The corrosion performance of carbon reinforced plain-weave laminates in 3.5% NaCl solution was evaluated by different corrosion measurement techniques to determine the suitability for applications in a corrosive environment. Based on the experimental studies it was observed that this composite offers a high resistance to corrosion in 3.5% NaCl solution both in static and in flow velocity up to 1.8 m/s.
2. Crowe, C.P. (1980). Localized Corrosion from Graphite/Aluminum and Welded SiC/Al Matrix Composite, NRL Report 5415, Naval Research Laboratory, Washington DC .
3.
3. Dull, D.L. , Harrigan, W.C. Jr. and Amateau, M.F. (1977). Final Report, The Effect of Matrix and Fiber Composition on Mechanical Strength and Corrosion Behavior of Graphite-Aluminum Composites, 15th Jan. 1977, Baltelle Memorial Institute, Columbus, Ohio, 4328 .
4.
4. ASTM G51-72 (1999). Standard Practice for Laboratory Immersion Corrosion Testing, Corrosion, Testing of Metals in Annual Book of Standards, Vol. 03-02, Philadelphia, ASTM, PA .
5.
5. Ahmad, Z. and Abdul Aleem, B.J. (1988). Final Report Erosion Corrosion of SiC-A16013 Composites in Sea Water at Controlled Flow Velocities, Final Report - AR-14-65, King Abdul Aziz City for Science and Technology, Riyadh .
6.
6. Ahmad, Zaki and Abdul Aleem, Jr. B.J. (2000). Mat. Eng. and Porf, 9(3): 338 .
7.
7. Boinard, P. , Boinard, E. and Pethrick, R.A.et al. (1999). MRS Fall Meeting, 1994, Symposium, NonDestructive Method for Material Characterization, Boston, Mass, U.S.A.
8.
8. Ahmad, Zaki (1988). British Corrosion Journal, 33(3): 230 .
9.
9. Aylor, Denise M. and Moran, Patrick J. (1980). J. Electrochemical Sc. and Tech., 132(6): 277 .