A multiaxis three-dimensional (3D) flat woven preform and a weaving method have been developed. The structure has five yarn sets, which are bias(+) and bias(—), warp, filling and Z-yarns. The weaving method has been introduced to form the structure. An experimental prototype was constructed to trial the method. In this technique, called “tube-carrier weaving”, bias(+) and bias(—) yarns are closely laid all over the surface. The preliminary study shows that the structure and weaving method seem feasible under the test conditions.
Dow, M.B., and Dexter H.B., "Development of Stitched, Braided and Woven Composite Structures in the ACT Program and at Langley Research Center (1985 to 1997)", NASA/TP-97-206234, November 1997.
Salway, D.J., Williams, J.L., and Gillig, D.P., "Method for Making a Textile", US Patent No. 6786242, September 7 2004 .
4.
Bhatnagar, A., and Parrish, E.S., "Bi-directional and Multiaxial Fabrics and Fabric Composites", US Patent No. 6841492, January 11 2005.
5.
Kamiya, R., Cheeseman, B.A., Popper, P., and Chou, T.W., Some Recent Advances in the Fabrication and Design of Three Dimensional Textile Preforms: A Review, Compos. Sci. Technol., 60, 33-47 (2000).
Yiping, Q., Wei, X., Youjiang, W., Zikry M.A., and Mohamed, M.H., Fabrication and Characterization of Three-dimensional Cellular-matrix Composites Reinforced with Woven Carbon Fabric, Compos. Sci. Technol. , 61(16), 2425-2435 (2001 ).
8.
Dow, N.F., "Triaxial Fabric", US Patent No. 3446251, May 27 1969.
9.
Dow, N.F. , and Tranfield, G., Preliminary Investigations of Feasibility of Weaving Triaxial Fabrics (Doweave), Textil. Res. J., 40(11), 986-998 (1970).
10.
Skelton, J. , Triaxially Woven Fabrics: Their Structure and Properties, Textil. Res. J., 41(8), 637-647 (1971).
11.
Cox, B.N. , Dadkhah, M.S., Morris, W.L., and Flintoff , J.G., Failure Mechanisms of 3D Woven Composites in Tension, Compression and Bending, Acta Metall. Mater., 42(12), 3967- 3984 ( 1994).
12.
Uchida, H., Yamamoto, T., and Takashima, H., Development of Low Cost Damage Resistant Composites, http://www.muratec.net/jp, [last accessed 12 March 2008] 2000.
13.
Bilisik, A.K. , and Mohamed, M.H., Multiaxis 3D weaving machine and properties of Multiaxial 3D woven carbon/epoxy composites, in the "39th International SAMPE Symposium", Anaheim, USA, April 11-14 1994.
14.
Mohamed, M.H. , and Bilisik, A.K., "Multilayered 3D Fabric and Method for Producing", US Patent No. 5465760, November 14 1995.
15.
Anahara, M., Yasui, Y., and Omori, H., "Three Dimensional Fabric and Method for Producing the Same", US Patent No. 5137058, August 11 1992.
16.
Anahara, M., Yasui, Y., Sudoh, M., and Nishitani, M., "Three-Dimensional Fabric with Symmetrically Arranged Warp and Bias Yarn Layers", US Patent No. 5270094, December 14 1993.
17.
Farley, G.L., "Method and Apparatus for Weaving a Woven Angle Ply Fabric", US Patent No. 5224519, July 6 1993.
18.
Iida, S., Ohmori, C., and Ito, T., "Multiaxial Fabric with Triaxial and Quartaxial Portions", US Patent No. 5472020, December 5 1995.
19.
Mood, G.I., "Multiaxial Yarn Structure and Weaving Method", US Patent No. 5540260, July 30 1996.
20.
Uchida, H., Yamamoto, T., Takashima, H., Otoshima, H., Yamamoto, T., Nishiyama, S., Sninya, M., "Three Dimensional Weaving Machine", US Patent No. 6003563, December 21 1999.
21.
Gowayed, Y.A. , Pastore, C.M., Analytical Techniques for the Prediction of Elastic Properties of Textile Reinforced Composites, Mech. Compos. Mater., 28(5), 393-408 ( 1993).