Fatigue Fracture Resistance Analysis of Polymer Composites Based on the Energy Expended on Damage Formation

Abstract

Analysis of the fatigue crack propagation behavior of filled polytetrafluoroethylene (PTFE) composites using the energy expended on damage formation was performed. A 25% chopped glass fiber filled PTFE with a commercial name of Rulon LR and a 25% polymer particle filled PTFE (Rulon J) were chosen as candidate materials for the study. Fatigue crack propagation (FCP) tests were performed using both unnotched and single edge notched (SEN) specimens under tension-tension load control condition. The notched specimens were prepared with the same notch length to sample width ratio (a/w) of 0.09. The applied frequency was 3 Hz. The maximum stress was 6 MPa, and the ratio of minimum stress to maximum stress was kept at 0.10. FCP data such as the crack length and the number of cycles were used to calculate the crack speed. The hysteresis energies for both notched and unnotched specimens during cyclic loading were obtained. The energy release rate was determined as the first derivative of the relationship between the potential energy and the crack length. The potential energy was calculated as the area above the unloading curve from the hysteresis loops at various crack lengths. The cyclic rate of energy dissipation on damage formation was calculated based on the hysteresis energies for both notched and unnotched specimens. It was found that the fatigue kinetics are related to the cyclic rate of energy dissipation into the active zone evolution. The specific energy of damage (γ) a material parameter characteristic of the fatigue fracture resistance was evaluated using the Modified Crack Layer (MCL) theory. It was found that the value of γ for the particle filled PTFE is 3200 kJ/m³, which is about three times higher than that for the fiber filled PTFE (750 kJ/m³). This indicates that the particle filled PTFE has higher fracture resistance than the fiber filled PTFE. The fracture surface of the second region for both materials was examined using scanning electron microscopy (SEM). Interfacial debonding, drawn ligaments and large voids were associated with the fatigue fracture of the fiber filled PTFE. The particle filled PTFE displayed more fibrillation than that of the fiber filled PTFE, which indicates a higher energy consuming process related to the fatigue crack growth in the particle filled PTFE.

Keywords

particle and fiber filled PTFE composites fatigue energy on damage formation modified crack layer (MCL) theory specific energy of damage fracture surface morphology

Get full access to this article

View all access options for this article.

References

1. Lemaitre, J. , Sermage, J.P. and Desmorat, R. (1999). International Journal of Fracture, 97: 67-81.

2. Jones, N.A. and Lesser, A.J. (1998). Journal of Polymer Science, Part B-Polymer Physics, 36: 2751-2760.

3. Walter, R. , Friedrich, K. , Privalko, V. and Savadori, A. (1997). Journal of Adhesion, 64: 87-109.

4. Azimi, H.R. , Pearson, R.A. and Hertzberg, R.W. (1996). Polymer Engineering and Science, 36: 2352-2365.

5. Azimi, H.R. , Pearson, R.A. and Hertzberg, R.W. (1995). Journal of Applied Polymer Science, 58: 449-463.

6. Shah, A. , Stepanov, E.V. , Capaccio, G. , Hiltner, A. and Baer, E. (1998). Journal of Polymer Science Part B-Polymer Physics, 36: 2355-2369.

7. Oever, M and Peijs, T. (1998). Composites Part A-Applied Science and Manufacturing, 29: 227-239.

8. Hull, D. (1994). Materials science and engineering a-structural materials properties. Microstructure and Processing, 184: 173-183.

9. Hellan, K. (1984). Introduction to Fracture Mechanics. New York: McGraw-Hill Book Company, pp. 49-69.

10.

10. Ellyin, F. (1997). Fatigue Damage, Crack Growth and Life Prediction. London: Chapman and Hall, pp. 86-89.

11.

11. Lefebvre, D. and Ellyin, F. (1984). Int. J. Fatigue, 6: 9-15.

12.

12. Ellyin, F. (1985). J. Eng. Mater. Technol., Trans. ASME, 107: 119-125.

13.

13. Ellyin, F. and Kujawski, D. (1984). J. Pressure Vessel Technol., Trans. ASME, 106: 342-347.

14.

14. Topoleski, L.D.T. , Ducheyne, P. and Cuckler, J.M. (1993). Biomaterials, 14: 1165-1172.

15.

15. Horst, J.J. and Spoormaker, J.L. (1996). Polymer Engineering and Science, 36: 2718-2726.

16.

16. Altus, E. and Herszage, A. (1995). Mechanics of Materials, 20: 209-223.

17.

17. Chen, T.J. , Chudnovsky, A. and Bosnyak, C.P. (1994). J. Mater. Sci., 29: 5903-5910.

18.

18. Pruitt, L. and Suresh, S. (1994). Polymer, 35: 3221-3229.

19.

19. Yamashita, A. , Higashi, S. , Komatsu, S.T. , Takahara A. and Kajiyama, T. (1998). Polymer Blends and Polymer Composites, 137: 147-154.

20.

