Interrupted blanking experiments were performed to study the deformation behavior of AA6082 (T6) sheets. An intentional asymmetry was introduced by having the punch and the die of different edge radii. High-resolution microstructural montages of sheet cross-section were used to experimentally measure the shear strain field during each interrupted blanking experiment. This provided a comprehensive experimentally measured spatial–temporal shear strain field for the blanking process. The shear strain was found to be high and localized at the top and bottom surfaces of the sheet which was in contact with the punch and the die. The shear strain was observed to monotonically reduce and get diffused at the interior of the sheet. The strain distribution was also calculated by finite element simulations and found to be in good agreement with the experimentally measured strain distributions. However, the peak strains predicted by the finite element simulations were always marginally lower than those observed by the experimental observations.
ChoKChiYCDuffyJ.Microscopic observations of adiabatic shear bands in three different steels. Metall Mater Trans A1990; 21: 1161–1175.
3.
DoddB.Shear instabilities in blanking and related processes. Met Technol1983; 10(1): 57–60.
4.
LiM.Micromechanisms of deformation and fracture in shearing aluminum alloy sheet. Int J Mech Sci2000; 42: 907–923.
5.
LeeTCChanLCWuBJ.Straining behaviour in blanking process—fine blanking vs conventional blanking. J Mater Process Tech1995; 48(1–4): 105–111.
6.
TengX.On the transition from adiabatic shear banding to fracture. Mech Mater2007; 39: 107–125.
7.
MishraAMartinMThadhaniNNKadBKKenikEAMeyersMA. High-strain-rate response of ultra-fine-grained copper. Acta Materialia2008; 56(12): 2770–2783.
8.
QianTMarxMSchülerK, et al. Plastic deformation mechanism of ultra-fine-grained AA6063 processed by equal-channel angular pressing. Acta Mater2010; 58(6): 2112–2123.
9.
ZhilyaevAPLangdonTG.Using high-pressure torsion for metal processing: fundamentals and applications. Prog Mater Sci2008; 53(6): 893–979.
10.
MahdavianMMGhalandariLReihanianM.Accumulative roll bonding of multilayered Cu/Zn/Al: an evaluation of microstructure and mechanical properties. Mater Sci Eng: A2013; 579: 99–107.
LiutkusTJ.Digital image correlation in dynamic punch testing and plastic deformation behavior of inconel 718. Master’s Thesis, The Ohio State University, Columbus, OH, 2014.
13.
MurrLERamirezACGaytanSM, et al. Microstructure evolution associated with adiabatic shear bands and shear band failure in ballistic plug formation in Ti–6Al–4V targets. Mater Sci Eng: A2009; 516(1–2): 205–216.
14.
KangJJainMWilkinsonDS, et al. Microscopic strain mapping using scanning electron microscopy topography image correlation at large strain. J Strain Anal Eng2005; 40(6): 559–570.
15.
QuintadaFonsecaJMummeryPMWithersPJ.Full-field strain mapping by optical correlation of micrographs acquired during deformation. J Microsc2005; 218(1): 9–21.
16.
HerteléSDe WaeleWDenysR, et al. Investigation of strain measurements in (curved) wide plate specimens using digital image correlation and finite element analysis. J Strain Anal Eng2012; 47(5): 276–288.
17.
TewariATiwariSBiswasP, et al. Vectorized 3D microstructure for finite element simulations. Mater Charact2010; 61(11): 1211–1220.
18.
ColliniLBonardiA.A micromechanical model of the evolution of stress and strain fields in ultrafine-grained metal structures under tension. J Strain Anal Eng2013; 48(2): 91–102.
19.
ChausovMGBerezinVBPylypenkoAP, et al. Strain field evolution on the surface of aluminum sheet alloys exposed to specific impact with oscillation loading. J Strain Anal Eng2015; 50(1): 61–72.
20.
GustafssonEKarlssonLOldenburgM.Experimental study of strain fields during shearing of medium and high-strength steel sheet. Int J Mech Mater Eng2016; 11(1): 14.
21.
QuaziTZShaikhRTotreA, et al. Blanking process optimization using Taguchi method. J Mater Process Tech2013; 7: 45–51.
22.
SubramonianSAltanTCiocirlanB, et al. Optimum selection of variable punch-die clearance to improve tool life in blanking non-symmetric shapes. Int J Mach Tool Manu2013; 75(1): 63–71.
23.
Vander VoortGF. Color metallography optical methods for producing color. In: Vander VoortGF (ed.) ASM handbook: metallography and microstructures, Vol. 9. Materials Park, OH: ASM International, 2004, pp.493–512.
24.
TewariAVijayalakshmiSTiwariS, et al. Influence of microstructure on uniaxial strain localization in AA5754 aluminum sheets produced by various processing routes. Metall Mater Trans A2013; 44(5): 2382–2398.
25.
ChenZHTangCYLeeTC, et al. A study of strain localization in the fine-blanking process using the large deformation finite element method. J Mater Process Tech1999; 86: 163–167.
26.
RoessigKMMasonJJ.Adiabatic shear localization in the dynamic punch test, part II: numerical simulations. Int J Plasticity1999; 15(3): 263–283.
27.
ChenZHChanLCLeeTC, et al. An investigation on the formation and propagation of shear band in fine-blanking process. J Mater Process Tech2003; 138(1–3): 610–614.
28.
PopatPBGhoshAKishoreNN.Finite element analysis of the blanking process. J Mech Work Technol1989; 18(3): 269–282.
29.
PoizatCCampagneLDaridonL, et al. Modeling and simulation of thin sheet blanking using damage and rupture criteria. Int J Form Process2005; 8: 29–47.