The glass fiber/epoxy composites with different loading of organo-montmorillonite (OMMT) were prepared using the hand lay-up technique. The effects of OMMT loading on the mechanical and morphological properties of glass fiber/epoxy/OMMT nanocomposites have been investigated. In this study, the effect of UV exposure on flexural properties and fracture toughness of glass fiber/ epoxy/OMMT nanocomposites has been studied using accelerated weathering test. The epoxy hybrid nanocomposites were subjected to UV radiation for 100 h. X-ray diffraction (XRD) and field emission scanning electron microscopy were performed to characterize the fractography of the glass fiber/epoxy/OMMT nanocomposites. The XRD analysis showed that glass fiber/epoxy/OMMT (1—3 wt%) exhibit exfoliated structures while glass fiber/epoxy/OMMT (4 wt%) showed intercalated structures. The retention-ability in flexural modulus and strength of epoxy hybrid nanocomposites after being subjected to accelerated weathering are considerably excellent. However, the fracture toughness of the glass fiber/epoxy/OMMT nanocomposites was reduced upon exposure to UV radiation.
Haque, A., Shamsuzzoha, M., Hussain, F. and Dean, D. ( 2003). S2-Glass/Epoxy Polymer Nanocomposites: Manufacturing, Structures, Thermal and Mechanical Properties, Journal of Composite Materials, 37: 1821-1837.
4.
Lin, L.Y. , Lee, J.H., Hong, C.E., Yoo, G.H. and Advani, S.G. (2006). Preparation and Characterization of Layered Silicate/Glass Fiber/Epoxy Hybrid Nanocomposites via Vacuum-Assisted Resin Transfer Molding (VARTM), Composites Science and Technology , 66: 2116-2125.
5.
Bozkurt, E., Tanoglu, M. and Kaya, E. ( 2007). Mechanical and Thermal Behavior of Non-Crimp Glass Fiber Reinforced Layered Clay/Epoxy Nanocomposite, Composites Science and Technology, 67: 3394-3403.
6.
Avila, A.F., Soares, M.I. and Neto, A.S. ( 2007). A Study on Nanostructured Laminated Plates Behavior Under Low-Velocity Impact Loadings, International Journal of Impact Engineering, 34: 28-41.
7.
Manfredi, L.B. , Vázquez, A. and Santis, D.H. (2008). Influence of the Addition of Montmorillonite to the Matrix of Unidirectional Glass Fibre/Epoxy Composites on Their Mechanical and Water Absorption Properties, Composites Part A: Applied Science and Manufacturing, 39: 1726-1731.
8.
Kornmann, X. , Rees, M., Thomann, Y., Necola, A., Barbezat, M. and Thomann, R. (2005). Epoxy-Layered Silicate Nanocomposites as Matrix in Glass Fibre-Reinforced Composites, Composites Science and Technology, 65: 2259-2268.
9.
Pang, S.S., Li, G.Q., Helms, J.E. and Ibekwe, S.I. ( 2001). Influence of Ultraviolet Radiation on the Low Velocity Impact Response of Laminated Beams, Composites Part B: Engineering , 32: 521-528.
10.
Kumar, B.G. , Singh, R.P. and Nakamura, T. (2002). Degradation of Carbon Fiber Reinforced Epoxy Composites by Ultraviolet Radiation and Condensation , Journal of Composite Materials, 36: 2713-2721.
11.
Jana, S. and Zhong, W.H. ( 2007). Effects of Hygrothermal Conditions and UV Radiation on UHMWPE Fibers/Nanofiber-Epoxy Composite, Journal of Composite Materials, 41: 2897-2914.
12.
Woo, R.S.C. , Kim, J.K., Leung, C.K.Y., Chen, Y.H., Zhu, H.G. and Li, J. (2007). Environmental Degradation of Epoxy-Organoclay Nanocomposites due to UV Exposure. Part I: Photo-degradation, Composites Science and Technology, 67: 3448-3456.
13.
Liu, T.X. , Tjiu, W.C., Tong, Y.J., He, C.B., Goh, S.S. and Chung, T.S. (2004). Morphology and Fracture Behavior of Intercalated Epoxy/Clay Nanocomposites, Journal of Applied Polymer Science, 94: 1236-1244.
14.
Jana, R.N. and Bhunia, H. ( 2008). Hygrothermal Degradation of the Composite Laminates from Woven Carbon/SC-15 Epoxy Resin and Woven Glass/SC-15 Epoxy Resin, Polymer Composites, 29: 664-669.
15.
Lei, S.G. , Hoa, S.V. and Ton-That, M.T. (2006). Effect of Clay Types on the Processing and Properties of Polypropylene Nanocomposites, Composites Science and Technology, 66: 1274-1279.
16.
Morlat, S., Mailhot, B., Gonzalez, D. and Gardette, J.L. ( 2004). Photo-Oxidation of Polypropylene/Montmorillonite Nanocomposites. 1. Influence of Nanoclay and Compatibilizing Agent, Chemistry of Materials, 16: 377-383.
17.
Plonka, R., Mader, E., Gao, S.L., Bellmann, C., Dutschk, V. and Zhandarov, S. ( 2004). Adhesion of Epoxy/Glass Fibre Composites Influenced by Aging Effects on Sizings, Composites Part A: Applied Science and Manufacturing, 35: 1207-1216.
18.
Yann, R., Damien, D., Rachid, E.G. and Patrick, F. ( 2006). Anisotropy of Hygrothermal Damage in Fiber/Polymer Composites: Effective Elasticity Measures and Estimates, Mechanics of Materials, 38: 1143-1158.
19.
Tjandraatmadja, G.F., Burn, L.S. and Jollands, M.C. (2002). Evaluation of Commercial Polycarbonate Optical Properties After QUV-A Radiation - The Role of Humidity in Photodegradation, Polymer Degradation and Stability, 78: 435-448.
20.
Devanne, T., Bry, A., Audoin, L. and Verdu, J. ( 2005). Radiochemical Ageing Cured Epoxy Network. Part I: Change of Physical Properties, Polymer, 46: 229-236.
21.
Velmurugan, R. and Mohan, T.P. (2009). Epoxy-Clay Nanocompositesand Hybrids: Synthesis and Characterization, Journal of Reinforced Plastics and Composites, 28: 17-37.
22.
Godara, A. and Raabe, D. ( 2007). Influence of Fiber Orientation on Global Mechanical Behavior and Mesoscale Strain Localization in a Short Glass-Fiber-Reinforced Epoxy Polymer Composite During Tensile Deformation Investigated Using Digital Image Correlation, Composites Science and Technology, 67: 2417-2427.
23.
Mazlan, N., Abu Bakar, A. and Chow, W.S. ( 2007). Effects of Organo-Montmorillonite on the Mechanical and Morphological Properties of Epoxy/Glass Fiber Composites, Polymer International, 56: 512-517.