20. Siebert, A.R. , Guiley, C.D. , Kinloch, A.J. , Fernando, M. and Heijnsbrock, E.P.L. (1996). Toughened Plastics, 252: 151-160.

21.

21. Liu J.Y. and Ross, R.J. (1996). J. Eng. Mater. Techonl., Trans. ASME, 118: 375-378.

22.

22. Kim, H.S. and Wang, X.M. (1995). J. Appl. Polym. Sci., 57: 811-817.

23.

23. Wyzgoski, M.G. and Novak, G.E. (1995). Polymer Composites, 16: 38-51.

24.

24. Strebel, J.J. and Moet, A. (1994). J. Appl. Polym. Sci., 52: 1815-1821.

25.

25. Pulos, G.C. and Knauss, W.G. (1998). Int. J. Fract., 93: 145-159.

26.

26. Chen, L.P. , Yee, A.F. and Moskala, E.J. (1999). Macromolecules, 32: 5944-5955.

27.

27. Parsons, M. , Stepanov, E.V. , Hiltner, A. and Baer, E. (1999). J. Mater. Sci., 34: 3315-3326.

28.

28. Strebel, J.J. and Moet, A. (1995). J. Polym. Sci. Part B-Polym. Phys., 33: 1969-1984.

29.

29. Ma, X. , Sauer, J.A. and Hara, M. (1995). Macromolecules, 28: 5526-5534.

30.

30. Arnold, J.C. (1995). Polym. Eng. Sci., 35: 165-169.

31.

31. Hristov, H.A. , Yee, A.F. , Xie, L. and Gidley, D.W. (1994). Polymer, 35: 4287-4292.

32.

32. Hristov, H.A. , Yee, A.F. and Gidley, D.W. (1994). Polymer, 35: 3604-3611.

33.

33. Wyzgoski, M.G. and Novak, G.E. (1994). J. Appl. Polym. Sci., 51: 873-885.

34.

34. Aglan, H. (1993). Int. J. Damage Mech., 2: 53-72.

35.

35. Aglan, H. , Othman, A. and Figueroa, L. (1994). J. of Matrl. Sci., 29: 4786-4792.

36.

36. Aglan, H. (1993). J. of Elas. and Plas., 25: 307-321.

37.

37. Aglan, H. , Shehata, I. , Figueroa, L. and Othman, A. (1992). Structure-fracture toughness relationships of asphalt concrete mixtures. In: Trans. Research Record 1353, TRB, Wash., D.C., pp. 24-30.

38.

38. Aglan, H. and Figueroa, J.L. (1993). J. of Eng. Mech., 119: 1243-1259.

39.

39. Aglan, H. and Moet, A. (1989). Int. J. of Fract., 40: 285.

40.

40. Aglan, H. , Othman, A. , Figueroa, L. and Rollings, R. (1993). Effect of styrene-butadiene-styrene modifier percentage on the fatigue crack propagation behavior of pavements. In: Trans. Research Record 1417, TRB, Wash., D.C., pp. 178-186.

41.

41. Aglan, H. , Othman, A. and Figueroa, F. (1994). Specific energy of damage as fracture toughness criteria for asphaltic pavements. In Trans. Research Record 1449, TRB, Wash., D.C., pp. 57-63.

42.

42. Aglan, H. and Chudnovsky, A. (1990). Int. J. Fract., 44: 167.

43.

43. Othman, A. , Figueroa, L. and Aglan, H. (1995). Fatigue behavior of SBS modified asphaltic mixtures exposed to low temperature cyclic aging. In: Trans. Research Record 1492, TRB, Wash., D.C., pp. 129-134.

44.

44. Aglan, H. and Bayomy, F.M. (1997). Innovative approach to fatigue crack propagation in concrete pavements. In Trans. Research Record 1568, TRB, Wash., D.C., pp. 17-23.

45.

45. Aglan, H. , Gan, Y.X. , Chin, B.A. and Grossbeck, M.L. (1999). J. Nucl. Mater., 237: 192-202.

46.

46. Aglan, H. and Gan, Y.X. (2001). J. Mater. Sci., 36: 389-397.

47.

47. Aglan, H. , Gan, Y. , El-Hadik, M. , Faughnan, P. and Bryan, C. (1999). J. Mater. Sci., 34: 83-97.

48.

48. Faughnan, P. , Bryan, C. , Gan, Y. and Aglan, H. (1998). J. Mater. Sci. Letts., 17: 1743-1746.

49.

49. El-Hadik, M. (1999). MSc Thesis (Advisor: Dr. H. Aglan), Tuskegee University.

50.

50. Zhang, Z. , Aglan, H. Faughnan, P. and Bryan, C. (1998). J. Reinforced Plastics and Composites, 17: 752-771.

51.

51. Aglan H. (2000). Fracture morphology of selective polymer systems under monotonic and fatigue loading, NASA Technical Annual Report, NASA John F. Kennedy Space Center, Florida, pp. 75-97.