Flexural and Morphological Properties of Poly(Methyl Methacrylate)/ Hydroxyapatite Composites: Effects of Planetary Ball Mill Grinding Time

Abstract

Poly(methyl methacrylate) (PMMA)/hydroxyapatite (HA) composites have potential applications in bone cement, prosthesis, and dental implant. In this study, PMMA containing 5 wt% of HA is prepared using polymerization followed by compression molding. PMMA and HA powder are ground using planetary ball milling. The grinding time takes from 30 to 120 min. The effects of the grinding time and particle size of the PMMA/HA powder on the flexural properties and morphology of the composites are investigated. The structure patterns of PMMA/5HA are characterized using X-Ray diffraction (XRD). No new phase is observed in the XRD pattern with the different sizes of PMMA/HA powder. This indicates that planetary milling solely reduces the size of PMMA/ HA powder. However, it does not modify the structure of PMMA and HA. A reduction of ~40% in the particle diameter is observed in both PMMA and PMMA/5HA powder after subjected to planetary milling for 60 min. For the planetary ball mill-ground PMMA/HA powder, the flexural modulus of the respective PMMA composites is slightly increased. Planetary milling can increase the volume of fine particles in the composites specimens, which results in a more homogeneous distribution of HA and a reduction of void contents in PMMA matrix. The reduction in void content is observed on the fractured surface of PMMA composites through field emission scanning electron microscopy.

Keywords

poly(methyl methacrylate)hydroxyapatite planetary ball mill flexural properties.

Get full access to this article

View all access options for this article.

References

Camilo, M. , Eliana, S. , Shereen, S.A. and Juan, M.U. ( 2007). Comparative Study of the Transverse Strength of Three Denture Base Materials, Journal of Dentistry, 35(12): 930-933.

Meng, T.R. and Latta, M.A. ( 2005). Physical Properties of Four Acrylic Denture Base Resins , Journal of Contemporary Dental Practice, 6(4): 93-100.

Cheang, P. and Khor, K.A. ( 2005). Effect of Particulate Morphology on the Tensile Behaviour of Polymer-hydroxyapatite Composites, Materials Science and Engineering, A345: 47-54.

Marino, X. ( 2005). Functional Fillers for Plastics, WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Sandrine, G. , Saioa, A. and Jacques, L. ( 2009). Preparation and Characterization of Dense Nanohydroxyapatite/PLLA Composites, Materials Science and Engineering, C29(1): 172-177.

Zuo, Y. , Li, Y.B. , Li, J.D. , Zhang, X. , Liao, H.B. , Wang, Y.Y. and Yang, W.H. ( 2007). Novel Bio-composite of Hydroxyapatite Reinforced Polyamide and Polyethylene: Composition and Properties, Materials Science and Engineering, A452-453: 512-517.

Joseph, R. , McGregor, W.J. , Martyn, M.T. , Tanner, K.E. and Coates, P.D. ( 2002). Effect of Hydroxyapatite Morphology/Surface Area on the Rheology and Processability of Hydroxyapatite filled Polyethylene Composites , Biomaterials, 23(21): 4295-4302.

Fang, L.M. , Leng, Y. and Gao, P. ( 2005). Processing of Hydroxyapatite Reinforced Ultrahigh Molecular Weight Polyethylene for Biomedical Applications, Biomaterials , 26(17): 3471-3478.

Fang, L.M. , Gao, P. and Leng, Y. ( 2007). High Strength and Bioactive Hydroxyapatite Nano-particles Reinforced Ultrahigh Molecular Weight Polyethylene, Composites Part B: Engineering, 38: 345-351.

10.

Zhang, X. , Li, Y.B. , Zuo, Y. , Lv, G.Y. , Mu, Y.H. and Li, H. ( 2007). Morphology, Hydrogen-bonding and Crystallinity of Nano-Hydroxyapatite/Polyamide 66 Biocomposites, Composites Part A: Applied Science and Manufacturing , 38(3): 843-848.

11.

Sreckovic, T. , Bernik, S. , Ceh, M. and Vojisavljevic , K. (2008). Microstructural Characterization of Mechanically Activated ZnO Powders, Journal of Microscopy, 232(3): 639-642.

12.

Ulrich, G. ( 2004). High-energy Dry Ball-milling of TiO2 White Pigments. Available at: http://www.123people.de/s/ulrich+gesenhues (accessed March 15, 2009).

13.

Ezequiel, C.S. , Enrique, T.M. , Cesar, D. and Fumio, S. (2004). Effects of Grinding of the Feldspar in the Sintering using a Planetary Ball Mill, Journal of Materials Processing Technology, 152(3): 284-290.

14.

O’Donnell, J.N.R. , Antonucci, J.M. and Skrtic, D. (2008). Illuminating the Role of Agglomerates on Critical Physicochemical Properties of Amorphous Calcium Phosphate Composites, Journal of Composite Materials, 42: 2231-2246.

15.

Pang, P.S. , Li, W. and Liu, Y. ( 2007). Effect of Ball Milling Process on the Microstructure of Titaniumnanohydroxyapatite Composite Powder, Rare Metals , 26(2): 118-123.

16.

O’Donnell, J.N.R. , Skrtic, D. and Antonucci, J.M. (2006). Amorphous Calcium Phosphate Composites with Improved Mechanical Properties, Journal of Bioactive and Compatible Polymers, 21: 169-184.

17.

Wang, M. , Porter, D. and Bonfield, W. ( 1994). Processing, Characterization, and Evaluation of Hydroxyapatite Reinforced Polyethylene Composites, British Ceramic Transations , 93: 91-95.

18.

Fernanda, F. , Marcelo, A.C. , Altair, A.D.B.C. and Renata , C.M.R.G. (2006). Impact Strength and Fracture Morphology of Denture Acrylic Resins, The Journal of Prosthetic Dentistry, 96(5): 367-373.

19.

Nina, O. , Nebojsa, M. and Vladimir, P. ( 2009). Structural and Electrical Properties of Sintered Zinc-titanate Ceramics, Ceramics International, 35(1): 35-37.

20.

Samayamutthirian, P. and Noorina, H.J. (2009). Influence of Milling Conditions on the Mechanochemical Synthesis of CaTiO3 Nanoparticles, Journal of Alloys and Compounds, 476(1-2): 894-902.

21.

Sousa, R.A. , Reis, R.L. , Cunha, A.M. and Bevis, M.J. (2003). Coupling of HDPE/hydroxyapatite Composites by Silane-based Methodologies, Journal of Material Science: Materials in Medicine, 14(6): 475-487.

22.

Saied, H.M. ( 2006). Mechanical, Physical and Biological Properties of Denture Base Poly(methyl methacrylate) Filled with Ceramic Fillers, PhD Dissertation, Universiti Sains Malaysia, Penang, Malaysia, pp. 89-92.

23.

Nasiri, T.B. , Pezhman, H. , Ebrahimi, K.R. and Peyman, H. (2009). Synthesis of Nanosize Single-crystal Hydroxyapatite via Mechanochemical Method, Materials Letters, 63(5): 543-546.