Fatigue Fracture Mechanisms of Particle and Fiber Filled PTFE Composites

Abstract

The effect of filler type on the fatigue fracture mechanisms of polytetrafluoroethylene (PTFE) composites was studied. The two composites were a silica particle filled PTFE (Garlock 3502‘) and a glass fiber filled PTFE (Garlock 8573‘). Tension-tension fatigue crack propagation tests were conducted on both materials at room temperature at a frequency of 3 Hz. The maximum stress was 6 MPa and the ratio of minimum load to maximum load was 0.1. It was found that the fatigue lifetime of the particle filled PTFE is approximately four times higher than that of the fiber filled PTFE. The fatigue data also revealed that the crack speed of the particle filled composite is always lower than that of the short fiber filled composite. Microscopic analysis on representative fracture surface of each material was performed to identify different fracture surface features. The three fracture regions, crack initiation, stable crack growth and unstable crack growth were examined. In the first region, both composites displayed extensive plastic deformation and severe debonding at the filler/matrix interface. In the second region, stable crack propagation, torn ligament bundles, fibrillation and debonded fillers are the main fracture surface features. The fracture surface of the fiber filled PTFE in the unstable crack propagation region has a more smooth appearance with extensive fiber pull-out. This indicates a fast fracture process and a brittle fracture mechanism dominating this region. The third region of the fracture surface for the particle filled PTFE displayed more severe matrix deformation. The particle filled PTFE displayed more intensive fibrillation in the second region than the fiber filled PTFE, indicating more damage formation and thus higher energy consumption in the stable crack propagation stage. Consequently, the crack speed of the particle filled PTFE is lower than that of the fiber filled PTFE composite.

Keywords

fatigue behaviors fracture surface analysis short fiber and particle filled PTFE composites

Get full access to this article

View all access options for this article.

References

1. Hult, J. 1994, in Engineering Mechanics of Fiber Reinforced Polymers and Composite Structures, Edited by J. Hult and F. G. Rammerstorfer , Springer-Verlag, Wien-New York, pp. l-8.

2. Foldi, A. P. 1992, in Composite Applications, The Role of Matrix, Fiber, and Interface, Edited by T. L. Vigo and B. J. Kinzig , VCH Publishers, Inc., pp. 133-178.

3. Andrews, E. H. 1968. Fracture in Polymers, American Elsevier, New York, pp. 99-101.

4. Bartenev, G. M. and V. S. Zuyev . 1968. Strength and Failure of Visco-Elastic Materials, Pergamon Press, Oxford, p. 349.

5. Hertzberg, R. W. and J. A. Manson , 1980. Fatigue of Engineering Plastics, Academic Press, New York, pp. 185-271.

6. Lehr, H. F. , E. Lach , U. Wiese , and A. Bohmann , 1997, Journal De Physique IV, 7: 553-558.

7. Carpinteri, A. and R. Massabo , 1997, International Journal of Solids and Structures, 34:2321-2338.

8. Jensen, H. M. and J. Christoffersen , 1997, Journal of the Mechanics and Physics of Solids, 45:1121-1136.

9. Gotoh, M. and A. B. M. Idris , 1997, JSME International Journal Series A-Solid Mechanics and Materials Engineering, 40:149-157.

10.

10. Adams, R. D. and M. M. Singh , 1996, Composites Science and Technology, 56:977-997.

11.

11. Mandell, J. F. , F. J. McGarry , D. D. Huang and C. G. Li . 1983. Polymer Composites, 4:32.

12.

12. Wang, S. S. and E. S.-M. Chim . 1983. Journal of Composite Materials, 17:114.

13.

13. Mandell, J. F. , 1991, in Fatigue of Composite Materials, Edited by K. L. Reifsnider , Elsevier, Amsterdam, p. 242.

14.

14. Piggott, M. R. , 1995, Composites Science and Technology, 55:269-276.

15.

15. Song, D. Y. , N. Takeda , T. Shioya and K. Nakata . 1996. Composites Part A, 27A:357-364.

16.

16. Kalinka, G. , A. Leistner and A. Hampe . 1997. Composites Science and Technology, 57:845-851.

17.

