; 37: 716–726.
AlcockBPeijsT. Technology and development of self-reinforced polymer composites. Adv Polym Sci2013; 251: 1–76.
17.
Karger-KocsisJBárányT. Single-polymer composites (SPCs): Status and future trends. Compos Sci Technol2014; 92: 77–94.
18.
PiggottM. The effect of fibre waviness on the mechanical properties of unidirectional fibre composites: A review. Compos Sci Technol1995; 53: 201–205.
19.
PrabhakaranRDLilholtHAvilesF. Fibre waviness and misalignment measurement of unidirectional glass/LPET commingled composites – Effect on mechanical properties. Risoe Int Symp Mater Sci Proc2013; 34: 349–363.
20.
PiggottM. A theoretical framework for the compressive properties of aligned fibre composites. J Mater Sci1981; 16: 2837–2845.
BogettiTAGillespieJWJrLamontiaMA. Influence of ply waviness on the stiffness and strength reduction on composite laminates. J Thermoplast Compos Mater1998; 5: 344–369.
23.
HsiaoHDanielI. Effect of fiber waviness on stiffness and strength reduction of unidirectional composites under compressive loading. Compos Sci Technol1996; 56: 581–593.
24.
SchneiderCKazemahvaziSÅkermoM. Compression and tensile properties of self-reinforced poly(ethylene terephthalate) composites. Polym Test2013; 32: 221–230.
25.
AlcockBCabreraNBBarkoulaN-M. The mechanical properties of woven tape all-polypropylene composites. Compos Part A2007; 38: 147–161.
26.
BaranyTIzerACziganyT. High performance self-reinforced polypropylene composites. Mater Sci Forum2007; 537–538: 121–128.
27.
ZhangJReynoldsCPeijsT. All-poly(ethylene terephthalate) composites by film stacking of oriented tapes. Compos Part A2009; 40: 1747–1755.
28.
ZhangJMPeijsT. Self-reinforced poly(ethylene terephthalate) composites by hot consolidation of bi-component pet yarns. Compos Part A2010; 41: 964–972.
29.
IzerABaranyT. Effect of consolidation on the flexural creep behavior of all-polypropylene composite. eXPRESS Polym Lett2010; 4: 210–216.
30.
ChenJWuCPuF. Fabrication and mechanical properties of self-reinforced poly(ethylene terephthalate) composites. eXPRESS Polym Lett2011; 5: 228–237.
31.
WuCChangCWangC. Optimum consolidation of all-polyester woven fabric-reinforced composite laminates by film stacking. Polym Compos2012; 33: 245–252.
32.
AlcockBCabreraNBBarkoulaN. Direct forming of all-polypropylene composites products from fabrics made of Co-extruded tapes. Appl Compos Mater2009; 16: 117–134.
33.
PeirceFT. The geometry of cloth structure. J Text Inst1937; 28: 145–196.