The objective of the present study is to develop and evaluate novel weld repairs of bainitic rail steel defects, such as detail fracture, induced by in service loading. Slots were machined in the bainitic rail steel to simulate the removal of service defects. Multipass gas metal arc welding was used to fill and repair the slots. Three-point bend tests of the parent and welded steels revealed that the flexural weld efficiency was 75%. Fatigue crack propagation (FCP) tests were performed on specimens from the welded joints and compared with the parent materials to determine the mechanical integrity of the slot repairs. The fatigue lifetime and FCP kinetics were similar for the parent and slot welded bainitic steels, indicating similar resistance to FCP. The fatigue fracture surface morphology of the parent and welded bainitic rail steels both revealed mostly a ductile fracture mechanism in all the three FCP stages.
RodriguesPCM, PerelomaEV, SantosDB: ‘Mechanical properties of an HSLA bainitic steel subjected to controlled rolling with accelerated cooling’, Mater. Sci. Eng. A, 2000, A283, (1–2), 136–143.
3.
FangHS, FengC, ZhengYK, YangZG, BaiBZ: ‘Creation of air-cooled Mn series bainitic steels’, J. Iron Steel Res. Int., 2008, 15, (6), 1–9.
4.
BramfittBL, SpeerJG: ‘A perspective on the morphology of bainite’, Metall. Trans. A, 1990, 21A, 817–829.
5.
SawleyKJ, KristanJ: ‘Evaluation of bainitic test rails’, TTCI Technology Digest, Transportation Technology Center Inc., Pueblo, CO, USA, 1998.
6.
SawleyKJ, DavisDD: ‘An improved bainitic steel for frogs’, TTCI Technology Digest, Transportation Technology Center Inc., Pueblo, CO, USA, 1996.
7.
LeeKM, PolycarpouAA: ‘Wear of conventional pearlitic and improved bainitic rail steels’, Wear, 2005, 259, 391–399.
8.
YokoyamaH, MitaoS, YamamotoS, FujikakeM: ‘Effect of the angle on flaking behavior in pearlitic and bainitic steel rails’, Wear, 2002, 9129, 1–7.
9.
SawleyKJ: ‘Bainitic steels for rails’, TTCI Technology Digest, Transportation Technology Center Inc., Pueblo, CO, USA, 1997.
10.
BhadeshiaHKDH: ‘Novel steels for rails’, in ‘Encyclopedia of materials science’, 1–7; 2002, Oxford, Pergamon.
AglanHA, LiuZY, HassanMF, FatehM: ‘Mechanical and fracture behavior of bainitic rail steel’, J. Mater. Process. Technol., 2004, 151, 268–274.
13.
AglanH, FatehM: ‘Fatigue damage tolerance of bainitic and pearlitc rail steels’, Int. J. Damage Mech., 2006, 15, 393–410.
14.
SatohY, IwafuchiK: ‘Crystal orientation analysis of running surface of rail damaged by rolling contact’, Wear, 2005, 258, (7–8), 1126–1134.
15.
JinX, XiaoX, WenZ, GuoJ, ZhuM: ‘An investigation into the effect of train curving on wear and contact stresses of wheel and rail’, Tribol. Int., 2009, 42, 475–490.
16.
JinX, WenZ, XiaoX, ZhouZ: ‘A numerical method for prediction of curved rail wear’, Multibody Syst. Dyn., 2007, 18, 531–557.
17.
SawleyK, KristanJ: ‘Development of bainitic rail steels with potential resistance to rolling contact fatigue’, Fatigue Fract. Eng. Mater. Struct., 2003, 26, 1019–1029.
WenZ, XiaoG, XiaoX, JinX, ZhuM: ‘Dynamic vehicle–track interaction and plastic deformation of rail at rail welds’, Eng. Fail. Anal., 2009, 16, (4), 1221–1237.
25.
TawfikD, MuttonPJ, ChiuWK: ‘Experimental and numerical investigations: alleviating tensile residual stresses in flash-butt welds by localised rapid post-weld heat treatment’, J. Mater. Process. Technol., 2008, 196, 279–291.
26.
DesimoneH, BerettaS: ‘Mechanisms of mixed mode fatigue crack propagation at rail butt-welds’, Int. J. Fatigue, 2006, 28, 635–642.
27.
BullochJH: ‘Fatigue crack growth studies in rail steels and associated weld metal’, Theor. Appl. Fract. Mech., 1986, 6, 75–84.
28.
BerettaS, BoniardiM, CarboniM, DesimoneH: ‘Mode II fatigue failures at rail butt-welds’, Eng. Fail. Anal. 2004, 12, 157–165.
29.
SkyttebolA, JosefsonBL, RingsbergJW: ‘Fatigue crack growth in a welded rail under the influence of residual stresses’, Eng. Fract. Mech., 2004, 72, 271–285.
30.
LawrenceFV, ChenYR, CyreJP, BarkanCPL: ‘Strategies for improving the fatigue resistance of thermite weldments’, Proc. Conf. AREMA 2001,Society of Automotive Engineers of Japan, Chicago, IL, USA, September 2001, 1–28.
31.
ZerbstU, LundénR, EdelKO, SmithRA: ‘Introduction to the damage tolerance behaviour of railway rails – a review’, Eng. Fract. Mech., 2009, 76, (17), 2563–2601.
32.
JeongDY, TangYH, OrringerO: ‘Damage tolerance analysis of detail fractures in rail’, Theor. Appl. Fract. Mech., 1997, 28, 109–115.