17. Mukherjee, S. , C. R. Ananth and N. Chandra . 1997. Composites Science and Technology, 57:1501-1512.

18.

18. Piggott, M. R. 1997. Composites Science and Technology, 57:853-857.

19.

19. Rashkovan, I. A. and Y. G. Korabelnikov . 1997. Composites Science and Technology, 57:1017-1022.

20.

20. Mader, E. 1997. Composites Science and Technology, 57:1077-1088.

21.

21. Sanders, B. P. and S. Mall . 1996. Journal of Composites Technology and Research, 18:22-29.

22.

22. Sanders, B. P. and S. Mall . 1996. Journal of Composites Technology and Research, 18:15-22.

23.

23. Cowley, K. D. and P. W. R. Beaumont . 1997. Composites Science and Technology, 57:1211-1219.

24.

24. Cowley, K. D. and P. W. R. Beaumont . 1997. Composites Science and Technology, 57:1309-1329.

25.

25. Gedde, U. W. 1995. Polymer Physics, Chapman & Hall, London, p.159.

26.

26. Strobl, G. R. 1996. The Physics of Polymers, Concepts for Understanding Their Structures and Behavior, Springer-Verlag, Berlin, p. 267.

27.

27. Argon, A. S. and R. E. Cohen . 1990, in Advances in Polymer Science, Crazing in Polymers, Edited by H. H. Kausch , Springer-Verlag, Berlin, 2:303-351.

28.

28. Oshmyan, V. G. and D. K. Muravin . 1997. Composites Science and Technology, 57:1167-1174.

29.

29. Argon, A. S. , R. E. Cohen and O. S. Gebizlioglu . 1987, in Mechanical Behavior of Materials, Edited by M. G. Yan , Pergamon Press, Oxford, 1:3.

30.

30. Boyce, M. E. , A. S. Argon and D. M. Park . 1987. Polymer, 28:1680.

31.

31. Seymour, R. B. 1990. Engineering Polymer Source Book, McGraw-Hill Publishing Company, New York, p. 217.

32.

32. Steijn, R. P. 1986, in Failure of Plastics, Edited by W. Brostow and R. D. Corneliussen , Hanser Publishers, Munich, p. 386.

33.

33. Arkles, B. , S. Gerakaris and R. Goodhue . 1974, in Advances in Polymer Wear, Edited by L.-H. Lee , Plenum Press, New York-London, 5B:663.

34.

34. Evans, D. G. and J. K. Lancaster . 1979, in Materials Science and Technology, Wear, Edited by D. Scott , Academic Press, New York, p. 34.

35.

35. Wu, H. F. , D. W. Pwight and N. T. Huff . 1997. Composites Science and Technology, 57:975-983.

36.

36. Fields, J. T. and A. Garton . 1996. Polymer Composites, 17:242-250.

37.

37. Kausch, H.-H. 1987. Polymer Fracture (Chapter 7), Springer-Verlag, Berlin, pp. 190-191.

38.

38. Cook, J. , and J. E. Gordon . 1964. Proc. Royal. Soc. Lond., A282:508.

39.

39. Gordon, J. E. , 1968. The New Science of Strong Materials, Walker, New York, p.108.

40.

40. Kendall, K. , 1975. Proc. Royal. Soc. Lond., A344:287.

41.

41. Kendall, K. , 1975. Proc. Royal. Soc. Lond., A341:409.

42.

42. Kendall, K. , 1975. Journal of Physics D: Applied Physics, 8:1449.

43.

43. Chellappa, V. and B. Z. Jang . 1996. Polymer Composites, 17:444.

44.

44. Aglan, H. , Y. Gan , M. El-Hadik , P. Faughnan and C. Bryan . 1998, Journal of Materials Science, 34:96.

45.

45. Aglan, H. 1997. “Fracture Morphology of Selective Polymer Systems Under Monotonic and Fatigue Loading,” NASA Technical Annual Report, NASA John F. Kennedy Space Center, Florida, pp. 37-86.

46.

46. Zhang, Z. , H. Aglan , P. Faughnan and C. Bryan , 1998, Journal of Reinforced Plastics and Composites, 17:752-771.